FRONTAL POLYMERIZATION OF ACRYLAMIDE FOR PREPARING POROUS POLYACRYLAMIDE HYDRO GEL ——EFFECTS OF INITIATOR AND SOLVENT ON PROPAGATION AND PRODUCTS

FENG Qiao; LU Guodong; LIU Yuqiong; YAN Qingzhi; GE Ch angchun

doi:10.3724/SP.J.1105.2009.00674

您当前的位置：

首页 >

文章列表页 >

FRONTAL POLYMERIZATION OF ACRYLAMIDE FOR PREPARING POROUS POLYACRYLAMIDE HYDRO GEL ——EFFECTS OF INITIATOR AND SOLVENT ON PROPAGATION AND PRODUCTS

Research Article | 更新时间：2021-03-19

- FRONTAL POLYMERIZATION OF ACRYLAMIDE FOR PREPARING POROUS POLYACRYLAMIDE HYDRO GEL ——EFFECTS OF INITIATOR AND SOLVENT ON PROPAGATION AND PRODUCTS
- Acta Polymerica Sinica Issue 7, Pages: 674-679(2009)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2009.00674
  CLC：
- Published：20 July 2009，
扫描看全文
FENG Qiao, LU Guodong, LIU Yuqiong, YAN Qingzhi, GE Ch angchun. FRONTAL POLYMERIZATION OF ACRYLAMIDE FOR PREPARING POROUS POLYACRYLAMIDE HYDRO GEL ——EFFECTS OF INITIATOR AND SOLVENT ON PROPAGATION AND PRODUCTS. [J]. Acta Polymerica Sinica (7):674-679(2009)
DOI：

FENG Qiao, LU Guodong, LIU Yuqiong, YAN Qingzhi, GE Ch angchun. FRONTAL POLYMERIZATION OF ACRYLAMIDE FOR PREPARING POROUS POLYACRYLAMIDE HYDRO GEL ——EFFECTS OF INITIATOR AND SOLVENT ON PROPAGATION AND PRODUCTS. [J]. Acta Polymerica Sinica (7):674-679(2009) DOI： 10.3724/SP.J.1105.2009.00674.

摘要

利用前端聚合结合发泡工艺制备了孔结构可调控的聚丙烯酰胺多孔水凝胶.研究发现溶剂和引发剂浓度变化对聚合前端的移动及形成的产物性能有重要影响.增加溶剂用量，聚合前端的移动速度和聚合前端最高温度下降，产物孔径增大，孔壁变厚，材料吸水溶胀性能降低；增加引发剂浓度，聚合前端移动速度显著加快，最高温度升高，产物的孔体积和溶胀率先增加后减小.

Abstract

Porous polyacrylamide (PAM) hydrogels with tuned po re size were prepared by frontal polymerization(FP) combined with foaming proces s.S tudies were conducted to investigate the effect of initiator concentration and r eactant diluents on the most relevant parameters of FP and the performances of t he final products.A dilution of the reactants resulted in an obvious decrease o f the front velocity as well as the maximum temperature of front.The pore diameters and the wall thicknesses showed an uptrend when the water content increased

and the swelling pr operties of the final products reduced.A significant enhancement of the propagation velocity was noticed with increasing of initiator concentration.The size of pore and swelling degree were characterized by a constant increase when APS c oncentration increased

and then

a large decrease was noticed.At an initiator/mo nomer mass ratio of 0.022

the maximum pore volume was obtained.

关键词

前端聚合孔结构聚丙烯酰胺水凝胶

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDIES ON SODIUM HUMATE/POLYACRYLAMIDE/CLAY HYBRID HYDROGELS

PREPARATION AND PROPERTIES OF TEMPERATURE-SENSITIVE N-ISOPROPYLACRYLAMIDE COPOLYMER HYDROGELS CONTAINING ADAMANTYL GROUPS

STUDIES ON SWELLING BEHAVIOR OF POLY(ACRYLIC ACID-co-OCTADECYL METHACRYLATE) HYDROPHOBIC ASSOCIATION HYDROGELS WITH HIGH MECHANICAL PROPERTIES

STRUCTURE AND RHEOLOGICAL PROPERTIES OF POLY(VINYL ALCOHOL) HYDROGELS OBTAINED BY FREEZING/THAWING CYCLES

SYNTHESIS AND PROPERTIES OF FAST RESPONSIVE AND ELECTRICAL SENSITIVE POROUS HYDROGEL

Related Author

No data

Related Institution

浙江科技学院环境与资源学院

浙江大学高分子科学与工程学系高分子功能构造与合成教育部重点实验室

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰