负载钛系催化剂催化合成高反式丁二烯-异戊二烯共聚物

贺爱华; 姚微; 贾志峰; 黄宝琛; 焦书科

doi:null

您当前的位置：

首页 >

文章列表页 >

负载钛系催化剂催化合成高反式丁二烯-异戊二烯共聚物

研究论文 | 更新时间：2021-03-19

- 负载钛系催化剂催化合成高反式丁二烯-异戊二烯共聚物
- SYNTHESIS OF HIGH trans-1,4-BUTADIENE-ISOPRENE COPOLYMERS BY SUPPORTED TITANIUM CATALYSTS
- 高分子学报 2002年第1期页码：19-24
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2002-2-20，
扫描看全文
贺爱华, 姚微, 贾志峰, 黄宝琛, 焦书科. 负载钛系催化剂催化合成高反式丁二烯-异戊二烯共聚物[J]. 高分子学报, 2002,(1):19-24.

HE Aihua, YAO Wei, JIA Zhifeng, HUANG Baochen, JIAO Shuke. SYNTHESIS OF HIGH trans-1,4-BUTADIENE-ISOPRENE COPOLYMERS BY SUPPORTED TITANIUM CATALYSTS[J]. Acta Polymerica Sinica, 2002,(1):19-24.
贺爱华, 姚微, 贾志峰, 黄宝琛, 焦书科. 负载钛系催化剂催化合成高反式丁二烯-异戊二烯共聚物[J]. 高分子学报, 2002,(1):19-24. DOI：

HE Aihua, YAO Wei, JIA Zhifeng, HUANG Baochen, JIAO Shuke. SYNTHESIS OF HIGH trans-1,4-BUTADIENE-ISOPRENE COPOLYMERS BY SUPPORTED TITANIUM CATALYSTS[J]. Acta Polymerica Sinica, 2002,(1):19-24. DOI：

摘要

采用负载钛系催化剂 [TiCl4/MgCl2-(i-Bu)3Al]催化丁二烯 (Bd) 异戊二烯 (Ip)共聚合

研究了单体配比、聚合温度、烷基铝浓度和催化剂浓度及单体浓度等对共聚合速率及共聚物特性粘数的影响 .结果表明

当单体配比中Bd/(Bd+Ip)摩尔百分比≤ 20%

可制得高分子量的共聚物 .IR光谱分析及1H-NMR分析表明所得共聚物为高反式1

4-结构

丁二烯单体单元的反式 1

4-含量大于90%

异戊二烯单体单元的反式 1

4-含量大于98%

共聚物中丁二烯含量高于单体初始配比中的含量 .在一定的载钛量下

聚合条件对共聚物的微观结构影响不大.

Abstract

Butadiene(Bd) and isoprene(Ip) were copolymerized with TiCl4／MgCl2-Al(i-Bu)3 catalyst system．The effect of polymerizafion conditions such as feed ratio

temperature

Al／Ti mole ratio

Ti／M mole ratio and comonomer concentration on catalytic efficiency and intrinsic viscosity of the copolymers was investigated in details．The DSC results indicated that the products with low butadiene feed ratio(f01≤20％) were copolymers．IR and 1H-NMR spectra analysis of the copolymers showed that the copolymers were mainly trans-1

4-structure. Ip units of the copolymers had trans-1

4-contents above 98％ and Bd units had trans-1

4-cntents above 90％ and copolymerization conditions had little effects on micro-structure of the copolymers．It was found that the reaction activity of Bd was greater than that of Ip．

关键词

丁二烯异戊二烯共聚物负载钛催化剂反式14结构

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

用均相的稀土催化剂进行丁二烯-异戊二烯本体共聚合的研究

4f金属化合物催化苯乙烯和双烯烃的共聚——共聚反应的主要特征和聚合物的表征

磁场作用下异戊二烯在四氟乙烯-丙烯共聚物表面的光化学接枝反应

电化学合成吡咯与己内酰胺导电共聚物

Ni(naph)2/A1R3/BF3·OEt2/DMEA/OctOH体系催化丁二烯配位聚合