BARRIER PROPERTY OF AZOBENZENE-CONTAINING SIDECHAIN LIQUID CRYSTALLINE POLYMER

LIU Jian; WU Xiaohua; WANG Mingle

doi:10.3724/SP.J.1105.2010.09393

您当前的位置：

首页 >

文章列表页 >

BARRIER PROPERTY OF AZOBENZENE-CONTAINING SIDECHAIN LIQUID CRYSTALLINE POLYMER

Research Article | 更新时间：2021-03-19

- BARRIER PROPERTY OF AZOBENZENE-CONTAINING SIDECHAIN LIQUID CRYSTALLINE POLYMER
- Acta Polymerica Sinica Issue 10, Pages: 1231-1237(2010)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2010.09393
  CLC：
- Published：20 October 2010，
扫描看全文
LIU Jian, WU Xiaohua, WANG Mingle. BARRIER PROPERTY OF AZOBENZENE-CONTAINING SIDECHAIN LIQUID CRYSTALLINE POLYMER. [J]. Acta Polymerica Sinica (10):1231-1237(2010)
DOI：

LIU Jian, WU Xiaohua, WANG Mingle. BARRIER PROPERTY OF AZOBENZENE-CONTAINING SIDECHAIN LIQUID CRYSTALLINE POLYMER. [J]. Acta Polymerica Sinica (10):1231-1237(2010) DOI： 10.3724/SP.J.1105.2010.09393.

摘要

合成了偶氮苯侧链液晶聚合物聚甲基丙烯酸(3-［4-(4′-氰基偶氮苯)苯氧基］丙酯)(PM3ABCN)，采用原位掠入射X射线衍射(GIXRD)方法研究了该聚合物膜在向列相和各向同性态(无定形相)时对气体的阻隔特性.并采用X射线能谱仪(EDS)分析铁片氧化后的氧含量，计算得到渗透通过聚合物膜的氧气的量.结果表明，当PM3ABCN膜处于各向同性态时，通过聚合物膜的氧气平均渗透量为1.92×10-3 cm3　day-1 m-2；而处于液晶态的膜对氧气的阻隔性提高了4.4倍，氧气平均渗透量为4.38×10-4　cm3day-1 m-2. 结合样品表面的显微分析结果，探讨了液晶凝聚相结构对气体小分子的阻隔机理.

Abstract

In order to study the properties of azobenzene-containing side-chain liquid crystalline polymer for preventing the permeation of small molecule

poly(3［4-(4′-cyanophenylazo)phenoxy］propyl methacrylate) (PM3ABCN) was synthesized in this study.The barrier properties of PM3ABCN was individually determined using in situ glancing incidence X-ray diffraction (GIXRD) scanning technology under the amorphous state and the liquid crystalline (nematic) state.GIXRD was used to collect the metal surface oxidation

which is a quantitative result of oxygen permeated through the polymer films covering the metal surface.The content of oxygen element in oxidized iron matrix samples was analyzed by means of X-ray energy dispersive spectroscopy (EDS)

and the amount of oxygen permeated through the synthesized polymer films was calculated based on the results gained from the XRD patterns and EDS analysis.The results indicated that the average permeation rate of oxygen through the PM3ABCN films was 1.92×10-3 cm3 day-1 m-2 and 4.38×10-4 cm3 day-1 m-2 under the isotropic phase and liquid crystalline phase respectively

and the permeation property of liquid crystalline PM3ABCN was 4.4 times slower than that of the amorphous state.In combination with the results of microscopic analysis on the specimen surface

the barrier mechanism of condensed state structure in liquid crystalline PM3ABCN was also investigated.

关键词

偶氮苯侧链液晶聚合物阻隔掠入射X射线衍射

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SYNTHESIS AND THEIR THERMOTROPIC LIQUID CRYSTALLINE BEHAVIOR OF CYCLOTRIPHOSPHAZENE BASED A3B3 MIKTOARM AZOBENZENE-CONTAINING STAR-SHAPED COPOLYMERS

PHOTO AND H+ DUAL-RESPONSIVE BEHAVIORS OF AZOBENZENE SHELLED POLY(AMINOAMINE) DENDRIMERS

EFFECT OF SIDE-CHAIN STRUCTURE ON THE THIRD-ORDER NONLINEAR OPTICAL PROPERTIES OF ACRYLATE POLYMERS

SYNTHESIS AND CHARACTERIZATION OF SIDE CHAIN LIQUID CRYSTALLINE POLYACRYLATES AND THEIR EFFECT ON THE CRYSTALLIZATION OF POLYETHYLENE USING AS A NUCLEATING AGENT

SYNTHESIS AND LIQUID CRYSTALLINE BEHAVIOR OF POLYSILOXANE CONTAINING AZOBENZENE SIDE GROUPS

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰