- PREPARATION OF HIGH MOLECULAR WEIGHT POLY(p-DIOXANONE) BY CHAIN-EXTENSION
- Acta Polymerica Sinica Issue 12, Pages: 1201-1204(2007)
- 作者机构：
  
  1. 四川大学化学学院降解与阻燃高分子材料研究中心
  2. 四川大学化学学院降解与阻燃高分子材料研究中心,成都,610064
- 作者简介：
- 基金信息：
- DOI：
  CLC： O633.1
- Published：2007，
扫描看全文
[1]白春燕,丁颂东,刘中平,王玉忠.扩链法制备高分子量聚对二氧环己酮的研究[J].高分子学报,2007(12):1201-1204.

BAI Chunyan, DING Songdong, LIU Zhongping, WANG Yuzhong. PREPARATION OF HIGH MOLECULAR WEIGHT POLY(p-DIOXANONE) BY CHAIN-EXTENSION. [J]. Acta Polymerica Sinica (12):1201-1204(2007)
[1]白春燕,丁颂东,刘中平,王玉忠.扩链法制备高分子量聚对二氧环己酮的研究[J].高分子学报,2007(12):1201-1204. DOI：

BAI Chunyan, DING Songdong, LIU Zhongping, WANG Yuzhong. PREPARATION OF HIGH MOLECULAR WEIGHT POLY(p-DIOXANONE) BY CHAIN-EXTENSION. [J]. Acta Polymerica Sinica (12):1201-1204(2007) DOI：

摘要

以辛酸亚锡为催化剂对对二氧环己酮单体（PDO）开环聚合合成聚对二氧环己酮（PPDO）

在聚合的后期

用1

6-六亚甲基二异氰酸酯（HDI）为扩链剂进行扩链反应.研究了扩链剂用量对扩链反应的影响

加入相对于PPDO用量的0.78 wt%的HDI就能得到粘均分子量为2.35×105的PPDO.在分子量相近的情况下

扩链后产物的热稳定性和玻璃化转变温度均比未扩链的高

扩链前后的晶型没有发生变化

但结晶度大幅度降低

拉伸性能变化不大.

Abstract

High molecular weight biodegradable poly（ether ester）

poly（p-dioxanone）（PPDO）

has been prepared by chain-extending from its prepolymer using hexamethylene diisocyanate（HDI） as a chain extender.The ring-opening polymerization of p-dioxanone（PDO） using stannous octoate（SnOct

） as a catalyst was conducted at 125℃ for 3 h

and then a certain amount of HDI was added into the reactive system to react with the resulting PPDO prepolymer for an additional 30 min.The effect of the weight ratio of HDI to PPDO on the molecular weight of the chain-extended PPDO has been studied

and the results show that when the ratio is 0.78 wt%

higher molecular weight PPDO can be obtained

demonstrating that HDI is an effective extender for PPDO.The thermal degradation behaviors of PPDO and chain-extended polymer（PPDO-HDI） in air have been investigated by TG.The results show that the thermal stability of PPDO-HDI is higher than that of PPDO.Differntial scanning calorimetry（DSC） and wide angle X-ray diffractometry（WXRD） have been utilized to investigate the crystallization behavior of PPDO-HDI and PPDO.There exists no obvious difference between the crystal structures of PPDO-HDI and PPDO

however

the crystallinity of PPDO-HDI decreases to 33% from 60% of PPDO;the melting point of PPDO-HDI decreases a little and its glass transition temperature increases compared with those of PPDO.Moreover

the tensile strength and the elongation at break of PPDO-HDI are 36 MPa and 464%

respectively

almost the same as those of PPDO.

关键词

聚对二氧环己酮16-六亚甲基二异氰酸酯扩链热稳定性结晶拉伸性能

Keywords

(Poly(p-dioxanone)) Hexamethylene diisocyanateChain-extensionThermal stabilityCrystallizationTensile property

references

更多指标>

Views

326

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of Low-shrinkage Polypropylene by Tailoring Crystallization

Preparation of High Performance Dielectric Elastomers by Tailoring the Aggregation Structure of Polyurethane

The Effect of Lamellar Thickness of iPP on the Formation of Trigonal Modification of PB-1 under Confinement Environment

Thermogravimetric Analysis and Its Applications in Polymer Characterization

Regulating the Crystallization Behaviors of High-molecular-weight Poly(lactic acid) Stereocomplex System Based on the Structure of Poly(ethylene glycol)

Related Author

No data

Related Institution

College of Polymer Science and Engineering, State Key Laboratory of Polymer Materials Engineering, Sichuan University

SINOPEC Beijing Research Institute of Chemical Industry

Bohai Rim Collaborative Innovation Center on Green Chemical Application Technology, Department of Chemical Engineering, Weifang Vocational College

Key Laboratory of Rubber-Plastics, Ministry of Education/Shandong Provincial Key Laboratory of Rubber-plastics, School of Polymer Science and Engineering, Qingdao University of Science & Technology

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰