EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE)

FENG Lin-xian; FAN Zhi-qiang; XU Xiou-zhu; BO Yi-min; YANG Shi-lin

doi:null

您当前的位置：

首页 >

文章列表页 >

EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE)

Research Article | 更新时间：2021-03-19

- EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE)
- Acta Polymerica Sinica Issue 3, Pages: 349-354(1989)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 June 1989，
扫描看全文
FENG Lin-xian, FAN Zhi-qiang, XU Xiou-zhu, BO Yi-min, YANG Shi-lin. EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE). [J]. Acta Polymerica Sinica (3):349-354(1989)
DOI：

FENG Lin-xian, FAN Zhi-qiang, XU Xiou-zhu, BO Yi-min, YANG Shi-lin. EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE). [J]. Acta Polymerica Sinica (3):349-354(1989) DOI：

摘要

本文用GPC结合特性粘度的方法

对聚辛烯-1四氢呋喃体系的Mark-Houmink常数进行订定。数据处理采用了Weiss法和流体力学平均分子量(?)_x两种方法

α值分别为0.701和0.625

相对误差10％左右

所得Mark-Hon-Wink方程Weiss法为:[η]THF25℃=3.89×10-4[M]0.701(?)x法为[η]THF℃25=4.14×10-4M0'625。本文还研完了聚合反应条件对聚辛烯-1分子量及分子量分布的影响。发现三种TiCl3为主催化剂

三乙基铝为助催化剂时

其GPC谱图均为双峰型

两个峰的比例随聚合反应条件不同而变化。表明聚合体系至少有两种不同性质的活性中心

有着不同的形成和增长速率。

Abstract

The Mark-Houwink constants of poly (1-octene) in THF at 25℃ were evaluated from GPC and [η] of broad distribution samples. Two methods were used: calculation of K and a from the method developed by weiss and from the linear relation between in In[η] and InMx made by Goldwasser. More reliable results were obtained with the latter method. Determination of the molecular weight was made with the light scattering method

which gave Mw value close to that obtained from GPC. Then the Mark-Houwink equation for poly(1-octene) is [n]25℃THF×10-4M0.625. The effects of polymerization conditions on molecular weight distribution were studied with GPC. When AlEt3 was used as cocatalyst

the distribution was bi-modal. The change of alkyl aluminiums caused greater effect on the distrbutions than the cha-nge of TiCl3 strucure.

关键词

聚辛烯-1分子量分布Mark-Houwink常数

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

INFLUENCE OF MONOMER COMPOSITION ON THE CHAIN TRANSFER COEFFICIENT IN METHYL METHACRYLATE/BUTYL ACRYLATE RAFT COPOLYMERIZATION

SYNTHESIS OF ISOTACTIC POLYSTYRENE WITH MgCl2 SUPPORTED TITANIUM CATALYST AND STUDIES ON ITS MOLECULAR WEIGHT DISTRIBUTION

DETERMINING MOLECULAR WEIGHT DISTRIBUTION INDEX FROM FLOW CURVES FOR POLYPROPYLENE

RING-OPENING POLYM[ERIZATION OF PROPYLENE OXIDE INITIATED BY Fe-Zn DOUBLE METAL CYANIDE CATALYST

LIVING FREE RADICAL POLYMERIZATION USING ETHYL α BROMOBUTYRATE/CuBr/BIPYRIDINE AS INITIATOR SYSTEM

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰