CRYSTALLIZATION STRUCTURES AND THERMAL PROPERTIES OF HIGH HEAT-RESISTANCE PLLA/PDLA BLENDS

Lu Chen; Song-chao Tang; Ji Xia; Wen-liang Pu; Rui Li

doi:10.3724/SP.J.1105.2013.12339

您当前的位置：

首页 >

文章列表页 >

CRYSTALLIZATION STRUCTURES AND THERMAL PROPERTIES OF HIGH HEAT-RESISTANCE PLLA/PDLA BLENDS

Research Article | 更新时间：2021-03-19

- CRYSTALLIZATION STRUCTURES AND THERMAL PROPERTIES OF HIGH HEAT-RESISTANCE PLLA/PDLA BLENDS
- Acta Polymerica Sinica Issue 8, Pages: 1006-1012(2013)
- 作者机构：
  
  华东理工大学材料科学与工程学院上海市先进聚合物材料重点实验室,上海,200237
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2013.12339
  CLC：
- Published：20 August 2013，
扫描看全文
Lu Chen, Song-chao Tang, Ji Xia, Wen-liang Pu, Rui Li. CRYSTALLIZATION STRUCTURES AND THERMAL PROPERTIES OF HIGH HEAT-RESISTANCE PLLA/PDLA BLENDS. [J]. Acta Polymerica Sinica (8):1006-1012(2013)
DOI：

Lu Chen, Song-chao Tang, Ji Xia, Wen-liang Pu, Rui Li. CRYSTALLIZATION STRUCTURES AND THERMAL PROPERTIES OF HIGH HEAT-RESISTANCE PLLA/PDLA BLENDS. [J]. Acta Polymerica Sinica (8):1006-1012(2013) DOI： 10.3724/SP.J.1105.2013.12339.

摘要

通过熔融共混法制备了一系列等比例聚左旋乳酸(PLLA)/聚右旋乳酸(PDLA)共混试样

采用差示扫描量热法(DSC)、核磁共振(13C-NMR)及广角X射线衍射(WAXD)等方法对共混产物进行了表征和研究分析.结果表明

等比例PLLA和PDLA熔融共混生成了立构复合物(stereocomplex

sc)

同时部分均聚物发生酯交换反应

生成了立体嵌段物(stereoblock

sb)

从而在DSC升温曲线上sc晶体处出现特殊的熔融双峰现象;随着熔融共混温度升高

sc晶体的生成率和结晶度逐渐下降;聚乳酸立构复合物的加工稳定性较好

二次加工后

sc晶体熔点基本不变

生成率和结晶度提高;由于sc晶体的存在

PLLA/PDLA共混物的耐热性能提高

退火热处理后耐热性能得到进一步提高.这对于开发高耐热聚乳酸及其加工应用具有重要的应用价值.

Abstract

A series of equimolar blends of poly(L-lactic acid)/poly(D-lactic acid) (PLLA/PDLA) were prepared by melt mixing and the blends were investigated by means of differential scanning calorimetry (DSC)

nuclear magnetic resonance (13C-NMR)

wide angle X-ray diffraction (WAXD)

etc.It was found that when the blending temperature was 210 ℃

the stereocomplex (sc) formed from equimolar PLLA/PDLA blends exhibited a high melting temperature at 229 ℃ and showed 98.1% crystallinity degree.As for the sample after isothermal annealing up to 120 ℃

the Vicat softening temperature approached to 126.4 ℃.It was indicated that double melting endotherms were characteristic for the sc crystals in the DSC thermograms

where formation of the stereoblock (sb) occured at high processing temperatures.The high-temperature-side (230 ℃) endotherm and the low-temperature-side (210 ℃) endotherm resulted from the melting of sc and sb crystals respectively.As the blending temperature increased

the high-temperature-side endotherm was reduced and the low-temperature-side endotherm was emphasized.The relative amounts and crystallinity degree of sc crystals decreased significantly with the increase of blending temperature.The sc-PLA had good processing stability.The melting temperature of sc crystals stayed constantly after second blending.Moreover

the relative amounts of sc crystals increased slightly.The PLLA/PDLA blends composed of networks of sc might be applicable to the heat-resistant materials

and this paper provided a new method of improving thermal stability and processing property of PLA.

关键词

聚乳酸立构复合物立体嵌段物熔融共混

Keywords

PLAStereocomplexStereoblockMelting blending

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Flame-retardant Properties of 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide Derivatives in Poly(lactic acid)

In Situ Polymerization of Polylactic Acid/Quaternary Fulvic Acid Intercalated Saponite Nanocomposites and Structure Characterizazion

EFFECT OF NUCLEATING AGENT AND ITS ADJUVANT ON CRYSTALLIZATION BEHAVIORS OF POLY(LACTIC ACID)

EFFECT OF POLY(ACRYLIC ACID) ON THE RHEOLOGICAL AND THERMAL PROPERTIES OF POLY(LACTIC ACID)

REPARATION AND CHARACTERIZATION OF POLY LACTIC ACID/ZINC OXIDE PILLARED SAPONITE NANOCOMPOSITES

Related Author

No data

Related Institution

College of Materials and Metallurgy, Guizhou University

National Engineering Research Center for Compounding and Modification of Polymer Materials

Key Laboratory of Oil and Gas Fine Chemicals, Ministry of Education and Xinjiang Uygur Autonomous Region, Xinjiang University

Xinjiang Institute of Light Industry Technology

College of Polymer Science and Engineering of Sichuan University, State Key Laboratory of Polymer Materials Engineering

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰