PREPARATION OF MONODISPERSE MAGNETIC P(ST/BA/MAA) MICROSPHERES

XIE Gang; ZHANG Qiuyu; LUO Zhengping; WU Min; ZHANG Junping

doi:null

您当前的位置：

首页 >

文章列表页 >

PREPARATION OF MONODISPERSE MAGNETIC P(ST/BA/MAA) MICROSPHERES

Research Article | 更新时间：2021-03-19

- PREPARATION OF MONODISPERSE MAGNETIC P(ST/BA/MAA) MICROSPHERES
- Acta Polymerica Sinica Issue 3, Pages: 314-318(2002)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 June 2002，
扫描看全文
XIE Gang, ZHANG Qiuyu, LUO Zhengping, WU Min, ZHANG Junping. PREPARATION OF MONODISPERSE MAGNETIC P(ST/BA/MAA) MICROSPHERES. [J]. Acta Polymerica Sinica (3):314-318(2002)
DOI：

XIE Gang, ZHANG Qiuyu, LUO Zhengping, WU Min, ZHANG Junping. PREPARATION OF MONODISPERSE MAGNETIC P(ST/BA/MAA) MICROSPHERES. [J]. Acta Polymerica Sinica (3):314-318(2002) DOI：

摘要

在共沉淀法合成超细磁流体的基础上

以苯乙烯(St)、丙烯酸丁酯 (BA)和甲基丙烯酸 (MAA)为共聚单体

在不同的介质体系中采用无皂乳液聚合法制备了单分散

粒径范围为 80～230nm的磁性P(St/BA/MAA)微球 .详细探讨了介质极性、磁流体中表面活性剂含量对磁性高分子微球粒径和单分散性的影响 .实验结果表明

在一定范围内随介质极性降低

磁性高分子微球的单分散性提高

随表面活性剂用量增加

单分散性变差 .总体来看

磁性高分子微球的单分散性与其表面静电斥力密切相关

过大或过小的静电斥力均会导致磁性高分子微球单分散性的降低.

Abstract

Monodispersity is one of the important characteristics of magnetic polymer microspheres．In this paper

monodisperse magnetic poly(styrene／butyl acrylate／methacrylic acid) [P(St／BA／MAA)] microspheres with the size ranging from 80 to 230 nm

were prepared by emulsifier-free emulsion polymerization in the mixture of water and polar solvent

such as acetone

ethanol or methanol

in the presence of ferrofluid prepared by a co-precipitation method．The effects of the medium polarity and the surfactant content in ferrofluid on the particle size and monodispersity of magnetic P(St／BA／MAA) microspheres were discussed in detail．The results showed that the electrostatic repulsion between microspheres and radicals had a geat effect on the monodispersity of magnetic micropsheres．Proper repulsion benefited the monodispersity

but the higher or lower repulsion would lead to the decrease in monodispersity．Moreover

the results revealed that some features of emulsifier-free emulsion polymerization in the presence of ferrofluid was analogous to that of conventional emulsifier-free emulsion polymerization．

关键词

无皂乳液聚合单分散性磁性高分子微球介质极性表面活性剂静电斥力

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

IN SITU IMMOBILIZATION OF HORSERADISH PEROXIDASE ON ELECTROSPUN POLY(STYRENE-co-METHACRYLIC AICD) NANOFIBROUS MEMBRANE FOR CATALYTIC TREATMENT OF POLYPHENOL

SYNTHESIS AND SOLUTION PHOTOPHYSICS PROPERTIES OF A meta-LINKED ANIONIC POLY(PYRIDINYLENE ETHYNYLENE) CONJUGATED POLYELECTROLYTE

SYNTHESIS OF CATIONIC THERMORESPONSIVE MICROGELS AND THEIR APPLICATION FOR BIOMIMETIC MINERALIZATION OF SILICA

COMPOSITION AND MICRO-MORPHOLOGY OF POROUS PVA HYDROGELS AND THEIR POISSON’S RATIO AND MECHANICAL PROPERTIES

SOAP-FREE EMULSION COPOLYMERIZATION OF METHYL METHACRYLATE-BUTYL ACRYLATE WITH SODIUM α-OLEFIN SULFONATES AS FUNCTIONAL MONOMER

Related Author

No data

Related Institution

College of Science, Dalian Ocean University

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰