气相生长碳纤维/形状记忆聚氨酯复合薄膜的力学及形状记忆性能研究

韩春韶; 傅雅琴; 倪庆清

doi:10.3724/SP.J.1105.2010.00167

您当前的位置：

首页 >

文章列表页 >

气相生长碳纤维/形状记忆聚氨酯复合薄膜的力学及形状记忆性能研究

研究论文 | 更新时间：2021-03-19

- 气相生长碳纤维/形状记忆聚氨酯复合薄膜的力学及形状记忆性能研究
- STUDIES ON MECHANICAL AND SHAPE MEMORY PROPERTIES OF VAPOR GROWN CARBON FIBER/SHAPE MEMORY POLYURETHANE COMPOISTE FILMS
- 高分子学报 2010年第2期页码：167-172
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2010.00167
  中图分类号：
- 纸质出版日期：2010-2-20，
扫描看全文
韩春韶, 傅雅琴, 倪庆清. 气相生长碳纤维/形状记忆聚氨酯复合薄膜的力学及形状记忆性能研究[J]. 高分子学报, 2010,(2):167-172.

HAN Chunshao, FU Yaqin, NI Qingqing. STUDIES ON MECHANICAL AND SHAPE MEMORY PROPERTIES OF VAPOR GROWN CARBON FIBER/SHAPE MEMORY POLYURETHANE COMPOISTE FILMS[J]. Acta Polymerica Sinica, 2010,(2):167-172.
韩春韶, 傅雅琴, 倪庆清. 气相生长碳纤维/形状记忆聚氨酯复合薄膜的力学及形状记忆性能研究[J]. 高分子学报, 2010,(2):167-172. DOI： 10.3724/SP.J.1105.2010.00167.

HAN Chunshao, FU Yaqin, NI Qingqing. STUDIES ON MECHANICAL AND SHAPE MEMORY PROPERTIES OF VAPOR GROWN CARBON FIBER/SHAPE MEMORY POLYURETHANE COMPOISTE FILMS[J]. Acta Polymerica Sinica, 2010,(2):167-172. DOI： 10.3724/SP.J.1105.2010.00167.

摘要

采用溶液混合法制备了不同含量的气相生长碳纤维（VGCF）增强形状记忆聚氨酯(SMPU)的复合材料薄膜，测试分析了纯SMPU及VGCF/SMPU复合材料薄膜的力学性能及形状记忆性能.结果表明，制得的复合材料薄膜在VGCF含量达到9 wt%时

VGCF在SMPU基体中仍具有较好的分散性；SMPU与VGCF复合后，得到的复合材料薄膜的拉伸强度和刚度有较大程度的提高，含量达到9 wt%时复合材料薄膜的拉伸强度比纯SMPU提高66%，弹性模量提高300%，储能模量也有较大程度提高；SMPU与VGCF复合后，形状记忆性能有一定的下降，但经过适当预处理后，其形状记忆性能可以基本接近纯SMPU.

Abstract

In order to improve the mechanical properties of SMPU

vapor grown carbon fiber(VGCF) reinforced SMPU composite films with various VGCF contents were prepared via a solution mixing method.The mechanical and shape memory properties of the pure SMPU and VGCF/SMPU composite films were studied.The results show that

the VGCF still shows good dispersion in SMPU when the VGCF content reaches 9 wt% in the prepared composite film.The tensile strength and stiffness of the prepared composite films are greatly improved after compounding SMPU with VGCF

the tensile strength is improved by 66% with adding 9 wt% VGCF in the composite film

the elastic modulus is improved by 300% at this content and the storage modulus is also greatly improved.The shape memory property of the composite film is decreased after compounding SMPU with VGCF

while its shape memory property can be close to that of the pure SMPU after appropriate pretreatment.

关键词

气相生长碳纤维形状记忆聚氨酯复合材料力学性能形状记忆

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

聚氯乙烯/纳米水滑石复合材料的形态与力学性能

LLDPE/纳米SiO2复合材料的力学性能和光学性能研究

高强度两性离子聚合物防污减阻水凝胶涂层的制备

碳纤维自焊接骨架结构的形成及其复合材料性能研究

聚丁二酸丁二酯/纳米高岭土共混体系结晶及力学性能研究