SOLID ALKALINE ELECTROLYTE MEMBRANES BASED ON POLY(VINYL ALCOHOL) FOR POTENTIAL USE IN FUEL CELLS

Research Article | 更新时间：2021-03-19

- SOLID ALKALINE ELECTROLYTE MEMBRANES BASED ON POLY(VINYL ALCOHOL) FOR POTENTIAL USE IN FUEL CELLS
- Acta Polymerica Sinica Issue 7, Pages: 701-708(2011)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2011.10178
  CLC：
- Published：20 July 2011，
扫描看全文
FU Jing, ZHANG Haiyan, QIAO Jinli, MA Jianxin. SOLID ALKALINE ELECTROLYTE MEMBRANES BASED ON POLY(VINYL ALCOHOL) FOR POTENTIAL USE IN FUEL CELLS. [J]. Acta Polymerica Sinica (7):701-708(2011)
DOI：

FU Jing, ZHANG Haiyan, QIAO Jinli, MA Jianxin. SOLID ALKALINE ELECTROLYTE MEMBRANES BASED ON POLY(VINYL ALCOHOL) FOR POTENTIAL USE IN FUEL CELLS. [J]. Acta Polymerica Sinica (7):701-708(2011) DOI： 10.3724/SP.J.1105.2011.10178.

摘要

通过在不同浓度KOH溶液中进行掺杂

制备出了聚乙烯醇(PVA)、聚乙烯醇/聚乙烯吡咯烷酮(PVA/PVP)和聚乙烯醇/聚乙二醇二甲醚 (PVA/PEGDE)碱性聚合物电解质膜.详细考察了膜的外观形貌、微观结构、热稳定性、离子电导率和化学稳定性等.结果表明

PVA与PVP以及PEGDE具有很好的相容性

所制备的复合膜断面致密、均匀

没有出现明显的相分离.同时

PVP和PEGDE的混入可以极大的提高复合膜的电导率.PVA中混入100%含量的PVP时

膜电导率可达210-3 Scm-1;混入25%的PEGDE时

膜电导率最高可达1.4310-3 Scm-1.经PVP和PEGDE改性后的PVA膜表现出很好的热稳定性和耐碱稳定性

所制备的样膜经80℃ 10 molL-1 KOH溶液中处理24 h后

没有观察到膜电导率的下降.红外光谱研究表明

处理温度升高有利于膜对KOH溶液的吸收

从而提高膜中OH-载流子的浓度.此外

PVA/PVP/KOH膜和PVA/PEGDE/KOH膜的甲醇吸收率随温度的升高没有明显变化

100℃时其甲醇吸收率仅为同条件下Nafion115膜的1/4.

Abstract

The solid alkaline electrolyte membranes have been succesfully prepared from poly(vinylalcohol) (PVA)

poly(vinyl alcohol)/poly(vinyl pyrrolidone) (PVA/PVP) and poly(vinyl alcohol)/poly(ethylene glycol) dimethyl ether (PVA/PEGDE) by doping different concentrations of KOH aquaous solutions.The morphology

microstructure

thermal stability

ionic conductivity and chemical stability of the membranes were investigated in detail.The wholly compact and homogeneous composite membranes were obtained due to the good compatibility between PVA and PVP and/or PEGDE

and no obvious phase seperation was observed.The ionic conductivity of the composite membranes was enhanced greatly with increasing the content of PVP and/or PEGDE in polymer.The measured conductivity of the membranes reached as high as up to 210-3 Scm-1 by addition 100% content of PVP and 1.4310-3 Scm-1by addition 25% content of PEGDE.The obtained PVA/PVP and PVA/PEGDE membranes exhibited excellent thermal stability and alkaline tolerance where no obvious decrease in ionic conductivty was observed even after the membrane being treated in 10 molL-1 KOH at an elevated temperature of 80℃.FTIR spectra results suggested that the KOH absorption of the membranes increased at elevated treatment temperatures

which gave rise to an increase in the OH- charge carriers density.In addition

the methanol uptake of PVA/PVP/KOH and PVA/PEGDE/KOH membranes showed almost no changes after conditioned at elevated temperatures and

were 4 times lower than that of Nafion115 membrane after conditioned at 100℃.It could indicate a potential feasibility as a promising PVA based solid alkaline electrolyte membrane for alkaline fuel cells.

关键词

碱性聚合物电解质膜聚乙烯醇聚乙烯吡咯烷酮聚乙二醇二甲醚化学稳定性

Keywords

Solid alkaline electrolyte membranesPoly(vinyl alcohol)Poly(vinyl pyrrolidone)Poly(ethylene glycol) dimethyl etherChemcial stability

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

PREPARATION AND CHARACTERIZATION OF BACTERIAL CELLULOSE REINFORCED PVA/PVP HYDROGELS

Preparation and Electrochemical Performance of Polyzwitterion Containing Intramolecular Salt as Solid Electrolytes for Lithium-ion Batteries

Adsorption Behavior of Lysozyme by Sponge-like Materials Based on Electrospinning

Design and Synthesis of Phase-Change-Material Aerogels for Personal Thermal Management

Mechanically Robust and Healable Poly(vinyl alcohol)-based Shape Memory Supramolecular Plastics

Related Author

No data

Related Institution

Department of Material Science and engineering, Jinan University

University of Science and Technology of China

CAS Key Laboratory of Renewable Energy, Guangdong Provincial Key Laboratory of New and Renewable Energy Research and Development, Guangzhou Institute of Energy Conversion, Chinese Academy of Sciences

Materials Science and Engineering, Shandong University of Technology

College of Chemistry and Chemical Engineering, Qingdao University

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰