- STUDIES ON THE KINETICS AND CHARACTERIZATION OF DGEBA/DDM SYSTEM MODIFIED WITH EPOXY TERMINATED DISILOXANE
- 高分子学报 1994年第1期页码：41-47
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1994-2-20，
扫描看全文
张保龙, 曹国强, 黄吉甫, 丁培元, 张宝申, 杜宗杰, 周秀中. 胺固化端环氧基二硅氧烷动力学及性能研究[J]. 高分子学报, 1994,(1):41-47.

ZHANG Bao-long, CAO Guo-qiang, HUANG Ji-fu, DING Pei-yuan, ZHANG Bao-shen, DU Zong-jie, ZHOU Xiu-chong. STUDIES ON THE KINETICS AND CHARACTERIZATION OF DGEBA/DDM SYSTEM MODIFIED WITH EPOXY TERMINATED DISILOXANE[J]. Acta Polymerica Sinica, 1994,(1):41-47.
张保龙, 曹国强, 黄吉甫, 丁培元, 张宝申, 杜宗杰, 周秀中. 胺固化端环氧基二硅氧烷动力学及性能研究[J]. 高分子学报, 1994,(1):41-47. DOI：

ZHANG Bao-long, CAO Guo-qiang, HUANG Ji-fu, DING Pei-yuan, ZHANG Bao-shen, DU Zong-jie, ZHOU Xiu-chong. STUDIES ON THE KINETICS AND CHARACTERIZATION OF DGEBA/DDM SYSTEM MODIFIED WITH EPOXY TERMINATED DISILOXANE[J]. Acta Polymerica Sinica, 1994,(1):41-47. DOI：

摘要

合成了１，３－二甲基－１，３－二乙基－１，３－双［３－（２，３－环氧丙氧基）丙基］二硅氧烷（ＴＥＤＳ）．对其与二正丁胺的模型反应、与ＤＤＭ（４，４’－二氨基二苯基甲烷）的固化反应劝力学研究表明，反应对ＴＥＤＳ为一级反应．ＴＥＤＳ改性环氧Ｅ—５１体系的动态力学性能、冲击性能和形态结构的研究表明，随改性体系中ＴＥＤＳ含量的增加，体系的玻璃化温度是线性下降、冲击强度增大、冲击试样的断裂面渐渐显现出韧性断裂的特征．

Abstract

imethyl - 1

3 - diethyl - 1

3 - his(3 - (2

3 - epoxy propoxy ) propyl )disiloxane (TEDS) was synthesized and used as modifier for epoxy reSin. Basedon the studies on the curing kinetics of TEDS/ DDM system as well as model rcasnon of TEDS/di - n- butylamine

the first order kinetic was proposed for TEDS.Besides

the dynamic mechanical behavior

impact strength and the morphology ofDGEBA/DDM system modified with TEDS were studied. Results showed thatthe impact strength of the modified system was found to be enhanced with the increase of TEDS content

whereas the glass transition temperature (Tg) was de-creased linearly. SEM observation of the fracture surface of the impact specimen al-so showed that as the increase of the modifier content the toughed fracture charac-ters were obviously appeared.

关键词

环氧树脂二硅氧烷固化动力学形态改性

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

环氧树脂/液晶聚合物体系的形态、力学性能和热稳定性

端羟基丁腈橡胶增韧环氧树脂研究

聚苯基硅氧烷与聚甲基苯基硅氧烷改性环氧树脂的合成与性能比较

2-乙基-4-甲基咪唑固化环氧树脂体系动力学模型

气相生长碳纤维对环氧树脂固化反应的影响及其复合物固化动力学研究