MICROSTRUCTURE AND PROPERTIES DEVELOPMENT OF THERMALLY STABILIZED PVC DURING PHOTOAGEING

PI Hong; CHEN Shenqing; GUO Shaoyun

doi:10.3724/SP.J.1105.2010.09206

您当前的位置：

首页 >

文章列表页 >

MICROSTRUCTURE AND PROPERTIES DEVELOPMENT OF THERMALLY STABILIZED PVC DURING PHOTOAGEING

Research Article | 更新时间：2021-03-19

- MICROSTRUCTURE AND PROPERTIES DEVELOPMENT OF THERMALLY STABILIZED PVC DURING PHOTOAGEING
- Acta Polymerica Sinica Issue 6, Pages: 660-665(2010)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2010.09206
  CLC：
- Published：20 June 2010，
扫描看全文
PI Hong, CHEN Shenqing, GUO Shaoyun. MICROSTRUCTURE AND PROPERTIES DEVELOPMENT OF THERMALLY STABILIZED PVC DURING PHOTOAGEING. [J]. Acta Polymerica Sinica (6):660-665(2010)
DOI：

PI Hong, CHEN Shenqing, GUO Shaoyun. MICROSTRUCTURE AND PROPERTIES DEVELOPMENT OF THERMALLY STABILIZED PVC DURING PHOTOAGEING. [J]. Acta Polymerica Sinica (6):660-665(2010) DOI： 10.3724/SP.J.1105.2010.09206.

摘要

通过UV-Vis、FTIR、DSC、以及色差、力学性能的测试表征，实时追踪分析了在紫外光老化过程中，含Pb、Sn以及Ca-Zn热稳定剂的PVC体系微观结构和宏观性能的演变过程.结果表明，在相同光老化条件下，PVC/Pb、PVC/Sn和PVC/Ca-Zn体系的微观结构变化规律基本一致，过程中主要的化学反应是，大分子吸收光能后，发生脱HCl生成共轭双键的反应、生成羰基的氧化反应、交联反应和降解反应；不同热稳定剂的作用，主要表现在对于微观结构变化的幅度和动力学过程的影响不同.相应地，3种体系的外观色差和力学性能的变化规律也相似，但色差的变化程度和速度以及老化后力学性能的保持率因所含热稳定剂的不同而不同，其中含Sn体系的颜色稳定性最好，含Pb体系的力学性能保持率最高.

Abstract

Three different poly(vinyl chloride) (PVC) formulations were submitted to photo ageing.The influence of the different thermal stabilizers was evaluated by means of ultraviolet-visible (UV-Vis) spectra

fourier transform infrared (FTIR) spectra and differential scanning calorimetry (DSC).The gel content formed in exposed samples was estimated gravimetrically

and the color and mechanical properties changes of PVC during photoageing were studied.It was found that microstructures of three PVC/thermal stabilizer blends changed in the same tendency.As UV irradiation time increases

the conjugated polyene sequence

carbonyl group and the gel content increase

respectively.And the molecular weight decreases.Meanwhile

the yellowness index

the elongation at break and impact strength of the PVC sheets gradually decrease with increasing UV irradiation time.The main photochemical reactions include photo-dehydrochlorination

photooxidation

degradation and crosslinking.The degree and the kinetics of dehydrochlorination

oxidative

degradation and crosslinking during photoageing were different in three PVC/thermal stabilizer blends.Sn was the most efficient on restraining dehydrochlorination.Pb was the most stable in the reaction of oxidative degradation and crosslinking.As a result PVC/Sn blends showed higher color stability

and the retained percentage of impact strength and elongation at break of PVC/Pb blends were the highest among of the three blends.

关键词

聚氯乙烯（PVC）光老化热稳定剂氧化降解交联

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Grafting of Maleic Anhydride onto Hyperbranched Polyethylene and Suppression of Chain Degradation and Crosslinking Side Reactions

The dynamic rheological characterization of structure development for impact polypropylene copolymer melt

STUDIES ON STRUCTURE EVOLUTION OF LDPE DURING CROSSLINKING PROCESS BY RHEOLOGICAL TESTS

Graft Polymerization of 2-Hydroxyethyl Methacrylate on Soy Protein Isolate via Atom Transfer Radical Polymerization

STUDY ON THE SHEARSTABILITY OF LOW CONCENTRATION HPAM/AlCIT-CROSSLINKED POLYMER SYSTEM

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰