THE COORDINATION CROSS-LINKAGE REACTION BETWEEN PVA IN STRONG BASIC AQUEOUS SOLUTION WITH Fe(III) ION

CHENG Chuan-xuan; ZHUANG Jin-shu; SU Ying-cao

doi:null

您当前的位置：

首页 >

文章列表页 >

THE COORDINATION CROSS-LINKAGE REACTION BETWEEN PVA IN STRONG BASIC AQUEOUS SOLUTION WITH Fe(III) ION

Research Article | 更新时间：2021-03-19

- THE COORDINATION CROSS-LINKAGE REACTION BETWEEN PVA IN STRONG BASIC AQUEOUS SOLUTION WITH Fe(III) ION
- Acta Polymerica Sinica Issue 2, Pages: 144-150(1993)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：20 April 1993，
扫描看全文
CHENG Chuan-xuan, ZHUANG Jin-shu, SU Ying-cao. THE COORDINATION CROSS-LINKAGE REACTION BETWEEN PVA IN STRONG BASIC AQUEOUS SOLUTION WITH Fe(III) ION. [J]. Acta Polymerica Sinica (2):144-150(1993)
DOI：

CHENG Chuan-xuan, ZHUANG Jin-shu, SU Ying-cao. THE COORDINATION CROSS-LINKAGE REACTION BETWEEN PVA IN STRONG BASIC AQUEOUS SOLUTION WITH Fe(III) ION. [J]. Acta Polymerica Sinica (2):144-150(1993) DOI：

摘要

在不断搅拌1×10-4m3 pH>13的5％ PVA碱性水溶液中

缓慢地添加1×10-4kgFeCl36H2O

溶液中即析出红棕色树胶状物.以XPS、ESR和IR等研究该析出物的组分及其形成过程.推定PVA部分羟基在上述条件下发生脱质子反应而提供L-配位体

Fe(Ⅲ)盐水解生成初生Fe(OH)3的Fe3+

它既有空轨道

又有较强的正电场

故能吸引PVA高分子配位体L-上的氧而形成O→Fe配位键

从而发生L-与Fe3+离子间的交联反应

生成多核Fe(Ⅲ)-PVA配位聚合物而析出红棕色树胶状物。

Abstract

The reddish brown resinoid substance was separated out

when 1×10-4kg of FeCl36H2O was added slowly to 1×10-4m3 of 5% PVA basic (pH>13) aqueous solution with stirring. Its composition and forming process was studied by XPS

IR and ESR

etc. It follows that the de-protonic reaction of hydroxide group for PVA had taken place in above solution

and the coordination group for deprotonic oxygen of PVA had produced more. These ligands interact with some Fe3+ of ferric hydroxide while the ferric hydroxide in new emergence is forming

causing the formation of Fe (III)-PVA coordination polymer-the composition of the reddish brown resinoid substance.

关键词

聚乙烯醇初生氢氧化铁配位聚合物

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS OF PAMPSPAM DOUBLE NETWORK HYDROGELS MODIFIED BY PVA WITH SUPER HIGH MECHANICAL PROPERTIES

STUDIES ON PROPERTIES OF PVA FILM PLASTICIZED WITH MIXTURE OF UREA/ETHANOLAMINE

STRUCTURE AND RHEOLOGICAL PROPERTIES OF POLY(VINYL ALCOHOL) HYDROGELS OBTAINED BY FREEZING/THAWING CYCLES

PREPARATION AND FLUORESCENCE PROPERTIES OFSAMARIUM COMPLEXES CONTAINING POLYARYLETHERKETONES BEARING PENDANT CARBOXYL GROUPS

COMPOSITION AND MICRO-MORPHOLOGY OF POROUS PVA HYDROGELS AND THEIR POISSON’S RATIO AND MECHANICAL PROPERTIES

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰