Preparation of Partly Fluorinated Anion Exchange Membranes with Side Chain Ionic Groups
via a Post-functionalization Process- Acta Polymerica Sinica Issue 12, Pages: 1974-1983(2017)
- 作者机构：
1.华南理工大学化学与化工学院 广州 510641
2.广东省燃料电池技术重点实验室 广州 510641
- 作者简介：
- 基金信息：
DOI：10.11777/j.issn1000-3304.2017.17059
CLC：Published：20 December 2017，
Received：25 March 2017，
Revised：2 May 2017，
扫 描 看 全 文
Jin-xiong Tao, Jun Feng, Biao-wen Wei, Shi-jun Liao, Xiu-hua Li. Preparation of Partly Fluorinated Anion Exchange Membranes with Side Chain Ionic Groups
via a Post-functionalization Process. [J]. Acta Polymerica Sinica (12):1974-1983(2017)Jin-xiong Tao, Jun Feng, Biao-wen Wei, Shi-jun Liao, Xiu-hua Li. Preparation of Partly Fluorinated Anion Exchange Membranes with Side Chain Ionic Groups
via a Post-functionalization Process. [J]. Acta Polymerica Sinica (12):1974-1983(2017) DOI： 10.11777/j.issn1000-3304.2017.17059.
摘要
以十氟联苯、双酚A低温聚合制备可高温官能化的聚合物主链，以3，5-二甲基苯酚为功能侧链，采用后官能化工艺制备了系列不同离子交换容量（IEC）值的含侧链苄基季铵基团的部分氟化阴离子交换膜.用GPC、
1
H-NMR、
19
F-NMR、IR、SASX等表征了膜的分子结构及聚集态结构，并且测试了膜的各种性能.结果表明，该系列部分氟化阴离子交换膜的分子主链线性好，官能度可控，具有明显的微相分离结构.部分氟化结构和微相分离的侧链离子结构极大的改善了膜的吸水溶胀性、电导率和化学稳定性.QFPAE-95膜具有最高的氢氧根离子电导率和适度吸水溶胀性，80℃时离子电导率和溶胀比分别达到108.6 mS cm
-1
和42.6%.QFPAE-55具有最大的拉伸强度，达到21.01 MPa.该系列膜还具有出色的碱稳定性，QFPAE-55膜在1 mol/L NaOH溶液中于60℃下浸泡20天后，其电导率和IEC值分别保持为原膜的82.3%和84.2%，有望作为新型阴离子交换膜并应用于碱性膜燃料电池.
Abstract
Controlled polycondensation of decafluorobiphenyl and bisphenol A at low temperature gave a highly linear polymer with its main chain consisting of octafluoro benzene moiety
which acted as grafting reaction position for post-functionalization at higher temperature. 3
5-dimethylphenol grafted onto the main chain of the mother polymer by partial elimination of the fluorine atoms in the octafluoro benzene moiety to form the ionomers precursor with side chain benzyl groups. The precursor transformed then into a series of partly fluorinated anion exchange membranes containing side chain benzyl quaternary ammonium groups with varying IEC values by bromination and quaternization. The participation of the ortho-and meta-fluorine atoms to the polycondensation
leading to the cross linking gelation
was successfully avoided through this method. Moreover
the method could achieve the controllable degree of functionalization by controlling the feed ratio of NBS to the benzyl groups in the precursor polymer. In addition
two benzyl groups on the side chains could be brominated and quaternized to form local domains of high density ionization
which could form ion clusters of microphase separation to increase the ion conductivity. The molecular structure and aggregation structure of the membranes were characterized by GPC
1
H-NMR
19
F-NMR
IR and SASX. The results confirmed that the precursor polymer of the partly fluorinated anion exchange membranes had a linear skeleton
adjustable functionality and the obtained membranes showed obvious microphase separation aggregation morphology. The results of the property evaluation indicated that the swelling ratio
ion conductivity and alkaline stability were greatly improved by the designed structure of the partly fluorinated main chain and the aromatic side chain ionic group. QFPAE-95 had the highest ion conductivity and appropriate swelling ratio with the values of 108.6 mS cm
-1
and 42.6% at 80℃ respectively. QFPAE-55 possessed the highest tensile strength of 21.01 MPa. Moreover
the series of membranes also showed excellent alkaline stability. The ion conductivity and IEC value of QFPAE-55 remained 82.3% and 84.2% of the values in the original membrane after being immersed into 1 mol/L NaOH solution at 60℃ for 20 days. The membranes are promising anion exchange membranes for alkaline fuel cells.
关键词
后官能化部分氟化侧链苄基季铵基团阴离子交换膜碱性膜燃料电池
Keywords
Post-functionalizationPartly fluorinatedSide chain benzyl quaternary ammonium groupsAnion exchange membranesAlkaline membrane fuel cells
references
L Zhu , J Pan , Y Wang , J J Han , L Zhuang , M A Hickner . Macromolecules , 2016 . 49 815 - 824 . DOI:10.1021/acs.macromol.5b02671http://doi.org/10.1021/acs.macromol.5b02671.
C Y Wang , C Xu , B Shen , X Y Zhao , J Li . Electrochim Acta , 2016 . 190 1057 - 1065 . DOI:10.1016/j.electacta.2015.12.181http://doi.org/10.1016/j.electacta.2015.12.181.
F J Jiang , Y Nie , L Yin , Y Feng , Q C Yu , C Y Zhong . J Membr Sci , 2016 . 510 1 - 9 . DOI:10.1016/j.memsci.2016.02.067http://doi.org/10.1016/j.memsci.2016.02.067.
S A Nuñez , C Capparelli , M A Hickner . Chem M , 2016 . 28 2589 - 2598 . DOI:10.1021/acs.chemmater.5b04767http://doi.org/10.1021/acs.chemmater.5b04767.
J C Chen , J A Wu , K H Chen . RSC Adv , 2016 . 6 33959 - 33970 . DOI:10.1039/C6RA00628Khttp://doi.org/10.1039/C6RA00628K.
Sh F Lu , J Pan , A B Huang , L Zhuang , J T Lu . China Basic Science , 2008 . 105 20611 - 20614.
J Ran , L Wu , Y B He , Z J Yang , Y M Wang , C X Jiang , L Ge , E Bakangura , T W Xu . J Membr Sci , 2017 . 522 267 - 291 . DOI:10.1016/j.memsci.2016.09.033http://doi.org/10.1016/j.memsci.2016.09.033.
X H Yan , R Z Wu , J B Xu , Z T Luo , T S Zhao . J Power Sources , 2016 . 311 188 - 194 . DOI:10.1016/j.jpowsour.2016.02.030http://doi.org/10.1016/j.jpowsour.2016.02.030.
R K Singh , K Kunimatsu , K Miyatake , T Tsuneda . Macromolecules , 2016 . 49 6621 - 6629 . DOI:10.1021/acs.macromol.6b00999http://doi.org/10.1021/acs.macromol.6b00999.
K Feng , L Liu , B B Tang , N W Li , P Y Wu . ACS Appl Mater Inter , 2016 . 8 11516 - 11525 . DOI:10.1021/acsami.6b02248http://doi.org/10.1021/acsami.6b02248.
Y J Wang , J L Qiao , R Baker , J J Zhang . Chem Soc Rev , 2013 . 42 5768 - 5787 . DOI:10.1039/c3cs60053jhttp://doi.org/10.1039/c3cs60053j.
J F Zheng , Q F Zhang , H D Qian , B X Xue , S H Li , S B Zhang . J Membr Sci , 2017 . 522 159 - 167 . DOI:10.1016/j.memsci.2016.09.021http://doi.org/10.1016/j.memsci.2016.09.021.
L Liu , S Q He , S F Zhang , M Zhang , M D Guiver , N W Li . ACS Appl Mater Inter , 2016 . 8 4651 - 4660 . DOI:10.1021/acsami.5b11519http://doi.org/10.1021/acsami.5b11519.
M Y Liu , Z Wang , J Mei , J M Xu , L S Xu , H L Han , H Z Ni , S Wang . J Membr Sci , 2016 . 505 138 - 147 . DOI:10.1016/j.memsci.2016.01.036http://doi.org/10.1016/j.memsci.2016.01.036.
T A Sherazi , S J Yong , L Y Moo , M D Guiver . J Membr Sci , 2013 . 441 148 - 157 . DOI:10.1016/j.memsci.2013.03.053http://doi.org/10.1016/j.memsci.2013.03.053.
Z J Yang , R Guo , R Malpass-Evans , M Carta , N B Mckeown , M D Guiver , L Wu , T W Xu . Angew Chem , 2016 . 128 11671 - 11674 . DOI:10.1002/ange.201605916http://doi.org/10.1002/ange.201605916.
X Dong , S H Hou , H C Mao , J F Zheng , S B Zhang . J Membr Sci , 2016 . 518 31 - 39 . DOI:10.1016/j.memsci.2016.06.036http://doi.org/10.1016/j.memsci.2016.06.036.
Dan Ning , Zhaoxia Hu , Rong Chen , Hanwen Chen , Hui Yang , Shouwen Chen . Acta Polymerica Sinica , 2017 . ( 5 ): 842 - 850 . http://www.gfzxb.org/CN/abstract/abstract14676.shtml.
宁 丹 , 胡 朝霞 , 陈 荣 , 陈 罕雯 , 杨 慧 , 陈 守文 . 高分子学报 , 2017 . ( 5 ): 842 - 850 . http://www.gfzxb.org/CN/abstract/abstract14676.shtml.
Rong Chen , Ang Li , Shichao Fang , Huiping Bi , Zhaoxia Hu , Shouwen Chen . Acta Polymerica Sinica , 2016 . ( 4 ): 436 - 442 . DOI:10.11777/j.issn1000-3304.2016.15225http://doi.org/10.11777/j.issn1000-3304.2016.15225http://www.gfzxb.org/CN/abstract/abstract14461.shtml.
陈 荣 , 李 昂 , 房 世超 , 毕 慧平 , 胡 朝霞 , 陈 守文 . 高分子学报 , 2016 . ( 4 ): 436 - 442 . DOI:10.11777/j.issn1000-3304.2016.15225http://doi.org/10.11777/j.issn1000-3304.2016.15225http://www.gfzxb.org/CN/abstract/abstract14461.shtml.
C Chen , Y S Tse , G E Lindberg , C Knight , G A Voth . J Am Chem Soc , 2016 . 138 991 - 1000 . DOI:10.1021/jacs.5b11951http://doi.org/10.1021/jacs.5b11951.
K A Nebavskaya , V V Sarapulova , K G Sabbatovskiy , V D Sobolev , N D Pismenskaya , P Sistat , M Cretin , V V Nikonenko . J Membr Sci , 2017 . 523 36 - 44 . DOI:10.1016/j.memsci.2016.09.038http://doi.org/10.1016/j.memsci.2016.09.038.
L Pasquini , Vona M L Di , P Knauth . New J Chem , 2016 . 40 3671 - 3676 . DOI:10.1039/C5NJ03212Ahttp://doi.org/10.1039/C5NJ03212A.
J F Zhou , M Ünlü , I Anestis-Richard , H Kim , P A Kohl . J Power Sources , 2011 . 196 7924 - 7930 . DOI:10.1016/j.jpowsour.2011.05.024http://doi.org/10.1016/j.jpowsour.2011.05.024.
X H Li , G H Nie , J X Tao , W J Wu , L C Wang , S J Liao . ACS Appl Mater Inter , 2014 . 6 7585 - 7595 . DOI:10.1021/am500915whttp://doi.org/10.1021/am500915w.
D Y Chen , M A Hickner . Macromolecules , 2013 . 46 9270 - 9278 . DOI:10.1021/ma401620mhttp://doi.org/10.1021/ma401620m.
S D Sajjad , Y Hong , F Q Liu . Polym Adv Technol , 2014 . 25 108 - 116 . DOI:10.1002/pat.v25.1http://doi.org/10.1002/pat.v25.1.
X H Li , Y F Yu , Q F Liu , Y Z Meng . ACS Appl Mater Inter , 2012 . 4 3627 - 3635 . DOI:10.1021/am3007005http://doi.org/10.1021/am3007005.
X H Li , Q F Liu , Y F Yu , Y Z Meng . J Membr Sci , 2014 . 467 1 - 12 . DOI:10.1016/j.memsci.2014.05.016http://doi.org/10.1016/j.memsci.2014.05.016.
X H Li , Q F Liu , Y F Yu , Y Z Meng . J Mater Chem A , 2013 . 1 4324 - 4335 . DOI:10.1039/c3ta00342fhttp://doi.org/10.1039/c3ta00342f.
Y B He , J J Si , L Wu , S L Chen , Y Zhu , J F Pan , X L Ge , Z J Yang , T W Xu . J Membr Sci , 2016 . 515 189 - 195 . DOI:10.1016/j.memsci.2016.05.058http://doi.org/10.1016/j.memsci.2016.05.058.
X Gong , X M Yan , T T Li , X M Wu , W T Chen , S Q Huang , Y Wu , D X Zhen , G H He . J Membr Sci , 2017 . 523 216 - 224 . DOI:10.1016/j.memsci.2016.09.050http://doi.org/10.1016/j.memsci.2016.09.050.
C X Lin , Y Z Zhuo , A N Lai , Q G Zhang , A M Zhu , Q L Liu . RSC Adv , 2016 . 6 17269 - 17279 . DOI:10.1039/C5RA22774Ghttp://doi.org/10.1039/C5RA22774G.
C X Lin , Y Z Zhuo , A N Lai , Q G Zhang , A M Zhu , M L Ye , Q L Liu . J Membr Sci , 2016 . 513 206 - 216 . DOI:10.1016/j.memsci.2016.04.054http://doi.org/10.1016/j.memsci.2016.04.054.
0
Views
11
下载量
0
CSCD
- L-PDFDownload
- BibTeXDownload
- EndnoteDownload
- RefMan Download
- NoteExpressDownload
- NoteFirstDownload
Publicity Resources
Related Articles
Related Author
Related Institution
- Postal code：100190
- Tel：010-62588927 Email：gfzxb@iccas.ac.cn
- Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8
京公网安备11010802024621 - It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
- Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.