马来酸酐-苯乙烯熔融接枝聚丙烯的影响因素及其性能研究

谢续明; 李颖; 张景春; 杨讯

doi:null

您当前的位置：

首页 >

文章列表页 >

马来酸酐-苯乙烯熔融接枝聚丙烯的影响因素及其性能研究

研究论文 | 更新时间：2021-03-19

- 马来酸酐-苯乙烯熔融接枝聚丙烯的影响因素及其性能研究
- STUDY OF MELT FREE RADICAL GRAFTING OF MALEIC ANHYDRIDE AND STYRENE ONTO POLYPROPYLENE AND ITS PROPERTIES
- 高分子学报 2002年第1期页码：7-12
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2002-2-20，
扫描看全文
谢续明, 李颖, 张景春, 杨讯. 马来酸酐-苯乙烯熔融接枝聚丙烯的影响因素及其性能研究[J]. 高分子学报, 2002,(1):7-12.

XIE Xuming, LI Ying, ZHANG Jingchun, YANG Xun. STUDY OF MELT FREE RADICAL GRAFTING OF MALEIC ANHYDRIDE AND STYRENE ONTO POLYPROPYLENE AND ITS PROPERTIES[J]. Acta Polymerica Sinica, 2002,(1):7-12.
谢续明, 李颖, 张景春, 杨讯. 马来酸酐-苯乙烯熔融接枝聚丙烯的影响因素及其性能研究[J]. 高分子学报, 2002,(1):7-12. DOI：

XIE Xuming, LI Ying, ZHANG Jingchun, YANG Xun. STUDY OF MELT FREE RADICAL GRAFTING OF MALEIC ANHYDRIDE AND STYRENE ONTO POLYPROPYLENE AND ITS PROPERTIES[J]. Acta Polymerica Sinica, 2002,(1):7-12. DOI：

摘要

用单螺杆挤出机制备了马来酸酐 (MAH) 苯乙烯 (St)对聚丙烯 (PP)的多组分单体自由基熔融接枝体系 .研究证实了当两种单体物质的量比约为 1∶1时

接枝物的接枝率最高

而熔体流动速率 (MFR)最大 .对反应体系影响因素的研究表明单体用量和引发剂用量对不同单体用量比的系列接枝物的接枝率会产生不同的影响 ;另外

单体用量增加

接枝物的MFR减小

过氧化二异丙苯 (DCP)用量增加

接枝物的MFR增加 .对多单体熔融接枝聚丙烯PP-g-(MAH-co-St)的力学性能研究发现

选用合适的单体用量比、单体用量和DCP用量时

所制备的接枝物可具有与纯PP相当或更佳的力学性能.

Abstract

Free radical melt-grafting of the multi-monomer system of maleic anhydride(MAH)／styrene(St) onto polypropylene(PP) has been studied by means of a single-screw extruder．It has been proved that the grafting degree and the melt flow rate (MFR) of the grafted PP both reached maximum points when molar ratio of the two monomer was 1:1．Monomer concentration and DCP content were found to have different effects on grafting level of the grafted PP obtained in systems with different concentration ratio of MAH to St．Besides

the MFR values of the grafted PP decreased with increasing monomer concentration and increased with increasing DCP content．The multi-monomers melt grafted PP

i．e．PP-g-(MAH-co-St) was investigated for its properties．Excellent mechanical properties were obtained when suitable monomer concentration ratio

monomer concentration and DCP content were applied to the grafting system．

关键词

聚丙烯熔融接枝马来酸酐苯乙烯

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

苯乙烯/马来酸酐和苯乙烯/甲基丙烯酸二甲氨基乙酯二元体系在聚四氟乙烯多孔膜上的γ辐射接枝

聚丙烯与马来酸酐在超临界CO2中的接枝聚合

稀土配位催化马来酸酐-苯乙烯-N-苯基马来酰亚胺三元共聚合

Fe-Al络合催化苯乙烯-马来酸酐交替共聚

聚丙烯熔融接枝中共单体的作用机理