α-环糊精准轮烷/N-异丙基丙烯酰胺交联共聚温敏型超分子结构水凝胶的制备与表征

魏宏亮; 于怀清; 朱凯强; 钱立军; 张爱英; 冯增国

doi:null

您当前的位置：

首页 >

文章列表页 >

α-环糊精准轮烷/N-异丙基丙烯酰胺交联共聚温敏型超分子结构水凝胶的制备与表征

研究论文 | 更新时间：2021-03-19

- α-环糊精准轮烷/N-异丙基丙烯酰胺交联共聚温敏型超分子结构水凝胶的制备与表征
- PREPARATION OF THERMOSENSITIVE AND SUPRAMOLECULAR STRUCTURED HYDROGEL BY COPOLYMERIZATION OF PHOTOCURABLE POLYPSEUDOROTAXANES BASED ON α-CYCLODEXTRINS WITH N-ISOPROPYLACRYLAMIDE AND ITS CHARACTERIZATION
- 高分子学报 2006年第4期页码：581-587
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2006-7-20，
扫描看全文
魏宏亮, 于怀清, 朱凯强, 钱立军, 张爱英, 冯增国. α-环糊精准轮烷/N-异丙基丙烯酰胺交联共聚温敏型超分子结构水凝胶的制备与表征[J]. 高分子学报, 2006,(4):581-587.

WEI Hongliang, YU Huaiqing, ZHU Kaiqiang, QIAN Lijun, ZHANG Aiying, FENG Zengguo. PREPARATION OF THERMOSENSITIVE AND SUPRAMOLECULAR STRUCTURED HYDROGEL BY COPOLYMERIZATION OF PHOTOCURABLE POLYPSEUDOROTAXANES BASED ON α-CYCLODEXTRINS WITH N-ISOPROPYLACRYLAMIDE AND ITS CHARACTERIZATION[J]. Acta Polymerica Sinica, 2006,(4):581-587.
魏宏亮, 于怀清, 朱凯强, 钱立军, 张爱英, 冯增国. α-环糊精准轮烷/N-异丙基丙烯酰胺交联共聚温敏型超分子结构水凝胶的制备与表征[J]. 高分子学报, 2006,(4):581-587. DOI：

WEI Hongliang, YU Huaiqing, ZHU Kaiqiang, QIAN Lijun, ZHANG Aiying, FENG Zengguo. PREPARATION OF THERMOSENSITIVE AND SUPRAMOLECULAR STRUCTURED HYDROGEL BY COPOLYMERIZATION OF PHOTOCURABLE POLYPSEUDOROTAXANES BASED ON α-CYCLODEXTRINS WITH N-ISOPROPYLACRYLAMIDE AND ITS CHARACTERIZATION[J]. Acta Polymerica Sinica, 2006,(4):581-587. DOI：

摘要

采用一锅法合成了甲基丙烯酰基封端的聚乳酸-聚乙二醇-聚孔酸(PLA-PEG-PLA)三嵌段大分子单体

然后再通过与α-环糊精进行超分子自组装

得到聚准轮烷.将制备的聚准轮烷悬浮在N-异丙基丙烯酰胺水溶液中

再加入适量的光引发剂

在紫外光的照射下

溶液快速固化

得到了具有超分子结构的温敏型凝胶体.采用FTIR、TG、XRD等分析手段对所得聚准轮烷及其水凝胶进行了表征.

Abstract

The macromer of PLA—PEG-PIA terminated with methacryloyl moieties was prepared by one—pot procedure in high yield

both the ring-opening polymerization of L—lactide and end—capped reaction with methacrylie anhydride were carried out in toluene under nitrogen atmosphere at 120℃．Then the polypseudorotaxanes were obtained through supramolecular self-assemblies between α—CDs and the macromer．Afterwards

the resultant polypseudomtaxanes were suspended in aqueous solution of N—isopropylacryamide(NIPA)in the presence of a photo—initiator．While exposed to UV irradiation

the suspension mixtures could be photopolymerized rapidly to give rise to the thermosensitive and supramolecular structured hydrogels．Their thermosensitivity was confirmed by the swelling ratio changes under different temperatures．The polypseudorotaxanes and hydrogels were characterized by FTIR

XRD and TG techniques．The studies on their potential use as biomedical materials are ongoing.

关键词

开环聚合光固化温敏型水凝胶超分子结构

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

亲电缩聚反应合成芳香环状低聚醚酮砜及其开环聚合

双聚己内酯封端苯胺三聚体三嵌段聚合物的合成与研究

聚(L-丙氨酸-co-羟丙-L-谷氨酰胺)无规共聚物的两亲性及其胶束行为研究

聚γ-缩水甘油醚氧丙基三甲氧基硅烷的合成与表征

ε-己内酯在咪唑型离子液体中开环聚合