Synthesis and Conduction Mechanism of Comb-like Polymethacrylate Solid Polymer Electrolytes

Wei-xin Luo; Yu-ping Liu; Shu-yan Yang; Zhi-meng Liu

doi:10.3724/SP.J.1105.2014.13146

您当前的位置：

首页 >

文章列表页 >

Synthesis and Conduction Mechanism of Comb-like Polymethacrylate Solid Polymer Electrolytes

Research Article | 更新时间：2021-03-19

- Synthesis and Conduction Mechanism of Comb-like Polymethacrylate Solid Polymer Electrolytes
- Acta Polymerica Sinica Issue 1, Pages: 63-71(2014)
- 作者机构：
  
  1. 东莞理工学院广东高校化工清洁生产与绿色化学品工程技术开发中心,东莞,523808
  2. 华南理工大学材料科学与工程学院,广州,510640
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2014.13146
  CLC：
- Published：20 January 2014，
扫描看全文
Wei-xin Luo, Yu-ping Liu, Shu-yan Yang, Zhi-meng Liu. Synthesis and Conduction Mechanism of Comb-like Polymethacrylate Solid Polymer Electrolytes. [J]. Acta Polymerica Sinica (1):63-71(2014)
DOI：

Wei-xin Luo, Yu-ping Liu, Shu-yan Yang, Zhi-meng Liu. Synthesis and Conduction Mechanism of Comb-like Polymethacrylate Solid Polymer Electrolytes. [J]. Acta Polymerica Sinica (1):63-71(2014) DOI： 10.3724/SP.J.1105.2014.13146.

摘要

采用溶液聚合方法，以甲基丙烯酸甲酯、聚乙二醇单甲醚甲基丙烯酸酯为共聚单体，制备一种新型无规梳状聚合物，并研究了一系列掺杂不同含量高氯酸锂全固态聚合物电解质的导电性能.FTIR、1H-NMR结果证实了新型梳状聚合物具有无规梳状结构特征. DSC和XRD结果表明了聚合物电解质主要是以无定型状态存在. SEM和FTIR结果证实了当锂盐含量低于16 wt%时，锂盐在聚合物中具有良好的溶解性，ClO4- 主要以单离子状态存在，此时聚合物电解质30℃离子电导率达到最大值，为4.8110-5 S/cm. 当锂盐含量超过16 wt%时，Li+ClO4-离子对含量明显增多，表明了锂盐溶解性能下降，同时聚合物电解质离子电导率显著下降，这主要是锂盐增加导致离子的缔合增强，不利于离子的传导所致.

Abstract

A novel comb-like polymer was synthesized by solution polymerization with methyl methacrylate and poly(ethylene glycol) methly ether methacrylate as monomers

and the conductive properties of solid polymer electrolytes incorporated with LiClO4 were investigated thoroughly.The characteristic comb-like structure of polymer was confirmed by FTIR and 1H-NMR.The solid polymer electrolytes based on the comb-like polymer were found to be almost amorphous at room temperature

which was verified by DSC and XRD measurements.SEM and FTIR results revealed that

at the salt content less than 16 wt%

the salt could dissolve in the polymer matrix well and anions mainly presented in the polymer matrix in terms of free ions.When the salt content was more than 16 wt%

the content of ion pairs increased significantly

indicating the bad solubility of salt in the polymer matrix.The ionic conductivity of the electrolytes was up to 4.8110-5 S/cm at 30℃ with the addition of 16 wt% LiClO4.Increasing the content of salt would lead to a dramatic decrease in the ionic conductivity of the polymer electrolytes

which could be attributed to the negative effect of large number of ionic pairs.

关键词

梳状固态聚合物电解质离子电导率甲基丙烯酸甲酯导电机理

Keywords

Comb-like solid polymer electrolytesIonic conductivityMethyl methacrylateConduction mechanism

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Reversible-deactivation Radical Polymerization of Methyl Methacrylate Mediated by Carbodiimide Catalysts

Kinetics of Methyl Methacrylate Polymerization Mediated by 4, 4'-Dimethoxydiphenyl Nitroxide

Effect of Graphene Modified by P[MMA-IL] on the Crystallization and Dielectric Behavior of PVDF Composite Film

Magnetic Responsive Oil-absorbing Polymeric Resins Based on 4-Tert-butyl-styrene and Methyl Methacrylate

Preparation and Characterization of Oil/Water Separation Membranes via Grafting Methyl Methacrylate onto Poly(vinylidene fluoride)

Related Author

No data

Related Institution

State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology

State Key Laboratory of Chemical Engineering(Zhejiang University), College of Chemical Engineering and Biochemical Engineering, Zhejiang University

School of Chemistry and Chemical Engineering, Hefei University of Technology

Key Laboratory of Advanced Functional Materials and Devices

The Center of New Energy Materials and Technology, School of Materials Science and Engineering, Southwest Petroleum University

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰