- INVESTIGATION ON THE MORPHOLOGY AND MOLECULAR MOTIONS OF THE in-situ STRETCHED POLY(ETHER-ESTER) BY SOLID-STATE HIGH-RESOLUTION 13C-NMR SPECTROSCOPY
- 高分子学报 2005年第3期页码：432-436
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2005-6-20，
扫描看全文
林伟信, 张莉莉, 张惠平, 陈群. 拉伸状态下弹性聚醚酯聚集态结构和分子运动的固体高分辨核磁共振研究[J]. 高分子学报, 2005,(3):432-436.

LIN Weixin, ZHANG Lili, ZHANG Huiping, CHEN Qun. INVESTIGATION ON THE MORPHOLOGY AND MOLECULAR MOTIONS OF THE in-situ STRETCHED POLY(ETHER-ESTER) BY SOLID-STATE HIGH-RESOLUTION 13C-NMR SPECTROSCOPY[J]. Acta Polymerica Sinica, 2005,(3):432-436.
林伟信, 张莉莉, 张惠平, 陈群. 拉伸状态下弹性聚醚酯聚集态结构和分子运动的固体高分辨核磁共振研究[J]. 高分子学报, 2005,(3):432-436. DOI：

LIN Weixin, ZHANG Lili, ZHANG Huiping, CHEN Qun. INVESTIGATION ON THE MORPHOLOGY AND MOLECULAR MOTIONS OF THE in-situ STRETCHED POLY(ETHER-ESTER) BY SOLID-STATE HIGH-RESOLUTION 13C-NMR SPECTROSCOPY[J]. Acta Polymerica Sinica, 2005,(3):432-436. DOI：

摘要

用固体高分辨核磁共振碳谱方法对不同拉伸比的聚醚酯嵌段共聚物的聚集态结构和分子运动进行了研究

发现共聚物中的聚四氢呋喃(PTMO)链段在拉伸比为20时开始就出现结晶

且结晶度和晶片厚度都随着拉伸比增加而明显增加

而样品中未结晶部分的高频分子运动随拉伸比的变化则不明显

拉伸导致的PTMO结晶主要发生在“纯”的PTMO非晶区.通过1H自旋扩散实验

估算出在拉伸比为4.0倍时

PTMO非晶区与结晶区的界面层厚度为1.1nm

PTMO非晶区与硬段的结晶区的界面厚度约为3.1nm.

Abstract

The morphollgy and molecular motion of in situ stretched poly (ether-ester) samples were studied by high-resolution solid-state 13C-NMR techniques Stretch-induced crystallization of the soft segment

i．e．ploy-(tetramethylene oxide)(PTMO)

was observed at a draw ratio of 2.0．The degree of erystallinity of PTMO and the lamellar thickness of the crystallites were found to increase with increasing of draw ratio．The molecular motion at high frequency of the amorphous PTMO was found to be almost independent on the draw ratio．It was demonstrated that the stretch-induced crystallization mainly happens in the“pure”PTMO region．1H spin diffusion experiment was carried out on the sample with the draw ratio of 4.0．The thickness of the interfacial region between the amorphous and crystalline PTMO of the sample was estimated to be 1.1 nm

while that between the amorphous PTMO and the erystalline hard domain to be 3.1 nm．

关键词

聚醚酯原位拉伸固体高分辨核磁共振聚集态结构分子运动

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

聚氧乙烯-高氯酸锂-水复合物体系的固体核磁共振研究

乙烯-丙烯酸共聚物非晶区结构和分子运动的固体核磁共振研究

聚(3-羟基丁酸酯)/聚氧化乙烯共混物非晶区相容性的固体核磁共振研究

聚丙烯材料聚集态结构的定量表征及其与力学性能的关系

聚醚酯嵌段共聚物熔体的流变性能