1,3-DIPOLAR CYCLOADDITION POLYMERIZATION OF BISPROPARGYL ETHER OF BISPHENOL-A WITH 4,4′-BIPHENYL DIBENZYL AZIDE AND THEIR THERMAL ANALYSES

HU Yanhong; LUO Yonghong; WAN Liqiang; QI Huimin; HUANG Farong; DU Lei

doi:null

您当前的位置：

首页 >

文章列表页 >

1,3-DIPOLAR CYCLOADDITION POLYMERIZATION OF BISPROPARGYL ETHER OF BISPHENOL-A WITH 4,4′-BIPHENYL DIBENZYL AZIDE AND THEIR THERMAL ANALYSES

Research Article | 更新时间：2021-03-19

- 1,3-DIPOLAR CYCLOADDITION POLYMERIZATION OF BISPROPARGYL ETHER OF BISPHENOL-A WITH 4,4′-BIPHENYL DIBENZYL AZIDE AND THEIR THERMAL ANALYSES
- Acta Polymerica Sinica Issue 4, Pages: 560-565(2005)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 August 2005，
扫描看全文
HU Yanhong, LUO Yonghong, WAN Liqiang, QI Huimin, HUANG Farong, DU Lei. 1,3-DIPOLAR CYCLOADDITION POLYMERIZATION OF BISPROPARGYL ETHER OF BISPHENOL-A WITH 4,4′-BIPHENYL DIBENZYL AZIDE AND THEIR THERMAL ANALYSES. [J]. Acta Polymerica Sinica (4):560-565(2005)
DOI：

HU Yanhong, LUO Yonghong, WAN Liqiang, QI Huimin, HUANG Farong, DU Lei. 1,3-DIPOLAR CYCLOADDITION POLYMERIZATION OF BISPROPARGYL ETHER OF BISPHENOL-A WITH 4,4′-BIPHENYL DIBENZYL AZIDE AND THEIR THERMAL ANALYSES. [J]. Acta Polymerica Sinica (4):560-565(2005) DOI：

摘要

合成了两种单体双酚A二炔丙基醚与4

4′-联苯二苄叠氮

研究了一种新的低温聚合体系——双酚A二炔丙基醚与4

4′-联苯二苄叠氮在烘箱中的本体聚合行为.通过红外、核磁共振以及质谱、元素分析等表征了单体的结构.利用傅立叶红外技术(FTIR)跟踪了聚合反应过程中特征基团的变化

采用差示扫描量热技术(DSC)研究了聚合反应工艺及其动力学

热失重分析(TGA)考察了聚合产物的热稳定性能.通过Kissinger法和0zawa法获得了反应的一些动力学参数.结果表明

双酚A二炔丙基醚与4

4′-联苯二苄叠氮易发生1

3偶极环加成聚合反应

在聚合物结构中形成三唑五元环

它们的聚合起始温度在70℃左右

聚合反应的主反应是一级反应

表观活化能ΔE=84.6kJ/mol

指前因子A=4.865×1010min-1.同时发现

聚合物具有较好的热稳定性能.

Abstract

Two monomers

bispmpargyl ether of bisphenol-A(BPEBA)and 4

4'-biphenyl dibenzyl azide (BPDBA) were synthesized and characterized with FT-IR

1H-NMR and elementary analysis．Their bulk polymerization was conducted in an oven

and a polytriazole was obtained by the 1

3-dipolar cycloaddition polymerization．The variation of the reactively functional groups during the polymerization was traced by FT-IR

the polymerizing reaction of BPEBA with BPDBA and its kinetics were investigated by using differential scanning calorimetry (DSC) at a variety of heating rates．Some kinetic parameters including the reaction order

activation energy and pre-exponential factor were obtained with the Kissinger and the Ozawa methods．The thermal stability of the polymer was evaluated with TGA．The results showed that BPEBA and BPDBA were easy to form polytriazole by 1

3-dipolar reaction．The polymerizing reaction happened at low temperature

i．e．70℃

the reaction was a one order reaction

the activation energy △E=84.6 kJ／mol．and the pre-exponential factor A=4.865×1010. min-1．The polymer exhibited good thermal stability．

关键词

双酚A二炔丙基醚叠氮化合物13-偶极环加成反应三唑低温固化

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

TETRAHYDROFURAN POLYMERIZATION INITIATED WITH HETEROPOLYACID Ⅷ. 1,1,1-TRIHYDROXYMETHYLENEPROPANE AS MOLECULAR WEIGHT CONTROLLER

PREPARATION OF MAGNETIC COMPOSITE MICROSHERES BY SOAP-FREE EMULSION POLYMERIZATION IN THE PRESENCE OF 1,1-DIPHENYLETHENE

Preparation and Characterization of Chloromethylated PolystyreneGrafted Partic les of MicronSized Silica Gel

SYNTHESIS AND CHARACTERIZATION OF COPOLYMERS WITH2,5-BIS [(5-DECAOXYPHENYL)-1,3,4-OXADIAZOLE] STYRENE MONOMER AND VINYL CARBAZOLES

SYNTHESIS AND CHARACTERIZATION OF THREE-ARM STAR-SHAPED POLYETHYLENE GLYCOLS WITH 1,1,1-TRIHYDROXMETHYLPROPANE AS CORES

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰