The physical gelation of PVC plastisol is an important procedure in rotational molding processes

at the early stage of which the variation characteristics of plastisol viscosity determine its distribution on the mold surface

then affect the quality of products.On the basis of the unsteady temperature fields of the nickel mould and PVC material simulated by finite element method

the evolution and distribution of PVC material structures are calculated according to a theoretical model fitting well with experimental results

and then the plastisol viscosity and its evolution characteristics are obtained by the material structure-performance relationship.Hence the effect of different plasticizers on the physical gelation process of PVC materials is compared and analyzed.The results show the that PVC plastisol close to a mold surface

gets faster heating rate and earlier gel transition because of its smaller heat resistance.During the heating process

the viscosity of the PVC material is first reduced to a minimum

then increases rapidly due to the start of the gel transition.The micro mechanism of the gelation process is that the solution of PVC in the plasticizer and the swelling of PVC particles by the plasticizer are both strengthened

while the macro picture is a sharp increase in viscosity which makes the material stop flowing.Different plasticizers have different impacts on the evolution of material structure and plastisol viscosity

which is mainly due to their different lengths of chains.For the rotational molding process

the PVC thickness distribution depends on three important factors appeared during the physical gelation process of PVC plastisol: the minimum viscosity determined by the plastisol

the rate of the gelation process and the gelation temperature.