SYNTHESIS AND PROPERIES OF POLY(AROMATIC ETHER KETONE KETONE ETHER KETONE KETONE)CONTAINING CARBOXYLIC ESTER SIDE GROUPS

SONG Cheng; LI Jing; YU Wenwen; ZHONG Ming; ZHU Zhifang; SONG Caisheng

doi:10.3724/SP.J.1105.2010.09191

您当前的位置：

首页 >

文章列表页 >

SYNTHESIS AND PROPERIES OF POLY(AROMATIC ETHER KETONE KETONE ETHER KETONE KETONE)CONTAINING CARBOXYLIC ESTER SIDE GROUPS

Research Article | 更新时间：2021-03-19

- SYNTHESIS AND PROPERIES OF POLY(AROMATIC ETHER KETONE KETONE ETHER KETONE KETONE)CONTAINING CARBOXYLIC ESTER SIDE GROUPS
- Acta Polymerica Sinica Issue 6, Pages: 624-628(2010)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2010.09191
  CLC：
- Published：20 June 2010，
扫描看全文
SONG Cheng, LI Jing, YU Wenwen, ZHONG Ming, ZHU Zhifang, SONG Caisheng. SYNTHESIS AND PROPERIES OF POLY(AROMATIC ETHER KETONE KETONE ETHER KETONE KETONE)CONTAINING CARBOXYLIC ESTER SIDE GROUPS. [J]. Acta Polymerica Sinica (6):624-628(2010)
DOI：

SONG Cheng, LI Jing, YU Wenwen, ZHONG Ming, ZHU Zhifang, SONG Caisheng. SYNTHESIS AND PROPERIES OF POLY(AROMATIC ETHER KETONE KETONE ETHER KETONE KETONE)CONTAINING CARBOXYLIC ESTER SIDE GROUPS. [J]. Acta Polymerica Sinica (6):624-628(2010) DOI： 10.3724/SP.J.1105.2010.09191.

摘要

以含羧基侧基的聚芳醚酮酮醚酮酮(PEKKEKK-A)树脂为原料，二氯亚砜(SOCl2)、二氯乙烷(DCE)、吡啶为催化溶剂体系，合成带甲酰氯侧基的聚芳醚酮酮醚酮酮(PEKKEKK-C)树脂.PEKKEKKC与甲醇、乙醇、丁醇、辛醇、苯酚等发生酯化反应，得到5种含羧酸酯侧基的聚芳醚酮酮醚酮酮(PEKKEKK-E)s.用红外光谱(FTIR)、氢核磁谱(1H-NMR)、广角X射线衍射(WAXD)、热失重(TGA)、示差扫描量热(DSC)等技术对其结构与性能进行了分析表征.结果表明，聚合物为非晶聚集态；玻璃化转变温度(Tg)在175.7~236.8℃之间，较PEKK有较大幅度提高；出现两次热失重平台，分别在335~365℃，460~505℃之间，第一次失重可能由于酯分解所致，第二次失重可能是分子主链开始分解；树脂能溶解于DMAc、NMP、二氯甲烷等普通有机溶剂中，溶剂挥发后成膜性良好，可制成透明薄膜；断裂伸长率在6.34%~15.43%之间，拉伸强度在74.68~85.35 MPa之间.

Abstract

Five novel poly(aryl ether ketone ketone ether ketone ketone) with carboxylic ester side groups (PEKKEKK-E)s were synthesized from poly(aryl ether ketone ketone ether ketone ketone) having pendent carboxyl groups (PEKKEKK-A) and alcohols

in the presence of 1

2-dichoroethane and thionyl chloride as acylchlorination reagent

pyridine as a catalyst.While PEKKEKK-A was prepared from trimellitic anhydride chloride (TMAC) and 1

4-bis(4-phenoxybenzoyl)benzene(p-EKKE) by low temperature solution polycondensation.PEKKEKKEs were characterized by FTIR

1H-NMR

WAXD

TGA

DSC

the solubility and mechanical properties of the polymers were investigated.Results show that the glass transition of the polymers is in the range of 175℃ to 237℃.The structure of the polymers is amorphous as expected.The esterified polymers have better solubility than the corresponding polymer.Flexible and colorless films were easily obtained by solution casting taking DMAc as solvent.It shows that the polymers have good mechanical properties.Tensile strength

elongation at break and Young’s module of polymers are in the range of 74.7 MPa to 85.4 MPa

6.34% to 15.43%

and 1.74 GPa to 3.08 GPa

respectively.

关键词

聚芳醚酮羧基侧基酯化结构与性能

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON GAS PERMEABILITY BEHAVIOR FOR CARDO POLYARYLETHERKETONE COPOLYMERS

PREPARATION AND CHARACTERIZATION OF LOW-PRESSURE NANOFILTRATION MEMBRANES BASEDON CROSSLINKED HYPERBRANCHED POLYESTER

PREPARATION AND CHARACTERIZATION OF AMBIENT SELF-CROSSLINKING ACRYLIC POLYMER LATEXES

SYNTHESIS AND PROPERTIES OF POLY(ARYL ETHER KETONE)S CONTAINING MULTI-CARBONYL IN THE MAIN CHAIN

THE INFLUENCE OF Br［C14im］(CH2)4［C14im］Br ON THE STRUCTURE AND PROPERTIES OF PP

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰