SYNTHESIS OF iPS-b -iPP BLOCK COPOLYMER WITH SN CATALYST Ⅰ.EFFECT OF POLYMERIZATION PARAMETERS ON SEQUENTIAL BLOCK COPOLYMERIZATION OF STYRENE WITH PROPYLENE

XU Guangxue; UN Shang' an

doi:null

您当前的位置：

首页 >

文章列表页 >

SYNTHESIS OF iPS-b -iPP BLOCK COPOLYMER WITH SN CATALYST Ⅰ.EFFECT OF POLYMERIZATION PARAMETERS ON SEQUENTIAL BLOCK COPOLYMERIZATION OF STYRENE WITH PROPYLENE

Research Article | 更新时间：2021-03-19

- SYNTHESIS OF iPS-b -iPP BLOCK COPOLYMER WITH SN CATALYST Ⅰ.EFFECT OF POLYMERIZATION PARAMETERS ON SEQUENTIAL BLOCK COPOLYMERIZATION OF STYRENE WITH PROPYLENE
- Acta Polymerica Sinica Issue 4, Pages: 416-422(1996)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 August 1996，
扫描看全文
XU Guangxue, UN Shang' an. SYNTHESIS OF iPS-b -iPP BLOCK COPOLYMER WITH SN CATALYST Ⅰ.EFFECT OF POLYMERIZATION PARAMETERS ON SEQUENTIAL BLOCK COPOLYMERIZATION OF STYRENE WITH PROPYLENE. [J]. Acta Polymerica Sinica (4):416-422(1996)
DOI：

XU Guangxue, UN Shang' an. SYNTHESIS OF iPS-b -iPP BLOCK COPOLYMER WITH SN CATALYST Ⅰ.EFFECT OF POLYMERIZATION PARAMETERS ON SEQUENTIAL BLOCK COPOLYMERIZATION OF STYRENE WITH PROPYLENE. [J]. Acta Polymerica Sinica (4):416-422(1996) DOI：

摘要

用稀土化合物改性的钛系载体催化剂（ＳＮ催化剂）进行苯乙烯和丙烯顺序嵌段共聚合（Ｓｅｑｕｅｎｔｉａｌｂｌｏｃｋｃｏｐｏｌｙｍｅｒｉｚａｔｉｏｎ）的研究．考察了苯乙烯预聚时间、单体比、外加给电子体（ＥＢ）、烷基铝浓度、催化剂浓度和聚合温度等条件对共聚合的影响．发现外加酯（ＥＢ）降低了共聚合反应催化活性

在ＥＢ／Ｔｉ摩尔比为５范围内

外酯有助于提高嵌段共聚物（ｉＰＳ—ｂ—ｉＰＰ）中ＰＳ段和ＰＰ段的等规度及增加苯乙烯链节含量．ＳＮ型催化剂对苯乙烯一丙烯嵌段共聚合有较高的催化活性

催化效率在１００ｇ聚合物／ｇ－Ｔｉ以上．共聚物通过溶剂革取分级除去均聚物后

所得嵌段共聚物中苯乙烯链节含量可在１５～８５ｍｏｌ％之间调节．其结构表征续见第ＩＩ报．

Abstract

Sequential block copolymerization of styrene with prOPylene were carried out with TiO4-NdojOR)

/MgCl2 /Ph2SiO2 / EB catalyst (called SN catalyst) which was developed in our laboratory. The influence of various polymerization conditions such as styrene prepolymerization time

monomer feed ratio

extend donor (EB)

Al(iBu). concentration

catalyst concentration and temperature on the copolymerization were studied in detail' Ethyl benzoate was found to reduce the activity of the catalyst.A much higher incorporation of styrene and higher stereoregularity of each segments of copolymer

however

were observed within mole ratio EB/Ti=5;while futher addition of EB reduced incorporation of styrene and suppressed the stereospecificity of PS segment. SN catalyst was found to give higher catalytic yield (over 1000gP/gTi) and conversion yield of styrene.The styene-units of copolymer obtained were whithin 15 to 85 mile%

depending upon the polymerization conditions.

关键词

Ｚｉｅｇｌｅｒ—Ｎａｔｔａ催化剂苯乙烯一丙烯共聚物苯乙烯丙烯

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS OF iPS-b-iPP BLOCK COPOLYMER WITH HIGH FUNCTIONAL ACTIVE SN CATALYST lI．STRUCTURAL CHARACITERIZATION AND PROPERTIES OF iPS-b-iPP BIXNLX COPOLYMER

PREPARATION AND PERFORMANCE OF MODIFIED POLYVINYLIDENE FLUORIDE MEMBRANES GRAFTED WITH SULFONATED POLY(STYRENE-co-ACRYLIC ACID)

RAFT ALTERNATING COPOLYMERIZATION OF STYRENE AND N-SUBSTITUTED MALEIMIDES

SYNTHESIS OF aPs-b-P(S-co-E)-b-PE BLOCK COPOLYMERSCATALYZED WITH HALF-TITANOCENE/Zn/BDGE/MAO CATALYST SYSTEM

MINIEMULSION COPOLYMERIZATION OF γ-METHACRYLOXYPROPYLTRIMETHOXYSILANE AND STYRENE INITIATED BY OIL-SOLUBLE AND WATER-SOLUBLE INITIATORS

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰