- BLENDS OF POLYAMIDE 1010 WITH UNGRAFTED AND MALEIC ANHYDRIDE GRAFTED HIGHIMPACT POLYSTYRENE
- 高分子学报 1999年第5期页码：557-563
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1999-10-20，
扫描看全文
陈广新, 刘景江. 尼龙1010分别与未接枝和接枝马来酸酐的高抗冲聚苯乙烯的共混体系研究[J]. 高分子学报, 1999,(5):557-563.

CHEN Guangxin, LIU Jingjiang. BLENDS OF POLYAMIDE 1010 WITH UNGRAFTED AND MALEIC ANHYDRIDE GRAFTED HIGHIMPACT POLYSTYRENE[J]. Acta Polymerica Sinica, 1999,(5):557-563.
陈广新, 刘景江. 尼龙1010分别与未接枝和接枝马来酸酐的高抗冲聚苯乙烯的共混体系研究[J]. 高分子学报, 1999,(5):557-563. DOI：

CHEN Guangxin, LIU Jingjiang. BLENDS OF POLYAMIDE 1010 WITH UNGRAFTED AND MALEIC ANHYDRIDE GRAFTED HIGHIMPACT POLYSTYRENE[J]. Acta Polymerica Sinica, 1999,(5):557-563. DOI：

摘要

研究了尼龙１０１０（ＰＡ１０１０）与高抗冲聚苯乙烯（ＨＩＰＳ）及马来酸酐官能化的ＨＩＰＳ（ＨＩＰＳ-ｇ-ＭＡ）间的相互作用

利用ＤＳＣ

ＤＭＡ

ＳＥＭ及拉伸测试等方法研究了不同组成比的共混物ＰＡ１０１０／ＨＩＰＳ与ＰＡ１０１０／ＨＩＰＳ-ｇ-ＭＡ的结晶、玻璃化转变、形态及力学性能．结果表明ＨＩＰＳ与ＰＡ１０１０虽然结构相差甚远

但两者之间仍存在着一定的相互作用；而ＨＩＰＳ-ｇ-ＭＡ可使ＰＡ１０１０的低温熔融峰变小

当ＨＩＰＳ-ｇ-ＭＡ的含量≤５０％时

随着其含量的增加

共混物中ＰＡ１０１０的结晶温度升高；当含量＞５０％时

ＰＡ１０１０发生分级结晶行为

其结晶温度由原来的１７８ ℃降至８３ ℃

同时ＨＩＰＳ-ｇ-ＭＡ与ＰＡ１０１０间的相互作用变大

ＤＭＡ谱上有明显的新的松驰峰．ＰＡ１０１０／ＨＩＰＳ-ｇ-ＭＡ共混体系的拉伸性能要优于相同组成的ＰＡ１０１０／ＨＩＰＳ体系．以上现象主要是由于ＨＩＰＳ-ｇ-ＭＡ与ＰＡ１０１０中的端胺基发生了化学反应

产生了接枝共聚物ＰＡ１０１０-ｇ-ＨＩＰＳ所致．

Abstract

The crystalliztation

dynamic mechanical properties

tensile properties andmorphology features of polyamidel 1010( PA1010) blends with the high impact polystyrere( HIPS) and maleic anhydride (MA) grafted HIPS(HIPS-g-MA) were examined at a widecomposition range . By comparison the PA1010/ HIPS-g-MA and PA1010/HIPS binaryblends

it wasfoundthatthe size ofthe domains of HIPS-g-M Awas much smallerthan thatof HIPS at the same compositions. It was found that the mechanical properties of PA1010/HIPS-g-MA blends were obviously higher than those of PA1010/HIPS blends. When the content of PA1010 is more than 50wt% in the blends

the crystallization temperatures

Tcs

of PA1010 increase with increasing the content of HIPS-g-MA. On the other hand

when the content of PA1010 in the blends is less than 35wt% the fraction crystallization is observed. The same result is not obtained for the blends of PA1010/HIPS. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/HIPS-g-MA blends.

关键词

PA1010HIPSHIPS-g-MA共混

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

POE-g-PMAH反应性增容PA1010/PP共混物的性能研究

聚乳酸/乙烯-醋酸乙烯酯共聚物共混物的形态与黏弹行为

PSF-g-PAA和PSF-g-PNIPAAm的合成及其共混膜的环境响应性研究

PSF-g-P(PEGMA)的合成及其共混超滤膜的制备与性能研究

咪唑基离子液体Br［C14im］(CH2)4［C14im］Br对PP结构与性能的影响