- 含环氧基的丙烯酸酯弹性体的合成及其对聚氯乙烯改性研究
- SYNTHESIS OF ACRYLATE RUBBER WITH EPOXY GROUP AND THE MODIFICATION FOR PVC
- 高分子学报 1994年第2期页码：211-218
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：1994-4-20，
扫描看全文
张保龙, 王淑芳, 黄吉甫, 丁培元, 杜宗杰, 宋谋道, 张邦华. 含环氧基的丙烯酸酯弹性体的合成及其对聚氯乙烯改性研究[J]. 高分子学报, 1994,(2):211-218.

ZHANG Bao-long, WANG Shu-fang, HUANG Ji-fu, DING Pei-yuan, DU Zong-jie, SONG Mou-dao, ZHANG Bang-hua. SYNTHESIS OF ACRYLATE RUBBER WITH EPOXY GROUP AND THE MODIFICATION FOR PVC[J]. Acta Polymerica Sinica, 1994,(2):211-218.
张保龙, 王淑芳, 黄吉甫, 丁培元, 杜宗杰, 宋谋道, 张邦华. 含环氧基的丙烯酸酯弹性体的合成及其对聚氯乙烯改性研究[J]. 高分子学报, 1994,(2):211-218. DOI：

ZHANG Bao-long, WANG Shu-fang, HUANG Ji-fu, DING Pei-yuan, DU Zong-jie, SONG Mou-dao, ZHANG Bang-hua. SYNTHESIS OF ACRYLATE RUBBER WITH EPOXY GROUP AND THE MODIFICATION FOR PVC[J]. Acta Polymerica Sinica, 1994,(2):211-218. DOI：

摘要

以丙烯酸丁酯（ＢＡ），甲基丙烯酸甲酯（ＭＭＡ）和甲基丙烯酸缩水甘油酯（ＧＭＡ）为原料，通过分段乳液聚合，合成了一系列具有不同组成结构的三元共聚物—Ｐ（Ｂ—Ｍ—Ｇ）弹性体，并对此弹性体改性的ＰＶＣ的抗冲击性能进行了系统研究．结果表明：改性剂组成结构的变化对改性体系的冲击性能有较大影响，改性ＰＶＣ的冲击性能最高可达７９ｋＪ／ｍ２．动态力学及ＳＥＭ实验表明，ＰＶＣ与改性体系系部分相容的共混体系，其断裂行为是明显的韧性断裂特征．本文还对改性体系的力学性能进行了研究．

Abstract

A series of terpolymers of butyl acrylate (BA )

methyl methacrylate (MMA )

and glyddyl methacrylate (GMA) were prepared by sequential emulsion copolymerization. The obtained acrylate elastomers with different structures were used as the modifier for PVC. The results showed that the impact strength of the modified PVC were greatly related with the components and structures of the terpolymers. The utmost impact strength of the modified PVC might reach the level of 20 times over that of the unmodified PVC. Based on the tests of dynamic mechanical analysis and the observation of SEM

it might be proved that the blends of PVC and the studied acrylate modifiers are partially compatible system.The appearance of the fracture surface of the modified PVC behaves typical tough characters. Moreover

the mechanical properties of the modified system were also investigated and discussed.

关键词

甲基丙烯酸缩水甘油酯丙烯酸酯弹性体聚氯乙烯共混改性剂

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

聚乳酸/乙烯-醋酸乙烯酯共聚物共混物的形态与黏弹行为

POE-g-PMAH反应性增容PA1010/PP共混物的性能研究

PSF-g-PAA和PSF-g-PNIPAAm的合成及其共混膜的环境响应性研究

在交联聚合物微球GMA/MMA表面接枝固载聚乙二醇的研究

PSF-g-P(PEGMA)的合成及其共混超滤膜的制备与性能研究