KINETICS STUDY OF COPOLYMERIZATION OF ACRYLAMIDE WITH ACRYLIC ACID IN THE PRESENCE OF POLYALLYLAMMONIUM CHLORIDE AS TEMPLATE

ZHANG Yuxi; WU Feipeng; LI Miaozhen; WANG Erjian

doi:null

您当前的位置：

首页 >

文章列表页 >

KINETICS STUDY OF COPOLYMERIZATION OF ACRYLAMIDE WITH ACRYLIC ACID IN THE PRESENCE OF POLYALLYLAMMONIUM CHLORIDE AS TEMPLATE

Research Article | 更新时间：2021-03-19

- KINETICS STUDY OF COPOLYMERIZATION OF ACRYLAMIDE WITH ACRYLIC ACID IN THE PRESENCE OF POLYALLYLAMMONIUM CHLORIDE AS TEMPLATE
- Acta Polymerica Sinica Issue 6, Pages: 889-892(2004)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 December 2004，
扫描看全文
ZHANG Yuxi, WU Feipeng, LI Miaozhen, WANG Erjian. KINETICS STUDY OF COPOLYMERIZATION OF ACRYLAMIDE WITH ACRYLIC ACID IN THE PRESENCE OF POLYALLYLAMMONIUM CHLORIDE AS TEMPLATE. [J]. Acta Polymerica Sinica (6):889-892(2004)
DOI：

ZHANG Yuxi, WU Feipeng, LI Miaozhen, WANG Erjian. KINETICS STUDY OF COPOLYMERIZATION OF ACRYLAMIDE WITH ACRYLIC ACID IN THE PRESENCE OF POLYALLYLAMMONIUM CHLORIDE AS TEMPLATE. [J]. Acta Polymerica Sinica (6):889-892(2004) DOI：

摘要

丙烯酰胺 (AM)和丙烯酸 (AA)模板共聚合是以聚烯丙基氯化铵 (PAAC)模板存在下

在水溶液中进行

在这体系中

模板PAAC和单体AA有很强的相互作用

而单体AM与模板则没有作用 .应用膨胀计和电导滴定方法研究了影响聚合反应速度的各种因素

得到的结果指出

在聚烯丙基铵模板作用下共聚合反应遵循Ⅰ型 (zip)模板聚合反应机制

速度最高值出现在模板单元T与单体AA等摩尔比 (T/AA =1)处

这表明在反应溶液中PAAC和单体AA具有很强的相互作用 .测得它们的竞聚率分别为r1=2.68(AA)和r2 =0.44(AM)

与没有模板存在时相比

大幅度增高的r1 值表明此共聚合反应

生成AA长序列结构的可能性大大增加 .同时发现聚合反应速度分别和单体浓度及引发剂浓度的1.1和0.83次方成正比

由于模板的作用数值高于常规值.

Abstract

Template copolymerization of acrylamide (AM) with acylic acid(AA) was carried out in the presence of polyallylammonium chloride (PAAC) as matrix in aqueous solutions．The various influences on the rate of polymerization were studied by dilatometer and electrical conductivity measurements．The obtained results indicated that the process of copolymerization under the effect of polyallylammonium salt was according to type I (zip) template mechanism．The maximum of reaction rate was appeared at equivalence mole ratio of template unit (T) to monomer AA. T／AA=1 indicated a high interaction between the monomer AA and the template in the solution．The reactivity ratios of r1 2.68 for AA and r2 0.44 for AM were also obtained. The considerable enhancement of r1 compared with that without the template indicated that the presence of PAAC significantly increases the probability of long sequences of AA unites in copolymers．The rate of polymerization was found to be proportional to the concentration of monomers and initiator with exponents of 1.1 and 0.83

respectively

which are larger than the ordinary values due to the effect of PAAC．

关键词

AM/AA模板共聚合聚烯丙基氯化铵模板作用聚合速度竞聚率

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDIES ON MICROBLOCK STRUCTURE OF AM/DMBAC CATIONIC COPOLYMERS

SYNTHESIS AND SALT SOLUTION PROPERTIES OF ZWITTERIONIC COPOLYMER P(AM-co-VPPS) CONTAINING SULFOBETAINE GROUPS

STUDIES ON COPOLYMERIZATION OF L-LACTIDE WITH ε-CAPROLATONE CATALYZED BY MAGNESIUM OCTOATE AND THE STRUCTURE AND PROPERTIES OF THE COPOLYMERS

KINETICS STUDIES ON POLYMERIZATION OF DIETHYLDIALLYLAMMONIUM CHLORIDE AND ITS COPOLYMERIZATION WITH ACRYLAMIDE AND ACRYLIC ACID

RING-OPENING COPOLYMERIZATION OF γ-VALEROLACTONE AND ε-CAPROLACTONE CATALYZED BY BORON TRIFLUORIDE ETHERATE

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰