PHOTOCROSSLINKING REACTION OF THERMOTROPIC PHOTOSENSITIVE LIQUID CRYSTALLINE POLYMERS IN LIQUID CRYSTALLINE FIELD

WU Biyao; YAMASHITA Keiji; TSUDA Kazuich

doi:null

您当前的位置：

首页 >

文章列表页 >

PHOTOCROSSLINKING REACTION OF THERMOTROPIC PHOTOSENSITIVE LIQUID CRYSTALLINE POLYMERS IN LIQUID CRYSTALLINE FIELD

Research Article | 更新时间：2021-03-19

- PHOTOCROSSLINKING REACTION OF THERMOTROPIC PHOTOSENSITIVE LIQUID CRYSTALLINE POLYMERS IN LIQUID CRYSTALLINE FIELD
- Acta Polymerica Sinica Issue 1, Pages: 6-10(1996)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 February 1996，
扫描看全文
WU Biyao, YAMASHITA Keiji, TSUDA Kazuich. PHOTOCROSSLINKING REACTION OF THERMOTROPIC PHOTOSENSITIVE LIQUID CRYSTALLINE POLYMERS IN LIQUID CRYSTALLINE FIELD. [J]. Acta Polymerica Sinica (1):6-10(1996)
DOI：

WU Biyao, YAMASHITA Keiji, TSUDA Kazuich. PHOTOCROSSLINKING REACTION OF THERMOTROPIC PHOTOSENSITIVE LIQUID CRYSTALLINE POLYMERS IN LIQUID CRYSTALLINE FIELD. [J]. Acta Polymerica Sinica (1):6-10(1996) DOI：

摘要

研究了具有肉桂酸酯侧链基的热致型液晶高分子的光交联行为．结果表明

在２０ｍｉｎ紫外光照射的条件下

形成液晶相的液晶高分子膜的光交联凝胶百分率要明显高于尚未形成液晶相的同种高分子膜．对形成液晶相的高分子膜

在环境温度低于液晶各向同性温度Ｔ时

温度对光交联凝胶百分率的影响甚微．这表明

由于液晶高分子中致介单元的聚集和有序排列形成的微区结构也影响了大分子链侧基肉桂酸酯的聚集状态．从而使其光化学性质发生变化．

Abstract

ehavior of photocrosslinking reaction of side-chain liquid crystalline copolymer P(MPAEB-co-VBC)and P(MPAHB-co-VBC) was investigated.When the sample membrane was irradiated by ultraviolet ray at room temperature for 20 minutes

the percent of gel for quenched membrane was higher than unquenched one for both P (MPAEB-co-VBC)and P(MPAHB-co-VBC)

but did not change for homopolymer.When the temperature of samples was changed from room temperature to 100℃

there was not dear difference in percent of gel for quenched P(MPAEB-co-VBC)and P(MPAEB-co-VBC) membranes.It was concluded from these obsrcations

that because of ordered arrangement of mesogen grous in L.C.copolymer

physicocrosslinking macromolecules

which had domain structre

was formed.The domain structure could influence aggregational condition of cinnamate groups in the L.C. polymer chains and resulted in different characteristics from amorphous one.

关键词

液晶高分子光交联反应凝胶化

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS,CHARACTERIZATION AND PROPERTIES OF POLY(p-PHENYLENEETHYNYLENE)CONJUGATED POLYMERS CONTAINING LIQUID CRYSTAL GROUPS

DYNAMIC LIGHT SCATTERING STUDIES OF SOL-GEL TRANSITION IN AQUEOUS ALGINATE SOLUTION INDUCED BY CALCIUM CATIONS

ULTRASONIC SYNTHESIS OF POLY[2-METHOXY-5-(2′-ETHYLHEXYLOXY)-p-PHENYLENEVINYLENE]

THE RHEOLOGICAL ANALYSIS OF GELATION KINETICS FOR PARTIAL HYDROLYZED POLYACRYLAMIDE WEAK GEL

SYNTHESIS AND CHARACTERIZATION OF SCHIFF BASE TYPE LIQUID CRYSTALLINE POLYMERS WITH CROWN ETHER CYCLE

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰