近晶C(Sc)相串型液晶高分子的合成与表征

李自法; 张征; 宁超峰; 郑世军; 张淑媛; 周其凤; 谢刃; 张东

doi:null

您当前的位置：

首页 >

文章列表页 >

近晶C(Sc)相串型液晶高分子的合成与表征

研究论文 | 更新时间：2021-03-19

- 近晶C(Sc)相串型液晶高分子的合成与表征
- SYNTHESIS AND CHARACTERIZATION OF SEMETIC C PHASE LIQUID CYSTAL POLYMERS WITH MESOGENIC LATERALLY FIXED ONTO THE MAIN CHAIN
- 高分子学报 1998年第4期页码：412-418
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1998-8-20，
扫描看全文
李自法, 张征, 宁超峰, 郑世军, 张淑媛, 周其凤, 谢刃, 张东. 近晶C(Sc)相串型液晶高分子的合成与表征[J]. 高分子学报, 1998,(4):412-418.

LI Zifa, ZHANG Zheng, NING Chaofeng, ZHENG Shijun, ZHANG Shuyuan, ZHOU Qifeng, XIE Ren, ZHANG Dong. SYNTHESIS AND CHARACTERIZATION OF SEMETIC C PHASE LIQUID CYSTAL POLYMERS WITH MESOGENIC LATERALLY FIXED ONTO THE MAIN CHAIN[J]. Acta Polymerica Sinica, 1998,(4):412-418.
李自法, 张征, 宁超峰, 郑世军, 张淑媛, 周其凤, 谢刃, 张东. 近晶C(Sc)相串型液晶高分子的合成与表征[J]. 高分子学报, 1998,(4):412-418. DOI：

LI Zifa, ZHANG Zheng, NING Chaofeng, ZHENG Shijun, ZHANG Shuyuan, ZHOU Qifeng, XIE Ren, ZHANG Dong. SYNTHESIS AND CHARACTERIZATION OF SEMETIC C PHASE LIQUID CYSTAL POLYMERS WITH MESOGENIC LATERALLY FIXED ONTO THE MAIN CHAIN[J]. Acta Polymerica Sinica, 1998,(4):412-418. DOI：

摘要

以２

５-二（对烷氧基苯甲酰氧基）对苯二酚和不同结构的脂族二酰氯为单体

采用低温溶液缩聚的方法

合成了一系列新的液晶基元垂直于分子主链的Ｓｃ相串型液晶高分子．单体的结构通过元素分析、ＩＲ、１Ｈ-ＮＭＲ和ＭＳ等方法确证．聚合物通过ＧＰＣ、ＤＳＣ、ＴＧ、ＷＡＸＤ和偏光显微镜等方法测试表征．研究发现

所有的聚合物加热至各自的熔点以上都能形成液晶态

在液晶态可以观察到纹影或焦锥织构．通过变温Ｘ射线衍射证明它们为Ｓｃ相．所有聚合物的熔点（Ｔｍ）和液晶态的清亮点（Ｔ１）随分子中末端烷氧基增大和柔性间隔段长度增加逐渐降低

液晶态温度范围变窄．

Abstract

A new series of semetic C phase liquid crystal polymers with mesogens laterally fixed onto the main chain was synthesized via low temperature solution polycondensation from 2

5 bis(p alkoxyl benzoloxy) hydroquinone and aliphatdiyl chloride with different structure.The low molecular weight compounds were analyzed by elemental analysis IR 1H-NMR and MS.The polymers were characterized by GPC DSC TG WAXD and polarizing microscope with heating stage.It was found that all the polymers went to liquid crystal phase when heated to their Tm.The Schlieren textyre or focal-conic texture can be observed.Temperature-variable X-ray diffraction realized that they are smectic c phase.Both Tm and Ti of all the polymers decreased with the increase of the end alkoxy group length and the flexible spacer unit in the polymers gets longer

the temperature range of the liquid crystal phase of the polymers becomes narrow.

关键词

近晶Ｃ相液晶高分子合成与表征

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

含冠醚环的席夫碱型液晶高分子的合成与表征

含T-型和棒型两种液晶基元的主链型液晶共聚酯的合成和表征

含X-型二维液晶基元和顺式-4,4′-双(4-羟基苯基偶氮)二苯并-18-冠-6冠醚环液晶共聚酯的合成与表征

含柔性链段的苯并二噁唑类聚合物合成与表征

含液晶基团的聚对亚苯基亚乙炔基类交替共聚物的合成、表征及性能研究