Preparation of High Hydrophilic PTFE Powder and Its Dispersion Stability

Li Hui; Zeng Hong-yan; Xing Zhe; Li Rong; Gao Qian-hong; Wang Hong-long; Wu Guo-zhong

doi:10.11777/j.issn1000-3304.2016.16009

您当前的位置：

首页 >

文章列表页 >

Preparation of High Hydrophilic PTFE Powder and Its Dispersion Stability

Research Article | 更新时间：2021-03-19

- Preparation of High Hydrophilic PTFE Powder and Its Dispersion Stability
- Acta Polymerica Sinica Issue 9, Pages: 1247-1253(2016)
- 作者机构：
  
  1. 湘潭大学化工学院,湘潭,411105
  2. 中国科学院上海应用物理研究所,上海,201800
- 作者简介：
- 基金信息：
- DOI：10.11777/j.issn1000-3304.2016.16009
  CLC：
- Published：1 September 2016，
扫描看全文
Li Hui, Zeng Hong-yan, Xing Zhe, Li Rong, Gao Qian-hong, Wang Hong-long, Wu Guo-zhong. Preparation of High Hydrophilic PTFE Powder and Its Dispersion Stability. [J]. Acta Polymerica Sinica (9):1247-1253(2016)
DOI：

Li Hui, Zeng Hong-yan, Xing Zhe, Li Rong, Gao Qian-hong, Wang Hong-long, Wu Guo-zhong. Preparation of High Hydrophilic PTFE Powder and Its Dispersion Stability. [J]. Acta Polymerica Sinica (9):1247-1253(2016) DOI： 10.11777/j.issn1000-3304.2016.16009.

摘要

通过预辐射接枝方法在聚四氟乙烯（PTFE）微粉上成功接枝丙烯酸（AAc）和2-丙烯酰胺-2-甲基丙磺酸（AMPS），制备了高亲水性的PTFE微粉.采用红外光谱（FTIR）、X射线光电子能谱（XPS）和接触角（CA）测试表征了改性PTFE微粉的化学结构和亲水性变化；采用扫描电子显微镜（SEM）观察改性PTFE微粉表面形貌；采用电泳法测试了改性PTFE微粉的zeta电位；通过热重分析（TGA）测试了辐射接枝对PTFE微粉热稳定性的影响.结果表明，改性PTFE微粉亲水性和分散稳定性随着接枝率的增加而增强；在单体浓度为20%，AAc与AMPS之比为2且反应温度为70℃时接枝率达到26.6%，此时改性样品PTFE-g-P（AAc-co-AMPS）在水溶液中的分散稳定性效果较好，并能够长期稳定存在.水接触角由改性前的148.8°下降到改性后的30.2°，对应的zeta电位从-4.3 mV降为-83.4 mV.

Abstract

Acrylic acid (AAc) and 2-acrylamide-2-methylpropanesulfonic acid (AMPS) were successfully grafted on polyterafluoroethylene (PTFE) powder by the fact that γ-ray radiation induced graft coploymerization for preparation of high hydrophilic PTFE powder.The chemical structure and hydrophilicity of the grafted PTFE powder were characterized by Fourier transform infrared spectrometer (FTIR)

X-ray photoelectron spectroscopy (XPS) and contact angle (CA)test.The surface morphology of the grafted PTFE powder was observed through scanning electron microscope (SEM).The electric potential of the grafted PTFE powder dispersion was determined by zeta potential test.The thermal stability of the grafted PTFE powder was analyzed by thermogravimetric analysis (TGA).It was found that the hydrophilicity and dispersion stability of modified PTFE powder was significantly improved with increasing grafting yield of AAc and AMPS.The PTFE powder with a grafting yield of 26.6% can be stably dispersed in water for a long period

which was prepared in the solution with the monomer concerntration of 20% and the AAc/AMPS ratio of 2 at 70℃.Water contact angle of the PTFE powder decreased from 148.8° before grafting to 30.2° after grafting.Simultaneously

the corresponding zeta potential of PTFE dispersion decreased from-4.3 mV to-83.4 mV.

关键词

聚四氟乙烯丙烯酸2-丙烯酰胺-2-甲基丙磺酸亲水性预辐射接枝

Keywords

PTFEAcrylic acid2-Acrylamide-2-methylpropanesulfonic acidHydrophilicPre-irradiation grafting

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Controllable Construction of Acrylic Composite Coatings with Impedance Gradient Structure for Low-reflectivity Electromagnetic Shielding in 5G High Frequency Band

Synthesis and Properties of Hydrophilic Poly(propylene carbonate) under UV Irradiation

Micellization Behavior of Poly(vinylidene chloride-methyl acrylate)-b-Poly(acrylic acid) Block Copolymers

PREPARATION AND CHARACTERIZATION OF CHITOSAN COATED MAGNETIC NANOPARTICLES AND THEIR BSA ADSORPTION PROPERTIES

Related Author

No data

Related Institution

College of Chemistry and Materials Engineering, Ministry of Education, Jiangnan University

Key Laboratory of Synthesis and Biocolloid, Ministry of Education, Jiangnan University

State Key Laboratory of Chemical Engineering, East China University of Science and Technology

College of Materials and Energy, South China Agricultural University

State Key Laboratory of Chemical Engineering, College of Chemical and Biological Engineering, Zhejiang University

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰