甲基丙烯酸N,N-二甲氨基乙酯/丙烯酸N,N-二甲氨基乙酯的可逆加成断裂链转移聚合研究

研究论文 | 更新时间：2021-03-19

- 甲基丙烯酸N,N-二甲氨基乙酯/丙烯酸N,N-二甲氨基乙酯的可逆加成断裂链转移聚合研究
- REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE
- 高分子学报 2005年第3期页码：398-402
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2005-6-20，
扫描看全文
辛秀强, 王延梅, 潘才元. 甲基丙烯酸N,N-二甲氨基乙酯/丙烯酸N,N-二甲氨基乙酯的可逆加成断裂链转移聚合研究[J]. 高分子学报, 2005,(3):398-402.

XIN Xiuqiang, WANG Yanmei, PAN Caiyuan. REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE[J]. Acta Polymerica Sinica, 2005,(3):398-402.
辛秀强, 王延梅, 潘才元. 甲基丙烯酸N,N-二甲氨基乙酯/丙烯酸N,N-二甲氨基乙酯的可逆加成断裂链转移聚合研究[J]. 高分子学报, 2005,(3):398-402. DOI：

XIN Xiuqiang, WANG Yanmei, PAN Caiyuan. REVERSIBLE ADDITION-FRAGMENTATION CHAIN TRANSFER POLYMERIZATION OF 2-(DIMETHYLAMINO)ETHYL METHACRYLATE/2-(DIMETHYLAMINO)ETHYL ACRYLATE[J]. Acta Polymerica Sinica, 2005,(3):398-402. DOI：

摘要

合成了二硫代苯甲酸2-(乙氧基羰基)异丙酯(ECPDB)、二硫代苯甲酸异丙苯酯(CDB)、二硫代苯甲酸1-苯基乙酯(PEDB)3种二硫代苯甲酸酯链转移剂.以这3种转移剂为基础

用凝胶渗透色谱和核磁共振测试了甲基丙烯酸N

N-二甲氨基乙酯(DMAEMA)和丙烯酸N

N-二甲氨基乙酯(DMAEA)两种碱性单体的可逆加成断裂链转移(RAFT)聚合的聚合物分子量、分子量分布和结构.发现有的聚合体系聚合物分子量分布较窄

但实验数均分子量与理论数均分子量相差较大;有的体系则转化率很低

聚合物分子量很小.这些可能是由聚合体系中单体活性和链转移剂链转移能力之间的匹配不太协调

使可逆加成断裂链转移快速平衡反应发生偏移或破坏造成的.因此

可通过更换单体或链转移剂来调节这种匹配

从而使可逆加成断裂链转移快速平衡保持稳定

达到聚合更可控

实验分子量与理论分子量更接近

分子量分布更窄的目的.

Abstract

Poly(2-(dimethylamino) ethyl methaerylate (PDMAEMA) and poly(2-(dimethylamino) ethyl aveate (PDMAEA) were prepared by using chain transfer agents (CTA)

dithioesters (2-(ethoxyearbonyl) prop-2-yl dithiobenzoate (ECPDB)

eumyl dithiobenzoate (CDB) and 1-phenylethyldithiobenzoate (PEDB) respectively

through reversible addition-fragmentation chain transfer (RAFT) polymerization．The molecular weight and molecular weight distribution of PDMAEMA and PDMAEA．were measured by gel permeation chromatography (GPC) and nuclear magnetic resonance spectrometer(1H-NMR)．The results showed the molecular weight distribution of PDMAEMA was narrow when the ECPDB/AIBN and CDB/AIBN as the initiator respectively．But the theoretical number average molecular weight Mn.th was not in good agreement with Mn.NMR and Mn.GPC. It demonstrated that the molecular weight of polymers could not be controlled．Its reason is probably that the balalive of the reversible addition-fragmentation chain transfer is disturbed by unapt match of monomer and CTA．With changing monomer or CTA

the molecular weight of polymers can be controlled．Compared with the CDB/AIBN system

the molecular weight distribution of PDMAEA by using PEDB/AIBN was narrower

and the molecular weisht was controllable．

关键词

可逆加成断裂链转移（RAFT）甲基丙烯酸NN-二甲氨基乙酯（DMAEMA）丙烯酸NN-二甲氨基乙酯（DMAEA）聚电解质

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

大投料比下自缩合原子转移自由基共聚合中聚合物支化结构的形成与演化

制备聚电解质空腔胶囊及其荧光蛋白装载

机理转移法合成聚丁二烯-b-聚(甲基丙烯酸N，N-二甲氨基乙酯)两亲性嵌段共聚物

甲基丙烯酸N,N-二甲氨基乙酯的CuX/PMDETA催化氧化聚合

原位凝聚法制备聚电解质微胶囊——模板中掺杂聚电解质量对微胶囊结构与性能的影响