SYNTHESIS OF SB-GRAFTED HVPBR AND ITS COMPATIBILITY WITH SBR

HUA  Jing; GUO  Liyun; TIAN  Yumn; GENG  Jieting; ZHUANG  Tao; DENG  Zhifeng; XU  Ling

doi:10.3724/SP.J.1105.2011.11032

您当前的位置：

首页 >

文章列表页 >

SYNTHESIS OF SB-GRAFTED HVPBR AND ITS COMPATIBILITY WITH SBR

Research Article | 更新时间：2021-03-19

- SYNTHESIS OF SB-GRAFTED HVPBR AND ITS COMPATIBILITY WITH SBR
- Acta Polymerica Sinica Issue 5, Pages: 461-466(2011)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2011.11032
  CLC：
- Published：20 May 2011，
扫描看全文
HUA Jing, GUO Liyun, TIAN Yumn, GENG Jieting, ZHUANG Tao, DENG Zhifeng, XU Ling. SYNTHESIS OF SB-GRAFTED HVPBR AND ITS COMPATIBILITY WITH SBR. [J]. Acta Polymerica Sinica (5):461-466(2011)
DOI：

HUA Jing, GUO Liyun, TIAN Yumn, GENG Jieting, ZHUANG Tao, DENG Zhifeng, XU Ling. SYNTHESIS OF SB-GRAFTED HVPBR AND ITS COMPATIBILITY WITH SBR. [J]. Acta Polymerica Sinica (5):461-466(2011) DOI： 10.3724/SP.J.1105.2011.11032.

摘要

以n-BuLi为引发剂，THF为结构调节剂合成一定分子量和苯乙烯结构单元含量的丁苯大分子（SB）.在SB的加氢汽油溶液中用Mo-Al（正辛醇取代的MoCl5和Al(OPhCH3)(i-Bu)2）催化丁二烯配位聚合制备丁苯接枝的高乙烯基聚丁二烯橡胶（SB-grafted HVPBR）.接枝结构是通过聚丁二烯活性链与SB分子上的双键反应生成.通过在HVPB主链上引入丁苯支链，使聚合物由线形变成含支链的聚合物，以此降低聚合物溶液的动力黏度，改善钼系催化丁二烯聚合溶液黏度大的缺点.采用FTIR、GPC、凝胶渗透色谱仪-激光光散射仪-在线黏度计联用系统、DSC等表征手段，研究SB用量和苯乙烯含量对SB-grafted HVPBR结构和聚合物溶液黏度的影响.通过差示扫描量热法（DSC）测试SB-grafted HVPBR与SBR不同共混比下硫化胶的玻璃化转变温度Tg，对SB-grafted HVPBR/SBR共混胶的相容性进行表征，初步探索SB-grafted HVPBR与SBR共混胶的共混比对两相相容性的影响.

Abstract

Graft copolymers of high vinyl polybutadiene with butadiene-styrene copolymer (SB-grafted HVPBR) were synthesized by polymerization of butadiene in hydrogasoline solution of styrenebutadiene random copolymer (SB) (St% was 30%

Mn was 3.710-3) using a homogeneous MoCl3(OC8H16)2/Al((OPhCH3)(i-Bu)2 catalyst.Graft copolymers were formed when the growing polybutadiene chains threaded through the double bonds of the dissolved SB

giving copolymers with proliferating chain structures.SB was synthesized by anionic polymerization with butyl-lithium as initiator and tetrahydrofuran as structural regulator.The effect of addition amount of SB on the structure and properties of SB-grafted HVPBR was studied by means of FTIR

GPC and GPC-MALLS-Viscometer Analysis System etc.Compared with HVPBR

the molecular weight of SB\|grafted HVPBR and molecular weight distribution and the content of gel raised slightly.The solution dynamic viscosity of HVPBR was decreased to a great extent as a result of the presence of the SB graft chain.The graft efficiency was the highest when the SBs addtion was 3 wt%.Glass transition temperature (Tg) of SB-grafted HVPBR/SBR compounds at varying blending ratios were measured using differential scanning calorimetry (DSC).The results of DSC confirmed that the compatibility of HVPBR and SBR was improved effectively by grafting SB onto HVPBR.

关键词

高乙烯基聚丁二烯接枝丁苯橡胶钼催化剂

Keywords

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SiO2 NANOPARTICLES MODIFICATION WITH POLYMER USING AN ESTERIFICATION METHOD AT ROOM TEMPERATURE

Grafting of Maleic Anhydride onto Hyperbranched Polyethylene and Suppression of Chain Degradation and Crosslinking Side Reactions

Preparation of Poly(sodium 4-styrenesulfonate) Grafted Carbon Black via Ultrasonic Irradiation Initiated Radical Polymerization

PREPARATION AND CHARACTERIZATION OF THE NATURAL RUBBER COMPOSITES REINFORCED BY EPOXY NATURAL RUBBER GRAFTED SILICA WITH GOOD DISPERSIBILITY

PREPARATION AND PERFORMANCE OF NATURAL RUBBER/STYRENE-BUTADIENE RUBBER BASED SEPARATORS

Related Author

No data

Related Institution

No data

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰