PREPARATION OF EXTRACTANT MICROCAPSULES BY SOLVENT EVAPORATION METHOD

YANG Weiwei; LUO Guangsheng; WU Fangyu; GONG Xingchu

doi:null

您当前的位置：

首页 >

文章列表页 >

PREPARATION OF EXTRACTANT MICROCAPSULES BY SOLVENT EVAPORATION METHOD

Research Article | 更新时间：2021-03-19

- PREPARATION OF EXTRACTANT MICROCAPSULES BY SOLVENT EVAPORATION METHOD
- Acta Polymerica Sinica Issue 2, Pages: 207-212(2005)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 2005，
扫描看全文
YANG Weiwei, LUO Guangsheng, WU Fangyu, GONG Xingchu. PREPARATION OF EXTRACTANT MICROCAPSULES BY SOLVENT EVAPORATION METHOD. [J]. Acta Polymerica Sinica (2):207-212(2005)
DOI：

YANG Weiwei, LUO Guangsheng, WU Fangyu, GONG Xingchu. PREPARATION OF EXTRACTANT MICROCAPSULES BY SOLVENT EVAPORATION METHOD. [J]. Acta Polymerica Sinica (2):207-212(2005) DOI：

摘要

萃取剂微胶囊的制备是利用微囊化方法将萃取剂包覆起来

解决传统液液萃取中的两相相分散、相混合、相分离以及溶剂的损失和设备结构复杂等问题 .用简单易控制的溶剂挥发法成功制备了聚砜及聚苯乙烯材料包覆的多种萃取剂 (如磷酸三丁酯

2-乙基己基磷酸

三辛胺和Aliquat 336 )微胶囊

并考察了壁材和分散剂的选择对不同萃取剂进行包覆的影响

同时研究了搅拌速度和膜溶液组成对微胶囊的形态、萃取剂包覆量的影响 .结果表明

(1)用聚砜作壁材可以包覆磷酸三丁酯、2-乙基己基磷酸

而用聚苯乙烯可以包覆三辛胺、Aliquat336 ;(2 )对于不同的O/W乳液体系

只有选择合适的分散剂

才能得到理想球形状、分散性好的微胶囊 ;(3)增大搅拌速度可以降低液滴尺度

从而减小微胶囊粒径 ;(4)膜溶液组成的影响则表现在两个方面

一是膜溶液的粘度和两相界面张力是除搅拌速度外微胶囊粒径的决定因素

二是膜溶液中壁材与萃取剂的比例优化时

才能得到萃取剂包覆量高的微胶囊.

Abstract

To encapsulate extractants by method of microencapsulation can solve the problems of phase dispersion

phase mixing

phase separation

the leakage of extractant

as well as complicated structure of equipment in the extraction process．In the present work polysuffone and polystyrene as polymer materials were used to encapsulate the extractants such as TBP

D2EHPA

TOA

Aliquat 336 etc by means of solvent evaporation．The influence of shell materials

dispersants

stirring speed and composition of the organic phase has been investigated．The experimental results showed that TBP and D2EHPA were successfully encapsulated with polysulfone as the shell material while for the preparation of TOA and Aliquat 336 the shell material of polystyrene should be applied．The spherical shape and monodispersity of the microcapsules were related to the dispersion agent used in the O/W system．The mean diameter of the microcapsules decreased greatly with an increase of the stirring speed．Besides the stirring speed

the viscosity of polymer solution and the interfacial tension of working systems are the major factors that influence the size of the microcapsules．An optimal encapsulation efiqciency of the mierocapsules was reached when the content ratio of the shell rnaterial to the extractant in the polymet solution was optimized．

关键词

溶剂挥发微胶囊萃取

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

PREPARATION OF MICROCAPSULES WITH SILICONE OIL AS CONTINUOUS PHASE USING A SOLVENT EVAPORATION METHOD

PREPARATION OF PHASE CHANGE MATERIAL WAX/P(MMA-co-AA) CORE-SHELL MICROCAPSULES

POLYELECTROLYTE MICROCAPSULES FABRICATED VIA in situ COACERVATION—— THE INFLUENCE OF DOPED POLYELECTROLYTE AMOUNT IN THE TEMPLATES ON THEIR STRUCTURES AND PROPERTIES

PREPARATION OF MICROCAPSULES WITH ENCAPSULATED DODECANOL BY COMPLEX COACERVATION OF POLY［2-(METHACRYLOYLOXY)-ETHYLTRIMETHYL AMMONIUM CHLORIDE］ AND ACACIA

FABRICATION AND CHARACTERIZATION OF GOLD NANOPARTICLES LOADED MICROCAPSULES

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰