聚辛烯-1Mark-Houwink常数的确定及其分子量分布研究

封麟先; 范志强; 徐秀珠; 卜一民; 杨士林

doi:null

您当前的位置：

首页 >

文章列表页 >

聚辛烯-1Mark-Houwink常数的确定及其分子量分布研究

研究论文 | 更新时间：2021-03-19

- 聚辛烯-1Mark-Houwink常数的确定及其分子量分布研究
- EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE)
- 高分子学报 1989年第3期页码：349-354
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1989-6-20，
扫描看全文
封麟先, 范志强, 徐秀珠, 卜一民, 杨士林. 聚辛烯-1Mark-Houwink常数的确定及其分子量分布研究[J]. 高分子学报, 1989,(3):349-354.

FENG Lin-xian, FAN Zhi-qiang, XU Xiou-zhu, BO Yi-min, YANG Shi-lin. EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE)[J]. Acta Polymerica Sinica, 1989,(3):349-354.
封麟先, 范志强, 徐秀珠, 卜一民, 杨士林. 聚辛烯-1Mark-Houwink常数的确定及其分子量分布研究[J]. 高分子学报, 1989,(3):349-354. DOI：

FENG Lin-xian, FAN Zhi-qiang, XU Xiou-zhu, BO Yi-min, YANG Shi-lin. EVALUATION OF MARK-HOUWINK CONSTANTS AND STUDY OF THE MOLECULAR WEIGHT DISTRIBUTION OF POLY (1-OCTENE)[J]. Acta Polymerica Sinica, 1989,(3):349-354. DOI：

摘要

本文用GPC结合特性粘度的方法

对聚辛烯-1四氢呋喃体系的Mark-Houmink常数进行订定。数据处理采用了Weiss法和流体力学平均分子量(?)_x两种方法

α值分别为0.701和0.625

相对误差10％左右

所得Mark-Hon-Wink方程Weiss法为:[η]THF25℃=3.89×10-4[M]0.701(?)x法为[η]THF℃25=4.14×10-4M0'625。本文还研完了聚合反应条件对聚辛烯-1分子量及分子量分布的影响。发现三种TiCl3为主催化剂

三乙基铝为助催化剂时

其GPC谱图均为双峰型

两个峰的比例随聚合反应条件不同而变化。表明聚合体系至少有两种不同性质的活性中心

有着不同的形成和增长速率。

Abstract

The Mark-Houwink constants of poly (1-octene) in THF at 25℃ were evaluated from GPC and [η] of broad distribution samples. Two methods were used: calculation of K and a from the method developed by weiss and from the linear relation between in In[η] and InMx made by Goldwasser. More reliable results were obtained with the latter method. Determination of the molecular weight was made with the light scattering method

which gave Mw value close to that obtained from GPC. Then the Mark-Houwink equation for poly(1-octene) is [n]25℃THF×10-4M0.625. The effects of polymerization conditions on molecular weight distribution were studied with GPC. When AlEt3 was used as cocatalyst

the distribution was bi-modal. The change of alkyl aluminiums caused greater effect on the distrbutions than the cha-nge of TiCl3 strucure.

关键词

聚辛烯-1分子量分布Mark-Houwink常数

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

单体组成对甲基丙烯酸甲酯/丙烯酸丁酯RAFT共聚合转移常数的影响

球形MgCl2负载钛催化剂催化苯乙烯等规聚合与产物分子量分布研究

从聚丙烯流动曲线估算分子量分布

Fe-Zn双金属氰化物催化环氧丙烷开环聚合的研究

α-溴代丁酸乙酯/CuBr/联吡啶体系引发的活性自由基聚合反应