PREPARATION OF MONODESPERSE BIOPOLYMER MICROBEADS USING A NEW AND SIMPLE METHOD

ZHU Liping; LI Yaogang; ZHANG Qinghong; WANG Hongzhi; ZHU Meifang

doi:10.3724/SP.J.1105.2009.01132

您当前的位置：

首页 >

文章列表页 >

PREPARATION OF MONODESPERSE BIOPOLYMER MICROBEADS USING A NEW AND SIMPLE METHOD

Research Article | 更新时间：2021-03-19

- PREPARATION OF MONODESPERSE BIOPOLYMER MICROBEADS USING A NEW AND SIMPLE METHOD
- Acta Polymerica Sinica Issue 11, Pages: 1132-1137(2009)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2009.01132
  CLC：
- Published：20 November 2009，
扫描看全文
ZHU Liping, LI Yaogang, ZHANG Qinghong, WANG Hongzhi, ZHU Meifang. PREPARATION OF MONODESPERSE BIOPOLYMER MICROBEADS USING A NEW AND SIMPLE METHOD. [J]. Acta Polymerica Sinica (11):1132-1137(2009)
DOI：

ZHU Liping, LI Yaogang, ZHANG Qinghong, WANG Hongzhi, ZHU Meifang. PREPARATION OF MONODESPERSE BIOPOLYMER MICROBEADS USING A NEW AND SIMPLE METHOD. [J]. Acta Polymerica Sinica (11):1132-1137(2009) DOI： 10.3724/SP.J.1105.2009.01132.

摘要

采用不同尺寸的聚四氟乙烯（PTFE）微管为内外管、玻璃毛细管（glass capillary）或聚丙烯（PP）中空纤维为内管管头设计制作了一种共轴微通道反应器（N-CAMFR）.以聚乳酸（PLA）/二氯甲烷（CH2Cl2）溶液和海藻酸钠（Na-alginate）水溶液分别作为分散相，在N-CAMFR内形成O/W和W/O乳液后，收集乳液并使其中的液滴固化，制备出单分散的生物质聚合物微珠（BPM）.研究了固定管头尺寸时，改变连续相的流速及表面活性剂的种类对微珠尺寸的影响.结果表明，使用N-CAMFR制备微珠，反应过程流畅，所制得的微珠粒径分布均匀，其分散系数（f）可低至2.16%；通过改变内管管头的尺寸可方便地调控N-CAMFR的尺度，与传统微通道反应器相比，降低制作成本的同时拓宽了其应用的范围，而且降低了微通道反应器堵塞的几率.为粒径范围200～800 μm的单分散聚合物微珠的可控连续制备提供了快捷绿色的新方法.

Abstract

A new and simple method to prepare the monodisperse microbeads was developed for soluble polymers.Using a microchannel

we generated the uniform droplets by pushing the dispersed phase into the continuous phase and then solidified them by solvent-evaporation or gelation to obtain the PLA and sodium alginate microbeads.The microchannel was fabricated in our lab

and all of the materials were commercially produced.By using a frequency-modulation oscillator to help evaporation

the droplets can be solidified within 2 h

and especially the surface of the microbeads was smooth

and small pores with diameter of 1～2 μm were well-dispersed.By controlling the flow rates of the continuous phase conveniently

we could adjust the sizes of the microbeads.The diameters of the microbeads decreased from 460 μm to 342 μm when we increased the flow rates from 100 μL/min to 900 μL/min

and the lowest coefficients of variance of the microbeads was 2.16%.Also we studied the effect of the different continuous phases on the size of the microbeads

and it was believed that the size of the microbeads can be controlled by using different surfactants or mixing them in the continuous phase.

关键词

微通道生物材料单分散微珠共轴

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS AND CHARACTERIZATION OF ELECTROACTIVE GRAFT COPOLYMER OF POLY(L-GLUTAMIC ACID)-g-ANILINE TETRAMER

SYNTHESIS AND CHARACTERIZATION OF POLY(BIS(2-METHOXYETHOXY) PHOSPHAZENE)-GRAFT-POLY(ε-CAPROLACTONE) COPOLYMERS

SYNTHESIS AND CHARACTERIZATION OF POLY(D,L-LACTIDE-co-CYCLIC CARBONATE)S WITH HYDROXYL PENDANT FUNCTIONAL GROUPS

PREPARATION OF UNIFORM POLY(METHYL METHACRYLATE) PARTICLES BY DISPERSION POLYMERIZATION

PREPARATION OF MONODISPERSE COPOLYMER MICROSPHERES WITH MICRON SIZE

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰