SYNTHESIS OF BLOCK COPOLYMER OF ETHENE AND STYRENE WITH NOVEL TITANOCENE CATALYST

WANG Zhenghui; LIN Shangan

doi:null

您当前的位置：

首页 >

文章列表页 >

SYNTHESIS OF BLOCK COPOLYMER OF ETHENE AND STYRENE WITH NOVEL TITANOCENE CATALYST

Research Article | 更新时间：2021-03-19

- SYNTHESIS OF BLOCK COPOLYMER OF ETHENE AND STYRENE WITH NOVEL TITANOCENE CATALYST
- Acta Polymerica Sinica Issue 6, Pages: 720-724(1998)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 December 1998，
扫描看全文
WANG Zhenghui, LIN Shangan. SYNTHESIS OF BLOCK COPOLYMER OF ETHENE AND STYRENE WITH NOVEL TITANOCENE CATALYST. [J]. Acta Polymerica Sinica (6):720-724(1998)
DOI：

WANG Zhenghui, LIN Shangan. SYNTHESIS OF BLOCK COPOLYMER OF ETHENE AND STYRENE WITH NOVEL TITANOCENE CATALYST. [J]. Acta Polymerica Sinica (6):720-724(1998) DOI：

摘要

乙烯（Ｅ）与苯乙烯（Ｓ）的嵌段共聚合用自制的两种催化剂———茂基三呋喃甲氧基钛［ＣｐＴｉ（ＯＣＨ２Ｏ）３］和茂基三苄氧基钛［ＣｐＴｉ（ＯＣＨ２Ｐｈ）３］进行了研究．考察了促进剂三甲基铝（ＴＭＡ）及乙烯的预聚合时间对聚合结果的影响

发现不同的催化体系有不同的［ＴＭＡ］最佳值以及随着乙烯预聚合时间的延长总的催化效率降低．对嵌段共聚合产物用丁酮、四氢呋喃和氯仿连续萃取分离

得到四氢呋喃中的可溶级分即嵌段共聚物ＰＥ-ｂ-ｓＰＳ

它占总嵌段共聚合产物的４０ｗｔ％～６０ｗｔ％．对嵌段共聚物用ＤＳＣ、ＷＡＸＤ、ＦＴＩＲ和１３Ｃ-ＮＭＲ等方法进行了表征．

Abstract

The PE b sPS block copolymers were synthesized with η5 cyclopentadiencyltri furfuryloxyltitanium/MAO and η5 cyclopentadiencyltribenzyloxyltitanium/MAO catalyst systems respectively.The effect of TMA and ethene prepolymerization time on catalytic efficiency were investigated.The results showed that total catalytic efficiency came down with the increasing of ethene prepolymerization time and the TMA had a optimum value for different catalyst system.The PE b sPS block copolymers were obtained by butanone extraction fractionation.The PE-b-sPS block copolymers accounted for 40wt%～60wt% of the total copolymerization products and the weight content of styrene segment in the block copolymer is up to 80%～85%.The block copolymers were characterized by DSC

WAXD

DTIR and 13C-BMR methods.

关键词

嵌段共聚合ＰＥ-ｂ-ｓＰＳ表征

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

ULTRATHIN FILMS PREPARED FROM A POLYSTYRENEBASED-POLYMERIC DIAZONIUM SALT VIA LAYER-BY-LAYER SELF\|ASSEMbLY

pH-SENSITIVE POLY(ACRYLAMIDE-co-ACRYLIC ACID) MICROGELS PREPARED BY INVERSE MICROEMULSION POLYMERIZATION

Methacrylate-Based Side-Chain Liquid Crystal Copolymers Containing Biphenyl Mesogens and Cinnamate Groups

SYNTHESIS AND CHARACTERIZATION OF SOLUBLE POLYIMIDES CONTAINING PERFLUOROCYCLOBUTANE RINGS

PREPARATION AND PERFORMANCE OF NATURAL RUBBER/STYRENE-BUTADIENE RUBBER BASED SEPARATORS

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰