SiO2@PANI光子晶体的制备及电致变色性能研究

梁飞跃; 李昕; 赵宁; 徐坚

doi:10.3724/SP.J.1105.2014.13430

您当前的位置：

首页 >

文章列表页 >

SiO2@PANI光子晶体的制备及电致变色性能研究

研究简报 | 更新时间：2021-03-19

- SiO2@PANI光子晶体的制备及电致变色性能研究
- Preparation and Electrochromic Property of SiO2@PANI Photonic Crystals
- 高分子学报 2014年第6期页码：860-864
- 作者机构：
  
  1. 北京服装学院材料科学与工程学院服装材料研究开发与评价北京市重点实验室,北京,100029
  2. 中国科学院化学研究所,北京,100190
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2014.13430
  中图分类号：
- 纸质出版日期：2014-6-20，
扫描看全文
梁飞跃, 李昕, 赵宁, 徐坚. SiO2@PANI光子晶体的制备及电致变色性能研究[J]. 高分子学报, 2014,(6):860-864.

Fei-yue Liang, Xin Li, Ning Zhao, Jian Xu. Preparation and Electrochromic Property of SiO2@PANI Photonic Crystals[J]. Acta Polymerica Sinica, 2014,(6):860-864.
梁飞跃, 李昕, 赵宁, 徐坚. SiO2@PANI光子晶体的制备及电致变色性能研究[J]. 高分子学报, 2014,(6):860-864. DOI： 10.3724/SP.J.1105.2014.13430.

Fei-yue Liang, Xin Li, Ning Zhao, Jian Xu. Preparation and Electrochromic Property of SiO2@PANI Photonic Crystals[J]. Acta Polymerica Sinica, 2014,(6):860-864. DOI： 10.3724/SP.J.1105.2014.13430.

摘要

应用Stber法合成单分散SiO2微球，通过垂直沉积自组装光子晶体，由电化学法在所组装的SiO2微球表面生成聚苯胺（PANI），得到了核-壳结构SiO2@PANI光子晶体薄膜. 测试了SiO2@PANI光子晶体薄膜的循环伏安曲线、多电位紫外吸收光谱、对比度、响应时间等电致变色性能，结果表明，该光子晶体薄膜在变色时颜色亮丽，其最大对比度可达77%，远高于单纯PANI薄膜的43%，同时响应时间变快. 初步实验结果说明将光子晶体结构引入导电聚合物中，能够提高其电致变色性能.

Abstract

Monodisperse silica particles were prepared by the modified Stber method

and the SiO2 opal film was obtained by a vertical deposition self-assembly method.Polyaniline was infiltrated into the SiO2 opal template via electrochemical methods

so as to fabricate core-shell structured SiO2@PANI photonic crystal films.The electrochromic properties

contrast and response time of the SiO2@PANI film were characterized via cycle voltammograms and spectroelectrochemistry.It was found that the color of the SiO2@PANI film was bright and vibrant with a maximal contrast of 77%

which was superior to that of the pure PANI film (43%)

and its response speed was faster.It is an effective method to improve the electrochromic performances of conducting polymers by introducing the photonic crystal structures.

关键词

光子晶体二氧化硅微球聚苯胺电致变色

Keywords

Photonic crystalSilica microspheresPolyanilineElectrochromism

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

电致变色型导电聚苯胺固态超级电容器的构建与性能研究

聚苯胺电致变色薄膜的红外发射特性研究

同时实现汗液酸碱监测及预警判断的非印制型聚苯胺基电子织物

基于聚苯胺微胶囊的双重自修复防腐涂层

基于聚乙二醇接枝丙烯酸树酯光固化电解质的制备及性能研究