THE SYNTHESIS OF ULTRA-HIGH MOLECULAR WEIGHT POLYSTYRENE AND POLYMERIZATION KINETICS

NIE Jian; ZHANG Yifeng; JIANG Liming; SHEN Zhiquan

doi:null

您当前的位置：

首页 >

文章列表页 >

THE SYNTHESIS OF ULTRA-HIGH MOLECULAR WEIGHT POLYSTYRENE AND POLYMERIZATION KINETICS

Research Article | 更新时间：2021-03-19

- THE SYNTHESIS OF ULTRA-HIGH MOLECULAR WEIGHT POLYSTYRENE AND POLYMERIZATION KINETICS
- Acta Polymerica Sinica Issue 2, Pages: 203-207(2002)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 2002，
扫描看全文
NIE Jian, ZHANG Yifeng, JIANG Liming, SHEN Zhiquan. THE SYNTHESIS OF ULTRA-HIGH MOLECULAR WEIGHT POLYSTYRENE AND POLYMERIZATION KINETICS. [J]. Acta Polymerica Sinica (2):203-207(2002)
DOI：

NIE Jian, ZHANG Yifeng, JIANG Liming, SHEN Zhiquan. THE SYNTHESIS OF ULTRA-HIGH MOLECULAR WEIGHT POLYSTYRENE AND POLYMERIZATION KINETICS. [J]. Acta Polymerica Sinica (2):203-207(2002) DOI：

摘要

杯芳烃钕与Mg(n-Bu)2、HMPA所组成的三元络合催化剂用于苯乙烯配位聚合能以高收率制得超高分子量聚苯乙烯 .以甲苯为溶剂

在一定条件下制成三元配位催化剂

当 [Nd]=8×10-4mol/L

[St]=4 .0mol/L

Mg/Nd=20.0 (摩尔比 )

HMPA/Mg=1.0 (摩尔比)

50℃聚合45min

聚合转化率可达到80%左右 .所得聚苯乙烯的重均分子量高达210×104

分子量分布指数为1.61.间规聚苯乙烯含量为81% .动力学研究表明

聚合反应速率与单体和主催化剂-杯[6]芳烃钕的浓度分别呈1次方关系

聚合反应的表观活化能为41.7kJ/mol.

Abstract

Calix[n]Nd／MgBun2／HMPA is an effective catalytic system for the synthesis of the ultra-high molecular weight polystyrene (UHMWPS)．The catalytic activity of different Calix[n]Nd complex decreases in the following order：Calix[6]Nd＞Calix[4]Nd＞Calix[8]Nd．It shows that the aging of catalyst plays an important role on catalytic activity．The optimum conditions are as follow：Mg／Nd=20.0(molar ratio)

HMPA／Mg=1.0(molar ratio)

and aged 2.5 h under 50℃．The study of influence of solvent shows that toluene is a good solvent．The polymerization result shows that the conversion is over 80％ at 50℃

45 min．The kinetics of styrene polymerization using Calix[6]Nd-20MgBun2-20HMPA in toluene were investigated by weight method．It was found that the rate of polymerization is first order with respect to both monomer (St) and Calix [6] Nd concentrations．According to Arrhenius equation

it was found that polymerization activation energy is 41.7 kJ／mol．GPC characterization of obtained polymer shows：Mw=21.0×105

MWD=1.61．1H-NMR spectra of UHMWPS shows that the content of syndiotactic triad is 81％.

关键词

苯乙烯杯芳烃钕稀土催化剂聚合反应动力学

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS OF HIGH MOLECULAR WEIGHT POLYSTYRENE WITH A RARE EARTH CATALYST

CONTROLLED RELEASE OF SALICYLIC ACID FROM ELECTROSPUN MATS OF POLY(-CAPROLACTONE) WITH LOW CRYSTALLINITY

PREPARATION AND PERFORMANCE OF MODIFIED POLYVINYLIDENE FLUORIDE MEMBRANES GRAFTED WITH SULFONATED POLY(STYRENE-co-ACRYLIC ACID)

RAFT ALTERNATING COPOLYMERIZATION OF STYRENE AND N-SUBSTITUTED MALEIMIDES

SYNTHESIS OF aPs-b-P(S-co-E)-b-PE BLOCK COPOLYMERSCATALYZED WITH HALF-TITANOCENE/Zn/BDGE/MAO CATALYST SYSTEM

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰