甲基丙烯酸甲酯 - 甲基丙烯酸共聚物/梯形聚苯基硅倍半氧烷原位共混体系的性能研究

李桂芝; 施良和; 叶美玲

doi:null

您当前的位置：

首页 >

文章列表页 >

甲基丙烯酸甲酯 - 甲基丙烯酸共聚物/梯形聚苯基硅倍半氧烷原位共混体系的性能研究

研究论文 | 更新时间：2021-03-19

- 甲基丙烯酸甲酯 - 甲基丙烯酸共聚物/梯形聚苯基硅倍半氧烷原位共混体系的性能研究
- STUDIES ON PROPERTIES OF POLY (METHYL METHACRYLATE METHYL ACRYLIC ACID)/ LADDERLIKE POLY(PHENYL SILSESQUIOXANE) IN SITU BLENDS
- 高分子学报 1998年第2期页码：160-166
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1998-4-20，
扫描看全文
李桂芝, 施良和, 叶美玲. 甲基丙烯酸甲酯 - 甲基丙烯酸共聚物/梯形聚苯基硅倍半氧烷原位共混体系的性能研究[J]. 高分子学报, 1998,(2):160-166.

LI Guizhi, SHI Lianghe, YE Meiling. STUDIES ON PROPERTIES OF POLY (METHYL METHACRYLATE METHYL ACRYLIC ACID)/ LADDERLIKE POLY(PHENYL SILSESQUIOXANE) IN SITU BLENDS[J]. Acta Polymerica Sinica, 1998,(2):160-166.
李桂芝, 施良和, 叶美玲. 甲基丙烯酸甲酯 - 甲基丙烯酸共聚物/梯形聚苯基硅倍半氧烷原位共混体系的性能研究[J]. 高分子学报, 1998,(2):160-166. DOI：

LI Guizhi, SHI Lianghe, YE Meiling. STUDIES ON PROPERTIES OF POLY (METHYL METHACRYLATE METHYL ACRYLIC ACID)/ LADDERLIKE POLY(PHENYL SILSESQUIOXANE) IN SITU BLENDS[J]. Acta Polymerica Sinica, 1998,(2):160-166. DOI：

摘要

甲基丙烯酸甲酯甲基丙烯酸共聚物（Ｐ（ＭＭＡ-ＭＡＡ））与低分子量或高分子量梯形聚苯基硅倍半氧烷（ＰＰＳＱ）的共混物经原位聚合法制成．用光学透明法、荧光光谱、ＤＳＣ等技术研究了该共混体系的相容性及组分间的相互作用及结构转变．结果表明

当ＰＰＳＱ含量较小时

由于ＰＰＳＱ与Ｐ（ＭＭＡ-ＭＡＡ）间存在着较强的氢键作用

该共混体系在一定配比下相容

且低分子量ＰＰＳＱ与Ｐ（ＭＭＡ-ＭＡＡ）间的相容性较好．当ＰＰＳＱ的含量≤１％时

ＰＰＳＱ的加入对该共混物的Ｔｇ影响不大

但其Ｔｆ随ＰＰＳＱ含量增加而增大．此外

还测试了Ｐ（ＭＭＡ-ＭＡＡ）／ＰＰＳＱ原位共混物的硬度及冲击强度．

Abstract

P(MMA MAA)/ladderlike PPSQ blends

in which PPSQ has a low or high molecular weight

were prepared by in situ copolymerization. Light transimissivity measurement

fluorescence

DSC techniques were used to study the miscibility

interactions of two components and structural transitions. The results indicate that P(MMA MAA) and PPSQ are completely miscible on a small scale of 200nm because of some strong hydrogen bonding interactions between molecules of P(MMA MAA) and PPSQ when the blends contain a small amount of PPSQ and that PPSQ with a low molecular weight has better miscibility with P(MMA-MAA)than that of PPSQ with higher Mw.Although compositions of the blends has little influence on Tg

of the blends almost increase with an increase of PPSQ content (PPSQ≤1%).Ball hardness and impact strength of all blend samples were also measured.

关键词

Ｐ（ＭＭＡ-ＭＡＡ）／梯形ＰＰＳＱ共混物相容性力学性能

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

丝素蛋白与聚氨酯共混膜的制备及结构和性能

聚丙烯酸丁酯/蓖麻油聚氨酯半互穿弹性体网络研究

高强度两性离子聚合物防污减阻水凝胶涂层的制备

聚丁二酸丁二酯/纳米高岭土共混体系结晶及力学性能研究

不同分子量的高密度聚乙烯与茂金属线型低密度聚乙烯的相容性