热处理对聚偏氟乙烯-酰胺类溶剂所制薄膜结晶行为的影响

宋锐; 杨德彬; 谢巧丽; 何领好; 刘宝菲

doi:null

您当前的位置：

首页 >

文章列表页 >

热处理对聚偏氟乙烯-酰胺类溶剂所制薄膜结晶行为的影响

研究论文 | 更新时间：2021-03-19

- 热处理对聚偏氟乙烯-酰胺类溶剂所制薄膜结晶行为的影响
- THE EFFECT OF ANNEALING TEMPERATURE ON CRYSTALLIZATION OF POLY(VINYLIDENE FLUORIDE) FILMS PREPARED FROM POLY(VINYLIDENE FLUORIDE)/AMIDE SOLUTION
- 高分子学报 2007年第2期页码：144-147
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2007-2-20，
扫描看全文
宋锐, 杨德彬, 谢巧丽, 何领好, 刘宝菲. 热处理对聚偏氟乙烯-酰胺类溶剂所制薄膜结晶行为的影响[J]. 高分子学报, 2007,(2):144-147.

SONG Rui, YANG Debin, XIE Qiaoli, HE Linghao, LIU Baofei. THE EFFECT OF ANNEALING TEMPERATURE ON CRYSTALLIZATION OF POLY(VINYLIDENE FLUORIDE) FILMS PREPARED FROM POLY(VINYLIDENE FLUORIDE)/AMIDE SOLUTION[J]. Acta Polymerica Sinica, 2007,(2):144-147.
宋锐, 杨德彬, 谢巧丽, 何领好, 刘宝菲. 热处理对聚偏氟乙烯-酰胺类溶剂所制薄膜结晶行为的影响[J]. 高分子学报, 2007,(2):144-147. DOI：

SONG Rui, YANG Debin, XIE Qiaoli, HE Linghao, LIU Baofei. THE EFFECT OF ANNEALING TEMPERATURE ON CRYSTALLIZATION OF POLY(VINYLIDENE FLUORIDE) FILMS PREPARED FROM POLY(VINYLIDENE FLUORIDE)/AMIDE SOLUTION[J]. Acta Polymerica Sinica, 2007,(2):144-147. DOI：

摘要

使用红外光谱和偏光显微镜对PVDF(聚偏氟乙烯)-DMF(N

N-二甲基甲酰胺)和PVDF-DMAc(N

N-二甲基乙酰胺)体系结晶行为的研究表明

PVDF薄膜的结晶受制备溶剂

后期热处理温度和膜厚度等因素的影响; 升高温度

β相含量减小; 当温度低于90℃时

PVDF-DMF体系的F(β)值较DMAc体系大

在90～160℃之间则相反

且两种体系的F(β)值分别在约90℃和80℃发生“突变”；同时

结晶还明显受到薄膜厚度的影响

厚度大

结晶较完善.

Abstract

The crystallization of poly(vinylidene fluoride) (PVDF) films prepared from dimethylformamide (DMF) and dimethylacetamide (DMAc) solution and subsequently annealed at various temperature was studied by FT-IR and optical microscope.The results indicate that the crystallization of PVDF film depends on solvent

annealing temperature and film thickness.For all samples the content of β phase

F(β)

decreases with elevating annealing temperature.When the annealing temperature is less than 90℃

the F(β) of PVDF-DMF system is higher than that of PVDF-DMAc system; however

at 90～160℃

a reversed observation is obtained.For the two systems

interestingly

the F(β) decreases drastically at the region of ca 90℃ and 80℃

respectively.In addition

the crystallization of PVDF is also affected by film thickness

higher film thickness will make the spherulite more resolved.

关键词

聚偏氟乙烯结晶薄膜厚度红外光谱

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

改性聚偏氟乙烯接枝磺化聚（苯乙烯-co-丙烯酸）膜的研制

聚对苯二甲酰对苯二胺纤维的热老化行为与机理研究

聚合物熔体冷却阶段结晶行为的多尺度模拟

剪切应力场中聚丙烯熔体在近熔点处冷却结晶的晶体结构研究

PP/PMMA/PP-g-MAH共混物的结晶和相形态研究