REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE

XIN Xiuqiang; WANG Yanmei; PAN Caiyuan

doi:null

您当前的位置：

首页 >

文章列表页 >

REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE

Research Article | 更新时间：2021-03-19

- REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE
- Acta Polymerica Sinica Issue 3, Pages: 398-402(2005)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 June 2005，
扫描看全文
XIN Xiuqiang, WANG Yanmei, PAN Caiyuan. REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE. [J]. Acta Polymerica Sinica (3):398-402(2005)
DOI：

XIN Xiuqiang, WANG Yanmei, PAN Caiyuan. REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE. [J]. Acta Polymerica Sinica (3):398-402(2005) DOI：

摘要

合成了二硫代苯甲酸2-(乙氧基羰基)异丙酯(ECPDB)、二硫代苯甲酸异丙苯酯(CDB)、二硫代苯甲酸1-苯基乙酯(PEDB)3种二硫代苯甲酸酯链转移剂.以这3种转移剂为基础

用凝胶渗透色谱和核磁共振测试了甲基丙烯酸N

N-二甲氨基乙酯(DMAEMA)和丙烯酸N

N-二甲氨基乙酯(DMAEA)两种碱性单体的可逆加成断裂链转移(RAFT)聚合的聚合物分子量、分子量分布和结构.发现有的聚合体系聚合物分子量分布较窄

但实验数均分子量与理论数均分子量相差较大;有的体系则转化率很低

聚合物分子量很小.这些可能是由聚合体系中单体活性和链转移剂链转移能力之间的匹配不太协调

使可逆加成断裂链转移快速平衡反应发生偏移或破坏造成的.因此

可通过更换单体或链转移剂来调节这种匹配

从而使可逆加成断裂链转移快速平衡保持稳定

达到聚合更可控

实验分子量与理论分子量更接近

分子量分布更窄的目的.

Abstract

Poly(2-(dimethylamino) ethyl methaerylate (PDMAEMA) and poly(2-(dimethylamino) ethyl aveate (PDMAEA) were prepared by using chain transfer agents (CTA)

dithioesters (2-(ethoxyearbonyl) prop-2-yl dithiobenzoate (ECPDB)

eumyl dithiobenzoate (CDB) and 1-phenylethyldithiobenzoate (PEDB) respectively

through reversible addition-fragmentation chain transfer (RAFT) polymerization．The molecular weight and molecular weight distribution of PDMAEMA and PDMAEA．were measured by gel permeation chromatography (GPC) and nuclear magnetic resonance spectrometer(1H-NMR)．The results showed the molecular weight distribution of PDMAEMA was narrow when the ECPDB/AIBN and CDB/AIBN as the initiator respectively．But the theoretical number average molecular weight Mn.th was not in good agreement with Mn.NMR and Mn.GPC. It demonstrated that the molecular weight of polymers could not be controlled．Its reason is probably that the balalive of the reversible addition-fragmentation chain transfer is disturbed by unapt match of monomer and CTA．With changing monomer or CTA

the molecular weight of polymers can be controlled．Compared with the CDB/AIBN system

the molecular weight distribution of PDMAEA by using PEDB/AIBN was narrower

and the molecular weisht was controllable．

关键词

可逆加成断裂链转移（RAFT）甲基丙烯酸NN-二甲氨基乙酯（DMAEMA）丙烯酸NN-二甲氨基乙酯（DMAEA）聚电解质

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

DEVELOPMENT OF BRANCHING STRUCTRUE IN SELF-CONDENSING ATOM TRANSFER RADICAL COPOLYMERIZATION WITH A LARGE COMONOMER/INIMER FEED RATIO

PREPARATION OF HOLLOW POLYELECTROLYTE MICROCAPSULES AND THEIR FLUORESCENT PROTEINS LOADING

SYNTHESIS OF POLYBUTADIENE-b-POLY［2-(DIMETHYLAMINO)ETHYL METHACRYLATE］ AMPHIPHILIC BLOCK COPOLYMER BY MECHANISM TRANSFORMATION

CATALYTIC OXIDATIVE POLYMERIZATION OF(N，N-DIMETHYLAMINO)ETHYL METHACRYLATE WITH CuX/PMDETA

POLYELECTROLYTE MICROCAPSULES FABRICATED VIA in situ COACERVATION—— THE INFLUENCE OF DOPED POLYELECTROLYTE AMOUNT IN THE TEMPLATES ON THEIR STRUCTURES AND PROPERTIES

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰