Frontal Polymerization Preparation of Poly(natural rubber-g-acrylamide) for Water-swellable Rubber

Qing-bin Li; Yong-jun Han; Qing-zhi Yan; Chang-chun Ge

doi:10.3724/SP.J.1105.2014.13455

您当前的位置：

首页 >

文章列表页 >

Frontal Polymerization Preparation of Poly(natural rubber-g-acrylamide) for Water-swellable Rubber

Rapid Communications | 更新时间：2021-03-19

- Frontal Polymerization Preparation of Poly(natural rubber-g-acrylamide) for Water-swellable Rubber
- Acta Polymerica Sinica Issue 4, Pages: 423-426(2014)
- 作者机构：
  
  1. 北京科技大学材料科学与工程学院,北京,100083
  2. 平顶山学院化学化工学院,平顶山,467000
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2014.13455
  CLC：
- Published：20 April 2014，
扫描看全文
Qing-bin Li, Yong-jun Han, Qing-zhi Yan, Chang-chun Ge. Frontal Polymerization Preparation of Poly(natural rubber-g-acrylamide) for Water-swellable Rubber. [J]. Acta Polymerica Sinica (4):423-426(2014)
DOI：

Qing-bin Li, Yong-jun Han, Qing-zhi Yan, Chang-chun Ge. Frontal Polymerization Preparation of Poly(natural rubber-g-acrylamide) for Water-swellable Rubber. [J]. Acta Polymerica Sinica (4):423-426(2014) DOI： 10.3724/SP.J.1105.2014.13455.

摘要

采用波聚合工艺快速制备了聚（天然橡胶-接枝-丙烯酰胺）吸水膨胀橡胶.该波聚合过程能够在45 ℃左右被引发，最高波温达到112 ℃，波速0.3~1.0 cmmin-1.与传统间歇聚合工艺相比，波聚合制备样品的接枝效率达到51.8%，是传统间歇聚合制品的2.8倍；最大吸水倍率为7.66 gg-1，是传统聚合制品的1.6倍；聚合时间为传统间歇聚合的1/8.扫描电镜观测发现，波聚合制备的吸水膨胀橡胶呈现均匀分布的蜂窝状微孔结构，孔直径在4~10 m之间，该结构有利于橡胶在保持高强度和弹性的同时，提高吸水性能；而传统间歇聚合制品内则以小于2 m的微孔为主，同时有少数近毫米级的条形大孔存在.

Abstract

For the first time

a water-swellable rubber

poly(natural rubber-g -acrylamide)

was prepared quickly by frontal polymerization.Compared with batch polymerization

the front polymerization process was studied and the polymers were characterized.The frontal polymerization reaction is ignited after the system temperature is higher than 45 ℃ approximately.As important process parameters

the frontal temperature is about 112 ℃ while the front velocity is between 0.3 cmmin-1 and 1.0 cmmin-1.The grafting efficiency of frontal polymerization is 51.8% which is 2.8 times as much as that of batch polymerization.The maximum water absorption of products prepared via FP was calculated as 7.66 gg-1 which is 60% higher than that of the batch polymerization.While the reaction time of frontal polymerization is an eighth of the reaction time of batch polymerization.The microstructure of water-swellable rubber synthesized by frontal polymerization was studied.The relatively uniform hollows

at a size range from 4 m to 10 m

can improve the swelling ability while keep the good strength and elasticity.While the batch polymerization polymers have a lots of holes less than 2 m and sporadic linear holes near 1 mm.

关键词

波聚合天然橡胶吸水膨胀橡胶接枝

Keywords

Frontal polymerizationNatural rubberWater-swellable rubberGrafting

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Rheological Behavior of Biomimetic Rubber

Preparation and Application of Lignin Grafted Natural Rubber Initiated by CaCl₂/H₂O₂

Preparation and Properties of High Performance Bio-based Elastomer Based on Methyl Methacrylate Grafted Natural Rubber

Related Author

No data

Related Institution

State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences

Key Laboratory of Rubber-Plastics, Ministry of Education, Qingdao University of Science & Technology

华南理工大学机械与汽车工程学院

材料科学与工程学院　广州 510640South China University of Technology, Guangzhou 510640 School of Materials Science and Engineering

College of Materials, Chemistry and Chemical Engineering, Hangzhou Normal University

Postal code：100190
Tel：010-62588927 Email：gfzxb@iccas.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备05002797号-8 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰