SYNTHESIS AND PROPERTIES OF POLYPHENYLSILICONE AND POLYMETHYLPHENYLSILICONE MODIFIED EPOXY RESINS

LI Yinwen; SHEN Minmin; HUANG Huoyang; MA Yijing; HA Chengyong

doi:10.3724/SP.J.1105.2009.01086

您当前的位置：

首页 >

文章列表页 >

SYNTHESIS AND PROPERTIES OF POLYPHENYLSILICONE AND POLYMETHYLPHENYLSILICONE MODIFIED EPOXY RESINS

Research Article | 更新时间：2021-03-19

- SYNTHESIS AND PROPERTIES OF POLYPHENYLSILICONE AND POLYMETHYLPHENYLSILICONE MODIFIED EPOXY RESINS
- Acta Polymerica Sinica Issue 11, Pages: 1086-1090(2009)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2009.01086
  CLC：
- Published：20 November 2009，
扫描看全文
LI Yinwen, SHEN Minmin, HUANG Huoyang, MA Yijing, HA Chengyong. SYNTHESIS AND PROPERTIES OF POLYPHENYLSILICONE AND POLYMETHYLPHENYLSILICONE MODIFIED EPOXY RESINS. [J]. Acta Polymerica Sinica (11):1086-1090(2009)
DOI：

LI Yinwen, SHEN Minmin, HUANG Huoyang, MA Yijing, HA Chengyong. SYNTHESIS AND PROPERTIES OF POLYPHENYLSILICONE AND POLYMETHYLPHENYLSILICONE MODIFIED EPOXY RESINS. [J]. Acta Polymerica Sinica (11):1086-1090(2009) DOI： 10.3724/SP.J.1105.2009.01086.

摘要

热熔法制备了一系列聚苯基甲氧基硅氧烷（PPMS）、聚甲基苯基甲氧基硅氧烷（PMPS）改性环氧树脂，通过环氧值、红外光谱（IR）分析表明聚硅氧烷接枝了E-20环氧树脂且环氧基保持不变.探讨了有机硅含量对改性树脂固化体系耐热性能及韧性的影响.实验表明，当E-20环氧树脂与PPMS、PMPS的质量比为7∶3时，改性树脂固化体系的耐热性能明显提高，玻璃化转变温度(Tg)为95.8、88.3℃，分别比改性前提高了9.0℃和1.5℃；质量损失50%时的热分解温度(Td)为476.5、487.8℃，分别比改性前提高了58.3℃和69.5℃.与ED-30固化体系相比，EPMS-30固化物的耐热性能，韧性等力学性能提高的更加明显，并且还具有优良的涂膜性能.

Abstract

Silicone modified epoxy resins were prepared by polycondensation of polyphenylmethoxysilicone (PPMS) and polymethylphenylsilicone (PMPS) with E-20 epoxy resin.Oxirane ring and epoxy values were determined by Fourier transform infrared (FTIR) spectroscopy and HCl/acetone method.The data indicated that silicone oligomers were incorporated into epoxy resin with a random polycondensation and without involving the opening of the oxirane ring in the silicone modified epoxy structure.The influences of silicone contents on the heat-resistant properties of cured silicone modified epoxy resin systems were investigated by differential scanning calorimetry (DSC) and thermogravimetic analysis (TGA).The DSC data showed with increasing siloxane content in copolymers the glass transition temperature (Tg) lowered gradually.But when the mass ratio of epoxy resin to PPMS

PMPS was 7∶3

the Tg was 958℃ and 883℃

higher than those of unmodified epoxy resins systems by 9.0℃ and 1.5℃ respectively.The TGA data indicated that siloxane moiety exerts its thermal stability on the copolymer through dissipation of the heat

thus delaying thermal degradation of the copolymers.when the mass ratio of epoxy resin to PPMS

PMPS was 7∶3

the 50% weight loss temperature of degradation (Td) was 476.5℃ and 487.8℃

higher than those of unmodified epoxy resins systems by 58.3℃ and 69.5℃ respectively.In contrast to ED-30 cured system

the heat-resistance and toughness of EPMS-30 cured systems improved more obvious

and its film coatings also showed more excellent filming properties.

关键词

PPMSPMPS环氧树脂改性韧性耐热性

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON MODIFICATION OF PHENOLIC RESIN BY ELASTOMERIC NANOPARTICLES OF NITRILE BUTADIENE

MODIFICATION OF BISPHENOL A EPOXY RESINS WITH CHLORIC ORGANIC SILICON

MORPHOLOGY,MECHANICAL PROPERTIES AND THERMAL STABILITY OF EPOXY RESIN/LIQUID CRYSTALLINE POLYMER BLENDS

STUDIES ON THE KINETICS AND CHARACTERIZATION OF DGEBA/DDM SYSTEM MODIFIED WITH EPOXY TERMINATED DISILOXANE

STUDY ON A NOVEL TOUGHENED EPOXY RESIN BY HTBN

Related Author

No data

Related Institution

大连理工大学高分子材料研究所

辽宁省高分子科学与工程重点实验室

辽宁省高性能树脂工程技术研究中心

中国科学院广州化学研究所

中国科学院研究生院

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰