Depolymerization of polybutylene terephthalate (PBT) in supercritical methanol was studied using a stainless stirred batch-type autoclave under high temperature (453～533 K) and high pressure (7～12 MPa) conditions．The main depolymerization products were dimethyl terephthalate (DMT) monomer and ethylene glycol．The effects of different reaction temperature and pressure on depelymerization of PBT were investigated by analysis of the solid phase and liquid phase products．Considering the critical point of methanol (512.6 K

8.09 MPa)

the reaction pressure was varied with in the mge of 7～12 MPa．The resuks silowed that the reaction pressure had littie influence on the depolymerization and the depolymerization rate was affected greatly by the reaction temperature．The depolymerization of PBT was only 30％ in 40 min at lower temperatures (453～463 K) but reached 100％ in 20 min when the temperature was above 513 K．Depolymerization kinetics of polybutylene terephthalate in supercritical methanol was studied．The results showed that the depolymedzation reaction rate constant (k1) in the temperature range of 513～533 K was much larger than the rate constant (k2) in the range of 453～483 K．The dissolution characteristics of PBT in supercritical methanol were the critical factors for depolymerization of PBT in a short time．These findings suggest that the supercfitical methanol treatment for depelymerization of polymers such as PBT will be potential for obtaining useful chemicals.