THE INFLUENCE OF THE FRACTURE MORPHOLOGICAL PARAMETERS ON BENDING BREAK ENERGY OF POLYSTYRENE

XU Tao; YU Jie; LUO Zhu; WANG Li

doi:null

您当前的位置：

首页 >

文章列表页 >

THE INFLUENCE OF THE FRACTURE MORPHOLOGICAL PARAMETERS ON BENDING BREAK ENERGY OF POLYSTYRENE

Research Article | 更新时间：2021-03-19

- THE INFLUENCE OF THE FRACTURE MORPHOLOGICAL PARAMETERS ON BENDING BREAK ENERGY OF POLYSTYRENE
- Acta Polymerica Sinica Issue 2, Pages: 141-145(1999)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 1999，
扫描看全文
XU Tao, YU Jie, LUO Zhu, WANG Li. THE INFLUENCE OF THE FRACTURE MORPHOLOGICAL PARAMETERS ON BENDING BREAK ENERGY OF POLYSTYRENE. [J]. Acta Polymerica Sinica (2):141-145(1999)
DOI：

XU Tao, YU Jie, LUO Zhu, WANG Li. THE INFLUENCE OF THE FRACTURE MORPHOLOGICAL PARAMETERS ON BENDING BREAK ENERGY OF POLYSTYRENE. [J]. Acta Polymerica Sinica (2):141-145(1999) DOI：

摘要

对缺口聚苯乙烯试样进行了不同加载速率下的三点弯曲实验

通过对加载速率、断面特征区特征参量、断裂能耗三者间关系的分析

指出断裂表面特征形貌中的镜面区、肋状区的形成是能量消耗的主要过程．实验结果表明

随着加载速率增大

镜面区尺寸增大并逐渐趋于平缓

肋条宽度减小而肋区粗糙度增大．断裂能耗与加载速率间存在极小值现象

该极小值出现在２.５ｍ／ｍｉｎ的加载速率下

与断面形貌特征的变化正好对应；加载速率＜２.５ｍ／ｍｉｎ时

断面主要由镜面区、最后断裂区组成

断裂能耗的变化取决于镜面区尺寸的变化；加载速率＞２.５ｍ／ｍｉｎ时

断面由镜面区、肋区、最后断裂区组成

断裂能耗的变化主要和肋区粗糙度的变化有关．

Abstract

The PS specimens were subjected to three point bending under different loading rate.Through the analysis of experimental results

the forming process of the mirror zone and the rib zone is the principal process of energy consumption.With the increase of loading rate

the size of mirror zone decreases and tends towards constant progressively.At the same time

the rib width decreases while the roughness of rib zone increases.A minimum appearing at the loading rate 2.5m/min exists in the relationships between energy consumption and loading rate.When loading rate below 2.5m/min

the fracture surfaces were chiefly made up by the mirror zone and the last fracture zone.The change of break energy is mainly decided by the change of the size of mirror zone.When the loading rate beyond 2.5m/min

the fracture surfaces were conposed of the mirror zone

the rib zone and the last fracture zone.The change of energy consumption is primarily decided by the roughness of rib zone.

关键词

加载速率断面形态特征参量断裂能聚苯乙烯

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

GLASS TRANSITION TEMPERATURE OF POLYSTYRENE DETERMINED BY DSC REVISITED

SYNTHESIS AND FLUORESCENT PROPERTYIES OF PHOSPHAPHENANTHRENECONTAINING POLYSTYRENE

PREPARATION AND CHARACTERIZATION OF POLYSTYRENE/LAYERED DOUBLE METAL HYDROXIDE NANOCOMPOSITES

PREPARATION OF PS/CaCO3 COMPOSITE NANOPARTICLES AND PS HOLLOW NANO-SPHERES

EFFECTS OF MELT VISCOSITY ON THE PREFERENTIAL INTERCALATIONBEHAVIOR OF CLAY IN IMMISCIBLE POLYPROPYLENE/POLYSTYRENE BLENDS

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰