STUDIES OF TRANSPARENT AND CONDUCTING FILM OF POLYANILINE BY A DIPPING POLYMERIZATION METHOD

LI Yongming; WAN Meixiang

doi:null

您当前的位置：

首页 >

文章列表页 >

STUDIES OF TRANSPARENT AND CONDUCTING FILM OF POLYANILINE BY A DIPPING POLYMERIZATION METHOD

Research Article | 更新时间：2021-03-19

- STUDIES OF TRANSPARENT AND CONDUCTING FILM OF POLYANILINE BY A DIPPING POLYMERIZATION METHOD
- Acta Polymerica Sinica Issue 2, Pages: 177-183(1998)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 1998，
扫描看全文
LI Yongming, WAN Meixiang. STUDIES OF TRANSPARENT AND CONDUCTING FILM OF POLYANILINE BY A DIPPING POLYMERIZATION METHOD. [J]. Acta Polymerica Sinica (2):177-183(1998)
DOI：

LI Yongming, WAN Meixiang. STUDIES OF TRANSPARENT AND CONDUCTING FILM OF POLYANILINE BY A DIPPING POLYMERIZATION METHOD. [J]. Acta Polymerica Sinica (2):177-183(1998) DOI：

摘要

采用浸渍聚合法制备透明导电的聚苯胺薄膜

并系统地研究了基片、反应温度、氧化剂和掺杂剂等因素对聚苯胺透明导电薄膜的电学和光学性能的影响．在最佳的制备条件下

所得薄膜的室温电导率可达１～５Ｓ／ｃｍ．当厚度为０.５μｍ时

在４５０至６５０ｎｍ的透光窗口内

该薄膜的透光率可达８０％．借助结构表征讨论了薄膜的生长机理和它的结构组成．

Abstract

A conducting and transparent film of doped polyaniline was prepared by a dipping polymerization method.The electric and optic properities of the resulting film were measured as a function of oxidant

dopant

substrate

reaction time and temperature.In proper condition

for the 0.5μm polyaniline film

the conductivity at room temperature and the transmittance at 450～650nm can be achived of 1～5S/cm and 80%

respectively.The growth mechnism and structure composition of polyaniline film were discussed.

关键词

浸渍聚合法聚苯胺透明导电薄膜

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS AND POLYMERIZATION MECHANISM OF POLYANILINE/TUNGSTEN CARBIDE COMPOSITES

PREPARATION AND CONDUCTIVE BEHAVIOR OF POLYANILINE/IONIC LIQUID/MONTIMORILLONITE NANOCOMPOSITES

SYNTHESIS AND INHIBITION STUDIES OF CARBOXYMETHL CHITOSAN DOPED POLIANILINE FOR MILD STEEL IN HYDROCHLORIC ACID

DOPING/DEDOPING PROCESS INDUCED WETTABILITY SWITCHING OF POLYANILINECOATED CONDUCTIVE TEXTILE

PREPARATION AND CHARACTERIZATION OF POLYIMIDF/POLYANILINE COMPOSITES

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰