STUDY ON BLEND MEMBRANE FROM REGENERATED CELLULOSE / POLYVINYL ALCOHOL

Research Article | 更新时间：2021-03-19

- STUDY ON BLEND MEMBRANE FROM REGENERATED CELLULOSE / POLYVINYL ALCOHOL
- Acta Polymerica Sinica Issue 2, Pages: 176-181(1994)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 1994，
扫描看全文
YANG Guang, ZHANG Li-na. STUDY ON BLEND MEMBRANE FROM REGENERATED CELLULOSE / POLYVINYL ALCOHOL. [J]. Acta Polymerica Sinica (2):176-181(1994)
DOI：

YANG Guang, ZHANG Li-na. STUDY ON BLEND MEMBRANE FROM REGENERATED CELLULOSE / POLYVINYL ALCOHOL. [J]. Acta Polymerica Sinica (2):176-181(1994) DOI：

摘要

由纤维素铜氨溶液与不同体积比（１－１０％）的聚乙烯醇（ＰＶＡ）水溶液共混制备了一系列再生纤维素共混膜．扫描电镜结果表明ＰＶＡ含量大于８％时，该共混膜产生明显相分离．当ＰＶＡ低于５％时，共混膜相容性较好．膜的结晶度，抗张强度，直角撕裂强度，断裂伸长及耐热性均优于单独用钢氨液制备的再生纤维素膜．此外，用流动速率法和超滤法测定了膜的孔径，渗透性及纯水通量，结果表明共混膜的孔性没有明显变化．本文得出：再生纤维素与５％ＰＶＡ共混能改善力学性能，并且能保持其生物降解性．

Abstract

egenerated cellulose blend membranes were prepared by coagulating a mixed solution of cellulose cuoxam (I) and aqueous polyvinyl alcohol (Ⅱ). SEM results showed that the phase separation on the mixing were seriously formed when the Ⅱ-content was higher than 8% by volume. But

when the Ⅱ-contCnt of blend was smaller than 5%

1 and Ⅱ are miscible

and the degree of crystallinity

tensile strength

tear strength

breaking elongation and thermostability of the blend membranes were superior to those of membrane from pure cellulose cuoxam. In addi-tion

the mean pore diameter

ethanol permeability and the transmembrane flows of water obtained by using a flow rate and ultrafiltration methods suggeted that the pore properties of the blend membranes were almost not variabe. In conclu-sion

the mechanical properties of blend membranes from regenerated cellu-lose / 5% polyvinyl alcohol were improved

and the blend membranes keep biodegradability yet.

关键词

再生纤维素共混膜力学性能孔性

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON THE TOUGHENED PVC BLENDS WITH NANO-CaCO3 PARTICLES AND ELASTIC CPE PARTICLES

Preparation of High Strength Zwitterionic Polymer Hydrogel Antifouling and Drag Reducing Coating

INVESTIGATION ON CRYSTALLIZATION AND MECHANICAL PROPERTIES OF POLY(BUTYLENE SUCCINATE)/NANO KAOLIN BLENDS

聚乳酸/乙烯-醋酸乙烯酯共聚物共混物的形态与黏弹行为

FILM-FORMING MECHANISM AND PROPERTIES OF KETONE HYDRAZINE CROSSLINKED AND SILANE COUPLED WATERBORNE POLYURETHANE

Related Author

No data

Related Institution

MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University

Zheda Institute of Advanced Materials and Chemical Engineering

扬州大学化学化工学院

扬州大学江苏省环境工程与环境材料重点实验室

扬州大学测试中心

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰