MORPHOLOGY AND RHEOLOGICAL BEHAVIOR OF CATIONIC POLYURETHANE/POLYDIMETHYLSILOXANE SELF-EMULSIFYING MICRO EMULSION

WANG Haihua; SHEN Yiding; FEI Guiqiang; FAN Xiaojing

doi:null

您当前的位置：

首页 >

文章列表页 >

MORPHOLOGY AND RHEOLOGICAL BEHAVIOR OF CATIONIC POLYURETHANE/POLYDIMETHYLSILOXANE SELF-EMULSIFYING MICRO EMULSION

Research Article | 更新时间：2021-03-19

- MORPHOLOGY AND RHEOLOGICAL BEHAVIOR OF CATIONIC POLYURETHANE/POLYDIMETHYLSILOXANE SELF-EMULSIFYING MICRO EMULSION
- Acta Polymerica Sinica Issue 4, Pages: 321-326(2007)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 2007，
扫描看全文
WANG Haihua, SHEN Yiding, FEI Guiqiang, FAN Xiaojing. MORPHOLOGY AND RHEOLOGICAL BEHAVIOR OF CATIONIC POLYURETHANE/POLYDIMETHYLSILOXANE SELF-EMULSIFYING MICRO EMULSION. [J]. Acta Polymerica Sinica (4):321-326(2007)
DOI：

WANG Haihua, SHEN Yiding, FEI Guiqiang, FAN Xiaojing. MORPHOLOGY AND RHEOLOGICAL BEHAVIOR OF CATIONIC POLYURETHANE/POLYDIMETHYLSILOXANE SELF-EMULSIFYING MICRO EMULSION. [J]. Acta Polymerica Sinica (4):321-326(2007) DOI：

摘要

在催化剂和少量助溶剂的作用下

以端羟基硅油（HPMS）/聚（四亚甲基醚）二醇（PTMG）为软段

异佛尔酮二异氰酸酯（IPDI）为硬段单体

以三羟甲基丙烷TMP为交联剂、N-甲基二乙醇胺(MDEA)为扩链剂合成了一系列自乳化双软段HPMS/PU微乳液.分析了HPMS用量对HPMS/PU微乳液粒径及微观形态的影响；研究了HPMS/PU中HPMS含量、MDEA用量、TMP用量、预聚体分子量对其流变性能的影响.研究结果表明

HPMS的加入使乳液粒径增加

HPMS/PU乳液为非牛顿流体

且具有一定的假塑性和触变性

表观粘度随切变速率的变化规律呈现一定的切力变稀特征

流动指数范围为0.885～0.531之间；其零剪切粘度值为13.59～25.08 mPa·s

随HPMS用量、MDEA用量、预聚体相对分子质量、TMP用量而异.

Abstract

With the action of catalyst and cosolvent

a series of hydroxyl-terminated polydimethylsiloxane (HPMS) based polyurethane (PU) micro emulsion were successfully prepared by self-emulsifying copolymerization.They were prepared by the reacton of isophorone isocyanate (IPDI)

poly(tetramethylene oxide)glycol (PTMG) and HPMS with N-methyldiethanolamine (MDEA) as chain extender and trimethylolpropane (TMP) as crosslinker.Effects of HPMS content on the particle size and morphology of HPMS/PU micro emulsion were analyzed.The effects of HPMS content

N-methyldiethanolamine content

TMP content

and the molecular weight of the prepolymer on the emulsion's rheological properties were studied.The results revealed that the average diameter of the particles and the distribution width became greater and wider with HPMS addition.Emulsions exhibit a Non-newtonian behavior

and they are endowed with pseudoplasticity and thixotropy.It is noticed that the apparent viscosity decreases with increasing the shear rate

that is

the emulsions show a characteristic of shear thinning

and their flow-behavior index (n) ranges from 0.885 to 0.531.It is also noticed that their zero shear viscosity ranges from 13.59 mPa\5s to 25.08 mPa\5s

changing with the content of HPMS

N-methyldiethanolamine

TMP and the molecular weight of the prepolymer.

关键词

聚氨酯端羟基硅油流变性微观形态微乳液

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS OF KONJAC GLUCOMANNAN ACETATE WITH HIGH DEGREE OFSUBSTITUTION AND OF ITS RHEOLOGICAL AND THERMOPLASTIC PROPERTIES

IMPROVING ADHESION OF SILICONE RUBBER COATING TO POLYURETHANE SURFACE

PREPARATION, STRUCTURE AND PROPERTIES OF BLENDED FILMS OF POLYURETHANE AND SILK FIBROIN

SYNTHESIS AND PROPERTIES OF WATERBORNE POLYURETHANES MODIFIED BY EPOXY RESIN

PREPARATION OF POLYURETHANE/CARBON NANOTUBES COMPOSITES FOAM THROUGH in situ POLYCONDENSATION

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰