RAFT GRAFTING POLYMERIZATION OF MMA/St FROM SURFACE OF SILICON WAFER

LI Deling; LUO YingWu; ZHANG Bingzi; LI Bogeng; ZHU Shiping

doi:null

您当前的位置：

首页 >

文章列表页 >

RAFT GRAFTING POLYMERIZATION OF MMA/St FROM SURFACE OF SILICON WAFER

Research Article | 更新时间：2021-03-19

- RAFT GRAFTING POLYMERIZATION OF MMA/St FROM SURFACE OF SILICON WAFER
- Acta Polymerica Sinica Issue 8, Pages: 699-704(2007)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 August 2007，
扫描看全文
LI Deling, LUO YingWu, ZHANG Bingzi, LI Bogeng, ZHU Shiping. RAFT GRAFTING POLYMERIZATION OF MMA/St FROM SURFACE OF SILICON WAFER. [J]. Acta Polymerica Sinica (8):699-704(2007)
DOI：

LI Deling, LUO YingWu, ZHANG Bingzi, LI Bogeng, ZHU Shiping. RAFT GRAFTING POLYMERIZATION OF MMA/St FROM SURFACE OF SILICON WAFER. [J]. Acta Polymerica Sinica (8):699-704(2007) DOI：

摘要

将3-(2-二硫代苯甲酸基丙酰氧基)丙基二甲基甲氧基硅烷化学键合于硅片表面.以甲基丙烯酸甲酯和苯乙烯为单体

在硅片表面进行可逆加成-断裂链转移（RAFT）接枝聚合.X-射线光电子能谱仪证实聚甲基丙烯酸甲酯（PMMA）、聚苯乙烯（PS）、苯乙烯/甲基丙烯酸甲酯的共聚物（poly(MMA-co-St)）都接枝到硅片表面.但3个体系表现出不同的性质

甲基丙烯酸甲酯的RAFT聚合可控性差

分子量比设计分子量大得多

分子量分布指数宽

接枝密度仅为0.03 chains/nm2；苯乙烯均聚合的活性/可控性好、分子量分布窄

接枝密度提高到0.21 chains/nm2；共聚合体系综合了两个均聚体系的优点

分子量分布较窄

接枝密度最高为0.31 chains/nm2

聚合物膜厚随转化率、数均分子量基本呈线性增长.

Abstract

Polystyrene (PSt)

polymethylmethacrylate (PMMA) and copolymers (poly(MMA-co-St)) were grafted from silicon wafer via RAFT agent that was anchored to the surface.X-ray photoelectron spectroscopy showed that while the polymers were successfully grafted

the control of polymer molecular weight (MW) behaved very differently.The Si-PMMA system yielded MW much higher than the theoretically targeted

broad molecular weight distribution and low grafting density (ca. 0.03 chains/nm2).In contrast

the Si-PSt system gave MW close to the theoretical value with polydispersities around 1.3.The grafting density increased to 0.21 chains/nm2.In Si-poly(MMA-co-St) system

the polymer layer thickness increased linearly with monomer conversion and molecular weight of free polymer in solution

suggesting that the RAFT copolymerization grafting of MMA and St from silicon wafer was well controlled.The MW was close to the theoretical value.The grafting density reached 0.31 chains/nm2

which was higher than those obtained in their homo-polymerizations.

关键词

表面改性接枝聚合RAFT聚合接枝密度

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Tri-block Terpolymers with Different Sequences Synthesized by Combination of Anionic and RAFT Polymerizations

Preparation of Polyethylene Polyamine-modified Cellulose and Its Adsorbability for As, F and Cr Anions

INTERACTION BETWEEN PNIPAAM MODIFIED SILICON SURFACES AND PLASMA PROTEINS

REVERSIBLE ADDITION-FRAGMENTATION TRANSFER POLYMERIZATION OF POLYMERS CONTAINING BOTH FORMYL AND β-PINENE FUNCTIONAL GROUPS

SYNTHESIS AND INVESTIGATION OF WELL-DEFINED AND FLUORESCENCELABELLED POLY(METHYL METHACRYLATE) BY RAFT POLYMERIZATION

Related Author

No data

Related Institution

The State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University

Technical Institute of Physics and Chemistry, Chinese Academy of Sciences

Zhong Ke San Huan Research

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰