Effect of Grafted Imidazolium Cations on Crystallization Behavior of Polylactide

Hai-li Wang; Yi-yang Zhou; Hua-gao Fang; Yu Li; Pei Xu; Yun-sheng Ding; Zhi-gang Wang

doi:10.11777/j.issn1000-3304.2016.16075

您当前的位置：

首页 >

文章列表页 >

Effect of Grafted Imidazolium Cations on Crystallization Behavior of Polylactide

Research Article | 更新时间：2021-03-19

- Effect of Grafted Imidazolium Cations on Crystallization Behavior of Polylactide
- Acta Polymerica Sinica Issue 11, Pages: 1606-1614(2016)
- 作者机构：
  
  1.合肥工业大学化学与化工学院先进功能材料与器件安徽省重点实验室合肥 230009
  2.中国科学院软物质化学重点实验室中国科学技术大学高分子科学与工程系合肥微尺度国家重点实验室合肥 230026
- 作者简介：
- 基金信息：
- DOI：10.11777/j.issn1000-3304.2016.16075
  CLC：
- Published：2016-11，
  
  Received：30 March 2016，
  
  Revised：30 May 2016，
扫描看全文
Hai-li Wang, Yi-yang Zhou, Hua-gao Fang, Yu Li, Pei Xu, Yun-sheng Ding, Zhi-gang Wang. Effect of Grafted Imidazolium Cations on Crystallization Behavior of Polylactide. [J]. Acta Polymerica Sinica (11):1606-1614(2016)
DOI：

Hai-li Wang, Yi-yang Zhou, Hua-gao Fang, Yu Li, Pei Xu, Yun-sheng Ding, Zhi-gang Wang. Effect of Grafted Imidazolium Cations on Crystallization Behavior of Polylactide. [J]. Acta Polymerica Sinica (11):1606-1614(2016) DOI： 10.11777/j.issn1000-3304.2016.16075.

摘要

聚乳酸(PLA)受到伽马射线辐照发生降解，加入1-烯丙基-3-甲基咪唑氯盐(AMIMCl)与PLA发生接枝反应，可缓解其降解，得到咪唑阳离子接枝聚乳酸(PLA-IM).核磁共振(NMR)和凝胶渗透色谱(GPC)测试结果表明和直接辐照样品(PLA-S)相比，PLA-IM端羟基含量显著下降，分子量为PLA-S的3倍.利用偏光显微镜(POM)和示差扫描量热仪(DSC)研究PLA-IM等温结晶行为，发现其结晶时仍呈现球晶形貌，晶体生长速度变化相对较小，主要仍受分子量的影响，在相同结晶温度时，PLA-S的晶体生长速度最快，其次是PLA-IM，而PLA-L最慢.咪唑阳离子接枝使PLA-IM成核密度显著提高，致使结晶动力学加快，当结晶温度≥125℃时，PLA-IM的半结晶时间小于低分子量的PLA-S.成核能力的提高是导致PLA-IM结晶动力学加速的主要原因.与共混物中离子液体降低PLA成核作用不同，PLA链上接枝阳离子后，离子相互作用有利于成核时高分子链段发生局部有序排列，促进晶核数目的提高.

Abstract

Polylactide (PLA) underwent molecular degradation when it was exposed to gamma ray radiation

the degradation was inhibited somehow in the presence of 1-allyl 3-methylimidazolium chloride (AMIMCl).The grafting reaction of AMIMCl on PLA chains occurred during the irradiation to obtain imidazolium cations grafted PLA (PLA-IM).The molecular masses and the contents of end groups of the resultant PLA samples were measured by gel permeation chromatography (GPC) and nuclear magnetic resonance (

H-NMR)

respectively.Compared with the PLA sample irradiated without AMIMCl (PLA-S)

PLA-IM possessed less hydroxyl end groups and higher molecular mass (3 times as high as that of PLA-S).The nucleation and growth of crystalline during isothermal crystallization process were observed using polarized optical microscopy (POM).The results revealed that PLA-IM possessed spherulitic morphology which was same as other PLA samples

and the growth rate of the spherulites was mainly dependent on the molecular mass of PLA samples

demonstrating highest growth rate for PLA-S

followed by PLA-IM and lowest for PLA-L at the same crystallization temperature.However

different from PLA-L and PLA-S

PLA-IM showed increased nucleation density in the whole experimental temperature range due to the presence of grafted imidazolium cations on PLA chains.Isothermal crystallization kinetics for the PLA samples was then investigated by differential scanning calorimetry (DSC) and analyzed using Avrami equation.The results showed that the crystallization rate of PLA-IM had improved obviously because of its higher nucleation density.When the isothermal crystallization temperature was higher than 125℃

the half crystallization time of PLA-IM was shorter than that of PLA-S with lower molecular mass.Different from the retardant effect of ionic liquids (ILs) on PLA nucleation in PLA/ILs blends

the ionic interaction between the imidazolium cations grafted on PLA chains facilitates the orderly arrangement of PLA chains and formation of nuclei in the crystallization process

which contributes to the acceleration of crystallization kinetics.

关键词

聚乳酸咪唑阳离子接枝结晶成核

Keywords

PolylactideImidazolium cationGraftCrystallizationNucleation

references

J R Dorgan , H J Lehermeier , L I Palade , J Cicero . Macromol Symp , 2001 . 175 55 - 66 . DOI:10.1002/(ISSN)1521-3900http://doi.org/10.1002/(ISSN)1521-3900.

L T Lim , R Auras , M Rubino . Prog Polym Sci , 2008 . 33 820 - 852 . DOI:10.1016/j.progpolymsci.2008.05.004http://doi.org/10.1016/j.progpolymsci.2008.05.004.

H G Fang , F Jiang , Q H Wu , Y S Ding , Z G Wang . ACS Appl Mater Interfaces , 2014 . 6 13552 - 13563 . DOI:10.1021/am502735qhttp://doi.org/10.1021/am502735q.

C Y Hung , C C Wang , C Y Chen . Polymer , 2013 . 54 1860 - 1866 . DOI:10.1016/j.polymer.2013.01.045http://doi.org/10.1016/j.polymer.2013.01.045.

J Z Xu , T Chen , C L Yang , Z M Li , Y M Mao , B Q Zeng . Macromolecules , 2010 . 43 5000 - 5008 . DOI:10.1021/ma100304nhttp://doi.org/10.1021/ma100304n.

J Bai , J Y Wang , W T Wang , H G Fang , Z H Xu , X S Chen . Wang Z G,ACS Sustain Chem Eng , 2016 . 4 273 - 283 . DOI:10.1021/acssuschemeng.5b01110http://doi.org/10.1021/acssuschemeng.5b01110.

H G Fang , Y Q Zhang , J Bai , Z G Wang . Macromolecules , 2013 . 46 6555 - 6565 . DOI:10.1021/ma4012126http://doi.org/10.1021/ma4012126.

G M Liu , X Q Zhang , D J Wang . Adv Mater , 2014 . 26 6905 - 6911 . DOI:10.1002/adma.v26.40http://doi.org/10.1002/adma.v26.40.

Q Chen , S Liang , H S Shiau , R H Colby . ACS Macro Lett , 2013 . 2 970 - 974 . DOI:10.1021/mz400476whttp://doi.org/10.1021/mz400476w.

U H Choi , Y Ye , D Salas-de la Cruz , W Liu , K I Winey , Y A Elabd . Macromolecules , 2014 . 47 777 - 790 . DOI:10.1021/ma402263yhttp://doi.org/10.1021/ma402263y.

B K Chen , T Y Wu , Y M Chang , A F Chen . Chem Eng J , 2013 . 215 886 - 893.

T Y Wei , S J Pang , N Xu , L S Pan , Z Q Zhang , R Z Xu . J Appl Polym Sci , 2015 . 132 41308 - 41319.

J B Zeng , F Wu , C L Huang , Y S He , Y Z Wang . ACS Macro Lett , 2012 . 1 965 - 968 . DOI:10.1021/mz300243thttp://doi.org/10.1021/mz300243t.

S L Xing , P Tang , Y L Yang . J Appl Polym Sci , 2015 . 132 41240 - 41252.

H J Xu , H G Fang , J Bai , Y Q Zhang , Z G Wang . Ind Eng Chem Res , 2014 . 53 1150 - 1159 . DOI:10.1021/ie403669ahttp://doi.org/10.1021/ie403669a.

H G Fang , Y Q Zhang , J Bai , Z K Wang , Z G Wang . RSC Adv , 2013 . 3 8783 - 8795 . DOI:10.1039/c3ra40879ehttp://doi.org/10.1039/c3ra40879e.

A Babanalbandi , D J T Hill , J H Odonnell , P J Pomery , A Whittaker . Polym Degrad Stab , 1995 . 50 297 - 304 . DOI:10.1016/0141-3910(95)00150-6http://doi.org/10.1016/0141-3910(95)00150-6.

A Babanalbandi , D J T Hill , A K Whittaker . Polym Degrad Stab , 1997 . 58 203 - 214 . DOI:10.1016/S0141-3910(97)00050-5http://doi.org/10.1016/S0141-3910(97)00050-5.

P Nugroho , H Mitomo , F Yoshii , T Kume . Polym Degrad Stab , 2001 . 72 337 - 343 . DOI:10.1016/S0141-3910(01)00030-1http://doi.org/10.1016/S0141-3910(01)00030-1.

H Chen , C R Peng , Y Y Yao , J X Wang , Z P Chen , Z R Yang , L J Xia , S Y Liu . J Appl Polym Sci , 2009 . 114 3152 - 3157 . DOI:10.1002/app.v114:5http://doi.org/10.1002/app.v114:5.

H Mitomo , A Kaneda , T M Quynh , N Nagasawa , F Yoshii . Polymer , 2005 . 46 4695 - 4703 . DOI:10.1016/j.polymer.2005.03.088http://doi.org/10.1016/j.polymer.2005.03.088.

L Y Wang , X B Jing , H B Cheng , X L Hu , L X Yang , Y B Huang . Ind Eng Chem Res , 2012 . 51 10731 - 10741 . DOI:10.1021/ie300524jhttp://doi.org/10.1021/ie300524j.

S H Lee , K S Hyun , Y K Han , Y H Kim . J Polym Sci,Part A:Polym Chem , 2001 . 39 973 - 985.

D Garlotta . J Polym Environ , 2001 . 9 63 - 84 . DOI:10.1023/A:1020200822435http://doi.org/10.1023/A:1020200822435.

S Baratian , E S Hall , J S Lin , R Xu , J Runt . Macromolecules , 2001 . 34 4857 - 4864 . DOI:10.1021/ma001125rhttp://doi.org/10.1021/ma001125r.

J Bai , H G Fang , Y Q Zhang , Z G Wang . Crystengcomm , 2014 . 16 2452 - 2461 . DOI:10.1039/c3ce42319khttp://doi.org/10.1039/c3ce42319k.

Hikosaka M,Watanabe K,Okada K,Yamazaki S.Topological mechanism of polymer nucleation and growth-The role of chain sliding diffusion and entanglement.In:Allegra G,ed.Interphases and Mesophases in Polymer Crystallization.Berlin:Springer-Verlag Berlin,2005.137-186

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Studies on the Effects of Four-armed Poly(L-lactide) on the Crystallization Behavior of Four-armed Poly(L-lactide)/Linear Poly(L-lactide) Blends

Designed Multicomplexation Based on Asymmetric Polylactide Enantiomeric Blends: A Quantitative Study

Preparation and Application of Lignin Grafted Natural Rubber Initiated by CaCl₂/H₂O₂

Preparation of Low-shrinkage Polypropylene by Tailoring Crystallization

Related Author

No data

Related Institution

College of Polymer Science and Engineering, Sichuan University, State Key Laboratory of Polymer Materials Engineering

College of Chemistry and Chemical Engineering, Nanjing University

Xinyang Vocational College of Art

College of Chemical Engineering, Hebei University of Technology

Key Laboratory of Rubber-Plastics, Ministry of Education, Qingdao University of Science & Technology

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰