在Bu2SnO-Bu_3PO4缩合物的存在下以端羟基聚醚增韧环氧树脂

吴琦; 徐建军; 马岳; 余云照

doi:null

您当前的位置：

首页 >

文章列表页 >

在Bu2SnO-Bu_3PO4缩合物的存在下以端羟基聚醚增韧环氧树脂

研究论文 | 更新时间：2021-03-19

- 在Bu2SnO-Bu_3PO4缩合物的存在下以端羟基聚醚增韧环氧树脂
- TOUGHENING OF EPOXY RESINS BY HYDROXYL-TERMINATED POLYETHER WITH Bu2SnO-Bu3PO4 CONDENSATE AS CATALYST
- 高分子学报 2001年第1期页码：68-72
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2001-2-20，
扫描看全文
吴琦, 徐建军, 马岳, 余云照. 在Bu2SnO-Bu_3PO4缩合物的存在下以端羟基聚醚增韧环氧树脂[J]. 高分子学报, 2001,(1):68-72.

WU Qi, XU Jianjun, MA Yue, YU Yunzhao. TOUGHENING OF EPOXY RESINS BY HYDROXYL-TERMINATED POLYETHER WITH Bu2SnO-Bu3PO4 CONDENSATE AS CATALYST[J]. Acta Polymerica Sinica, 2001,(1):68-72.
吴琦, 徐建军, 马岳, 余云照. 在Bu2SnO-Bu_3PO4缩合物的存在下以端羟基聚醚增韧环氧树脂[J]. 高分子学报, 2001,(1):68-72. DOI：

WU Qi, XU Jianjun, MA Yue, YU Yunzhao. TOUGHENING OF EPOXY RESINS BY HYDROXYL-TERMINATED POLYETHER WITH Bu2SnO-Bu3PO4 CONDENSATE AS CATALYST[J]. Acta Polymerica Sinica, 2001,(1):68-72. DOI：

摘要

工业中大量生产的端羟基聚醚

由于羟基的反应活性不够

不能直接用于增韧胺类固化的环氧树脂 .Bu2SnO-Bu3PO4 缩合物能催化羟基对环氧基的加成反应.本文研究在Bu2 SnO-Bu3PO4 缩合物Sn-P6700的存在下以端羟基聚四氢呋喃 (PTMG)增韧芳香胺 4

4′-二氨基二苯砜 (DDS)固化的环氧树脂 .PTMG首先与环氧树脂反应生成嵌段共聚物

在固化时发生微相分离 .分散相的尺寸在有利于增韧的范围内 .PTMG在分子量与浓度适当时

能使树脂的断裂韧性大大提高 ;抗弯强度也有显著提高

而Tg和模量略有降低.

Abstract

The hydroxyl terminated polyethers

though industrially widely available

have not been used as tougheners for amine cured epoxy resins. The Bu2SnO-Bu3PO4 condensate Sn P6700 was used to catalyze the addition of hydroxyl group to epoxy group. In the presence of this catalyst hydroxyl terminated poly(tetramethylene glycols)(PTMG) were used directly as the toughener for the epoxy resin with 4

4′-diamino diphenyl sulfone as the curing agent. PTMG was first reacted with the epoxy resin to form block copolymers.Micro-phase separation took place upon curing.The particle size of the dispersed phase was in the range of 0.4 to 1.4μm when the molecular weight was in the range of 700 to 2000

which was favorable to the toughening.When ca. 5 phr of PTMG was used as modifier

the toughness of the cured resin was improved greatly with a slight lowering of Tg and modulus.

关键词

环氧树脂端羟基聚四氢呋喃Bu_2SnO-Bu_3PO_4缩合物增韧

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

功能基化介晶高聚物增韧环氧树脂性能研究——材料断裂面形态结构与力学性能的关系

含刚性链节和脲端基聚醚增韧剂改性环氧树脂的研究———反应活性及力学性能

含柔性间隔基的扩链脲增韧环氧树脂性能研究——环氧树脂/扩链脲/双氰双胺体系性能研究

正离子光固化聚硅氧烷的合成及其环氧树脂复合固化膜的性能

升温与等温法非模型动力学研究环氧树脂固化反应