- WAXD STUDIES ON LOW TEMPERATURE CRYSTALLIZATION BEHAVIOR OF THE CIS-1,4 POLYBUTADINE PREPARED WITH RARE-EARTH CATALYST SYSTEM
- 高分子学报 1988年第6期页码：416-421
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1988-12-20，
扫描看全文
张宏放, 莫志深, 魏学军, 张书香, 韩平. X-射线衍射法研究稀土顺-1,4-聚丁二烯低温结晶动力学[J]. 高分子学报, 1988,(6):416-421.

ZHANG Hong-fang, MO Zhi-shen, WEI Xue-jun, ZHANG Shu-xiang, Han Ping. WAXD STUDIES ON LOW TEMPERATURE CRYSTALLIZATION BEHAVIOR OF THE CIS-1,4 POLYBUTADINE PREPARED WITH RARE-EARTH CATALYST SYSTEM[J]. Acta Polymerica Sinica, 1988,(6):416-421.
张宏放, 莫志深, 魏学军, 张书香, 韩平. X-射线衍射法研究稀土顺-1,4-聚丁二烯低温结晶动力学[J]. 高分子学报, 1988,(6):416-421. DOI：

ZHANG Hong-fang, MO Zhi-shen, WEI Xue-jun, ZHANG Shu-xiang, Han Ping. WAXD STUDIES ON LOW TEMPERATURE CRYSTALLIZATION BEHAVIOR OF THE CIS-1,4 POLYBUTADINE PREPARED WITH RARE-EARTH CATALYST SYSTEM[J]. Acta Polymerica Sinica, 1988,(6):416-421. DOI：

摘要

本文用广角X-射线衍射法(WAXD)研究了稀土催化聚合顺-1

4-聚丁二烯(Ln-PB)低温下分子量和温度对结晶过程的影响.随着分子量的改变

结晶速度在Mη=8×105左右有一极小值;在Mη=29×105左右有一极大值.最大结晶速度发生在Tc

max=-60～-70℃之间.最大平衡结晶度值

在Mη大于106以上与分子量无关

而最大平衡结晶度值所对应的温度与Mη呈线性关系.随着温度上升

晶胞参数略有增大.Ln-PB主级结晶属于非均相成核

以原纤状和盘状混合生长.

Abstract

The effects of molecular weight and temperature on crystallization processes at low temperature for cis-l

4-polybutadine prepared with rare-earth catalyst (Ln-PB) have been studied by WAXD method. In the range of molecular weight from Mη≈2.13×105 to 46.8×105 there are a maximum of crystallization rate at Mη≈29 × 105 and a minimum at Mη≈8×105. The temperature related to maximum crystallization rate

max is observed to be between -60℃ and -70℃. The degree of equilibrium crystallinity of Ln-PB is independent of mo-lecular weight at Mn greater than 106

also the linearity is shown between the correspondent remperature

degree of equilibrium crystallinity and molecular weight. Values of unit cell pa-rameters of Ln-PB increase with temperature. The main crystallzation of Ln-PB belongs to heterogeneous nucleation. The crystallization processes are mixed growth one and two di-mensions.

关键词

广角X-射线衍射结晶速率非均相成核平衡结晶度聚丁二烯

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

机理转移法合成聚丁二烯-b-聚(甲基丙烯酸N，N-二甲氨基乙酯)两亲性嵌段共聚物

石蜡或聚丁二烯填充型高吸油树脂的合成及其性能比较

原位插层聚合制备聚丁二烯/蒙脱土纳米复合材料的结构与性能研究

成核剂对聚2,6-萘二甲酸乙二酯结晶行为的影响

碳笼(C60/C70)载体钕系催化聚合丁二烯的研究　Ⅱ.聚合物分子量及其微观结构