PREPARATION AND IN VITRO RELEASE OF POLY(BUTYL CYANOACRYLATE) NANOCAPSULES WITH AN AQUEOUS CORE CONTAINING BOVINE SERUM ALBUMIN

LI Sai; QIAN Zhiyong; LIU Xiaolei; LIU Xiaobo

doi:null

您当前的位置：

首页 >

文章列表页 >

PREPARATION AND IN VITRO RELEASE OF POLY(BUTYL CYANOACRYLATE) NANOCAPSULES WITH AN AQUEOUS CORE CONTAINING BOVINE SERUM ALBUMIN

Research Article | 更新时间：2021-03-19

- PREPARATION AND IN VITRO RELEASE OF POLY(BUTYL CYANOACRYLATE) NANOCAPSULES WITH AN AQUEOUS CORE CONTAINING BOVINE SERUM ALBUMIN
- Acta Polymerica Sinica Issue 5, Pages: 679-682(2003)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 October 2003，
扫描看全文
LI Sai, QIAN Zhiyong, LIU Xiaolei, LIU Xiaobo. PREPARATION AND IN VITRO RELEASE OF POLY(BUTYL CYANOACRYLATE) NANOCAPSULES WITH AN AQUEOUS CORE CONTAINING BOVINE SERUM ALBUMIN. [J]. Acta Polymerica Sinica (5):679-682(2003)
DOI：

LI Sai, QIAN Zhiyong, LIU Xiaolei, LIU Xiaobo. PREPARATION AND IN VITRO RELEASE OF POLY(BUTYL CYANOACRYLATE) NANOCAPSULES WITH AN AQUEOUS CORE CONTAINING BOVINE SERUM ALBUMIN. [J]. Acta Polymerica Sinica (5):679-682(2003) DOI：

摘要

利用界面乳液聚合方法制备了新型含水核载牛血清白蛋白(BSA)的聚氰基丙烯酸丁酯 (PBCA)纳米微囊 .分别研究了纳米微囊的粒径及其分布

表面Zeta电势的变化 .并以牛血清白蛋白为模型药物考察了药物包裹率和载药量的变化以及载药纳米微囊在磷酸缓冲溶液中的体外释放行为 .结果表明

所制备的纳米微囊平均粒径为 200nm

多分散度为 0.226;表面Zeta电势的变化证明了BSA是包裹于纳米微囊的内部而不是吸附在其表面;包裹率和载药量取决于水相中BSA的初始浓度

当BSA的浓度为0.8mg/mL时

包裹率和载药量分别为 35%和 0.485×10-9mol/mg;药物的释放速率取决于纳米微囊的壁厚

通过调节壁厚可以达到控释的目的.

Abstract

Poly(butyl cyanoacrylate) (PBCA) nanocapsules with an aqueous core containing bovine serum albumin (BSA) were prepared by interfacial polymerization in a W／O emulsion．The nanocapsule sizes and their distribution were measured by laser scattering technique and transmission electron micrography．The change of Zeta potential

encapsulation efficiency

drug loading and in vitro release of nanocapsules were investigated using BSA as a model drug. The experimental results showed that nanocapsules were approximately 200 nm in diameters

0.226 in polydispersity. Encapsulation efficiency and drug loading were depended on the initial BSA concentration in aqueous phase. When the concentration was 0.8 mg／mL

encapsulation efficiency and drug loading were 35％ and 0.485×10-9 ～mol／mg of polymer．With the increase in the wall thickness of nanocapsules

the release time of BSA in PBS solution increased．The release rate could be controlled through adjusting the wall thickness of nanocapsules.

关键词

纳米微囊控制释放聚氰基丙烯酸丁酯(PBCA)

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

THE SYNTHESIS OF CARBOXYMETHYLCHITOSAN HYDROGEL AND THE APPLICATION IN DRUG CONTROLLED RELEASE SYSTEMS

STUDIES ON POLY(TEREPHTHALYL TYROSINE ESTER AMIDE) CARBONATES DRUG CONTROLLED RELEASE MATERIALS

THE SYNTHESIS AND DRUG RELEASE PROPERTY OF POLYSILOXANE BEARING PENDANT LONG ALKYL ETHER GROUP

PREPARATION AND RELEASING BEHAVIOUR OF TEMPERATURE RESPONSIVENESS OF GRAFT COPOLYMER PAA-g-PIPA MICROSPHERES

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰